The topography, structure, thermal, magnetic, and electrical properties of Bi4V2-xFexO11-δ ceramics substituted with x = 0.5 and 0.7 Fe were studied. The microscope analysis showed the presence of iron-rich nanocrystals formed on the Bi-Fe-V-O grains. The X-ray diffraction studies confirmed that grains are built mostly of tetragonal Bi4V1.5Fe0.5O10.5 phase. Thermal properties analysis showed an order-disorder type γ ↔ γʹ phase transition at a temperature of around 916 K, pronounced in samples doped with x = 0.5 Fe. The magnetic anomaly was observed in ceramics doped with x = 0.7 Fe which was assigned to Morin transition of Fe2O3. The conductivity was measured over a wide frequency range from 10 mHz to 1 MHz and at a wide temperature range from 373 to 923 K, using impedance spectroscopy. The D.C. conduction process was due to oxygen vacancies hopping while at low temperatures electron holes hopping is also possible.
Cytowania
-
3
CrossRef
-
0
Web of Science
-
3
Scopus
Autorzy (5)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jeurceramsoc.2022.05.012
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
nr 42,
strony 5015 - 5022,
ISSN: 0955-2219 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Wójcik N., Polcyn K., Karczewski J., Górnicka K., Barczyński R.: High-conducting Bi4V2-xFexO11-δ ceramics containing Fe2O3 nanocrystals: Structure and properties// JOURNAL OF THE EUROPEAN CERAMIC SOCIETY -Vol. 42,iss. 12 (2022), s.5015-5022
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jeurceramsoc.2022.05.012
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 154 razy
Publikacje, które mogą cię zainteresować
Structure and magnetic properties of BeO-Fe2O3-Al2O3-TeO2 glass-ceramic composites
- N. Wójcik,
- N. Tagiara,
- S. Ali
- + 6 autorów
Fe3–xInSnxO6 (x = 0, 0.25, or 0.5): A Family of Corundum Derivatives with Sn-Induced Polarization and Above Room Temperature Antiferromagnetic Ordering
- C. E. Frank,
- E. E. McCabe,
- F. Orlandi
- + 19 autorów
ALTERNATIVE, DIRECT SYNTHESIS METHOD OF THE CERAMIC SOLID SOLUTIONS BASED ON BaTiO3 THROUGH A HIGH ENERGY BALL MILLING
- W. Bąk,
- P. Dulian,
- B. Garbarz-Glos
- + 2 autorów