Fatigue life improvement using low transformation temperature weld material with measurement of residual stress
Abstrakt
Welding processes often produce high levels of tensile residual stress. Low transformation temperature (LTT) welding wires utilise phase transformation strains to overcome the thermal contraction of a cooling weld. In this paper, the residual stress within each weld was quantified using the milling/strain gauge method, being the strain change measured as the weldment was milled away. The fatigue tests were conducted under uniaxial loading considering two types of LTT materials. The results show that the crack propagation of all samples was similar in cycles although both LTT materials extended the crack initiation, and, therefore, the overall life of the part. It was found that both LTT materials reduced the residual tensile stresses, increased the residual compressive stresses, leading to increase in fatigue life about 30%.
Cytowania
-
7
CrossRef
-
0
Web of Science
-
6
Scopus
Autorzy (7)
-
Jordan Franks
-
Greg Wheatley
-
Pedram Zamani
-
Reza Masoudi Nejad
-
Ricardo Branco
-
Farzaneh Samadi
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
INTERNATIONAL JOURNAL OF FATIGUE
nr 164,
ISSN: 0142-1123 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Franks J., Wheatley G., Zamani P., Masoudi Nejad R., Macek W., Branco R., Samadi F.: Fatigue life improvement using low transformation temperature weld material with measurement of residual stress// INTERNATIONAL JOURNAL OF FATIGUE -Vol. 164, (2022), s.107137-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ijfatigue.2022.107137
- Źródła finansowania:
-
- COST_FREE
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 63 razy
Publikacje, które mogą cię zainteresować
An investigation on residual stress and fatigue life assessment of T-shape welded joints
- F. Samadi,
- J. Mourya,
- G. Wheatley
- + 4 autorów
The effect of elevated temperature on LCF damage growth in 2024AA – Experiment and modeling
- A. Falkowska,
- A. Tomczyk,
- A. Seweryn
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
- W. Macek,
- R. Masoudi Nejad,
- S. Zhu
- + 5 autorów