High temperature monoclinic-to-tetragonal phase transition in magnesium doped lanthanum ortho-niobate

Aleksandra Dorota Mielewczyk-Gryń; Katarzyna Gdula-Kasica; Bogusław Kusz; Maria Gazda

doi:10.1016/j.ceramint.2012.09.102

High temperature monoclinic-to-tetragonal phase transition in magnesium doped lanthanum ortho-niobate

Abstrakt

Magnesium doped lanthanum ortho-niobate (La0.98Mg0.02NbO4) was prepared by the molten salt synthesis method. X-ray diffraction and dilatometry methods were used to study high temperature behavior of the ceramic material. Special attention was paid to the phase transition between the monoclinic and tetragonal phases. The values of spontaneous strain on the basis of unit cell parameter, obtained by Rietveld refinement, have been calculated as well as Landau order parameter. The thermal expansion coefficient (TEC) of La0.98Mg0.02NbO4 was determined to be 12×10−6 1/K and 8×10−6 1/K below and above 500 °C, respectively.

Cytowania

1 4

CrossRef
0

Web of Science
1 6

Scopus

Autorzy (4)

Aleksandra Dorota Mielewczyk-Gryń dr hab. inż.
Katarzyna Gdula-Kasica dr inż.
Bogusław Kusz prof. dr hab. inż.
Maria Gazda prof. dr hab. inż.

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

pełna treść artykułu zobacz w serwisie zewnętrznym otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:: Publikacja w czasopiśmie
Typ:: artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:: CERAMICS INTERNATIONAL nr 39, wydanie 4, strony 4239 - 4244,
ISSN: 0272-8842
Język:: angielski
Rok wydania:: 2012
Opis bibliograficzny:: Mielewczyk-Gryń A., Gdula-Kasica K., Kusz B., Gazda M.: High temperature monoclinic-to-tetragonal phase transition in magnesium doped lanthanum ortho-niobate// CERAMICS INTERNATIONAL. -Vol. 39, iss. 4 (2012), s.4239-4244
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ceramint.2012.09.102
Weryfikacja:: Politechnika Gdańska