Performance of LaNi 1-x Co x O 3−δ (LNC) (x=0.4 to 0.7) as a cathode in solid oxide fuel cell (SOFC) is evaluated. Symmetrical cathode/electrolyte/cathode cells for electrochemical testing are prepared by infiltration of yttria stabilized zirconia (YSZ) backbone with LNC solutions. It is showed that the cathode infiltrated with LaNi 0.5 Co 0.5 O 3−δ (LNC155) has the lowest polarization resistance and activation energy, 197 mΩ cm 2 at 600 °C and 0.91 eV, respectively. Therefore it is the most promising material of the LNC group for electrochemical applications. X-ray diffraction analysis revealed that none of the materials is single-phased after heat treatment at 800 °C as they contain residues of La 2 O 3 and La 2 NiO 4−δ
Cytowania
-
2
CrossRef
-
0
Web of Science
-
3
Scopus
Autorzy (3)
-
Simona Ovtar dr
- Technical University of Denmark Department of Energy Conversion and Storage
-
Ming Chen
- Technical University of Denmark Department of Energy Conversion and Storage
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Aktywność konferencyjna
- Typ:
- materiały konferencyjne indeksowane w Web of Science
- Tytuł wydania:
- 39th International Microelectronics and Packaging IMAPS Poland 2015 Conference strony 1 - 7
- ISSN:
- 1757-8981
- Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Chrzan A., Ovtar S., Chen M..: LaNi1-xCoxO3-δ(x=0.4 to 0.7) cathodes for solid oxide fuel cells by infiltration, W: 39th International Microelectronics and Packaging IMAPS Poland 2015 Conference, 2015, IOP PUBLISHING LTD,.
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1088/1757-899x/104/1/012019
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 115 razy
Publikacje, które mogą cię zainteresować
Nanocrystalline cathode functional layer for SOFC
- A. Chrzan,
- J. Karczewski,
- D. Grudzień
- + 1 autorów
Characteristics of LaCo 0.4 Ni 0.6-x Cu x O 3-δ ceramics as a cathode material for intermediate-temperature solid oxide fuel cells
- Y. Liu,
- S. Wang,
- Y. Hsu
- + 2 autorów
High-performance NdSrCo2O5+δ–Ce0.8Gd0.2O2-δ composite cathodes for electrolyte-supported microtubular solid oxide fuel cells
- S. Wang,
- Y. Hsu,
- Y. Liao
- + 2 autorów