Porous CaTi0.9Fe0.1O3-δ (CTF) perovskites were synthesized by the standard solid state method at different sintering temperatures with carbon black (CB), corn starch (CS) and potato starch (PS) as pore-forming agents. The ceramic samples of porosity between 9% and 42% with 5 - 40 μm pore sizes, were obtained by a 6 h sintering at either 1130º C or 1200º C of precursor powder prepared at 1470º C. X-ray diffraction analysis proved the existence of orthorhombic single-phase perovskites crystalline structure. Electrical conductivity at 800° C was between 1.42 ×10−2 S cm−1 and 1.86×10−3 Scm−1 . The conductivity markedly depended on the sample porosity. It should be noted that 30% of porosity, resulted in reduction of conductivity by less than one order of magnitude. Activation energy of conductivity varied between 0.41 and 0.56 eV. Cornstarch has been chosen as the most suitable pore-forming agent for obtaining the cathode of good properties. The best amount of the cornstarch has been proposed as between 5 and 10%.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (5)
-
Aleksandra Mielewczyk-Gryn
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/v10077-011-0006-8
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Advances in Materials Science
nr 11,
strony 55 - 63,
ISSN: 1730-2439 - Język:
- angielski
- Rok wydania:
- 2011
- Opis bibliograficzny:
- Lendze T., Mielewczyk-Gryn A., Gdula-Kasica K., Kusz B., Gazda M.: Influence of pore formers on electrical properties of CaTi0.9Fe0.1O3-δ perovskite-type ceramics// Advances in Materials Science. -Vol. 11., nr. nr 1 (2011), s.55-63
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/v10077-011-0006-8
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 109 razy
Publikacje, które mogą cię zainteresować
Proton conductivity in multi-component ABO4-type oxides
- A. A. Elameen,
- A. Dawczak,
- T. Miruszewski
- + 2 autorów
Electrical and structural properties of Nb-doped SrTiO3
- J. Karczewski,
- B. Bochentyn,
- M. Gazda
- + 2 autorów
New synthesis route of highly porous InxCo4Sb12 with strongly reduced thermal conductivity
- N. Gostkowska-Lekner,
- B. Trawinski,
- A. Kosonowski
- + 5 autorów
Electrical conductivity of nanostructured acceptor-doped ceria fabricated by spark plasma sintering (SPS)
- A. Kabir,
- S. Colding-Jørgensen,
- S. Molin
- + 1 autorów