Development of dual nozzle slurry extrusion 3D printer by integrating material extrusion and photopolymerization for the fabrication of engineered ceramics
Abstrakt
This research focuses on developing a dual-nozzle slurry-based extrusion 3D printer capable of fabricating intricate zirconia structures. The designed 3D printer combines material extrusion and photopolymerization technologies to improve material diversity, precision, and cost-effectiveness. The 3D printer design incorporates ultraviolet curing to instantly cure extruded zirconia slurry thereby, eliminating the need for a step-wise curing procedure. Printing parameters were optimized to achieve high-quality prints, and supports made of polyethylene terephthalate glycol (PETG) were used for intricate geometries. The printability and mechanical properties were evaluated for two different zirconia slurry compositions: 70/30 and 80/20 powder-to-resin weight percentages. The printed green body was subjected to a two-phase sintering process. The 3D printer fabricated structures with features subtending angles greater than 50 degrees and a filling density above 80% without any supports. Shrinkage analysis showed the 80/20 composition resulted in higher density parts, with shrinkage ratios of 25.23%, 26.23%, and 27.26% along the X, Y, and Z axes, respectively. The sintered objects displayed hardness (1525 HV) and flexural strength (117 MPa), with minimal porosity. This study demonstrates the development of a cost-effective dual-nozzle 3D printer that can effectively fabricate functional parts with complex material compositions and geometries that can cater to the futuristic requirements of high-end industries.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (6)
-
Yulius Romario
-
Chinmai Bhat
-
Lin Yu-yang
-
Maziar Ramezani
-
Cho-pei Jiang
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1108/RPJ-09-2024-0387
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach dostępnych w wersji elektronicznej [także online]
- Opublikowano w:
-
RAPID PROTOTYPING JOURNAL
ISSN: 1355-2546 - Język:
- angielski
- Rok wydania:
- 2025
- Opis bibliograficzny:
- Romario Y., Bhat C., Yu-yang L., Macek W., Ramezani M., Jiang C., Development of dual nozzle slurry extrusion 3D printer by integrating material extrusion and photopolymerization for the fabrication of engineered ceramics, RAPID PROTOTYPING JOURNAL, 2025,10.1108/RPJ-09-2024-0387
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1108/rpj-09-2024-0387
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 0 razy
Publikacje, które mogą cię zainteresować
Advancements in the Additive Manufacturing of Magnesium and Aluminum Alloys through Laser-Based Approach
- S. K. Sharma,
- H. S. Grewal,
- K. K. Saxena
- + 7 autorów
Wire Arc Additive Manufactured Mild Steel and Austenitic Stainless Steel Components: Microstructure, Mechanical Properties and Residual Stresses
- K. U. Rani,
- R. Kumar,
- M. M. Mahapatra
- + 4 autorów