The aim of this study was to investigate the effect of three different nanofillers on the properties of rigid polyurethane foams, which were prepared by a one-step, laboratory-scale method from a two-component system at the ratio of NCO groups to OH groups equaled to 2. The reaction mixture consisted of the proper amounts of the commercial oligoether polyol, catalysts, water, nanoclays, and polymeric diphenylmethane diisocyanate. Three types of montmorillonite were used as clay component, i.e., montmorillonite modified by methyl tallow bis-2-hydroxyethyl ammonium (Cloisite VR 30B), a synthetic layered silicate (Laponite VR RD), and an aluminium phyllosilicate absorbent, essentially impure clay consisting mostly of montmorillonite (Bentonite). Thermal properties of rigid polyurethane foams and nanocomposite foams were investigated by dynamical thermal analysis, thermogravimetry, oxygen index, and thermal conductivity measurements. It has been shown that the foams modified by selected nanofillers are characterized by high mechanical strength, as well as improved fire barrier properties.
Cytowania
-
3 8
CrossRef
-
0
Web of Science
-
4 0
Scopus
Autorzy (5)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF APPLIED POLYMER SCIENCE
nr 130,
wydanie 4,
strony 2272 - 2281,
ISSN: 0021-8995 - Język:
- angielski
- Rok wydania:
- 2013
- Opis bibliograficzny:
- Danowska M., Piszczyk Ł., Strankowski M., Gazda M., Haponiuk J.: Rigid polyurethane foams modified with selected layered silicate nanofillers// JOURNAL OF APPLIED POLYMER SCIENCE. -Vol. 130, iss. 4 (2013), s.2272-2281
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1002/app.39432
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 155 razy