Abstrakt
The study presents the results of the research on the rate of fatigue crack growth subjected to bending in the ferritic-pearlitic structure. The studies were carried out at a constant amplitude of the moment and at various values of the load ratios R and at the operating frequency of the machine of 28.4 Hz. Flat specimens made of S355 steel and with fillet welds and with double-sided blunt external notches as well as concave and convex welds were tested. The tests were performed on specimens without and after relief annealing. The study showed that the heat treatment had an influence on the dispersion of the test results described by the energy parameter. It was also observed that the effect of the applied treatment increased the rate of fatigue crack growth.
Cytowania
-
6
CrossRef
-
0
Web of Science
-
8
Scopus
Autorzy (6)
-
Dariusz Rozumek
-
Janusz Lewandowski
-
Grzegorz Lesiuk
-
Zbigniew Marciniak
-
José A.F.O. Correia
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
THEORETICAL AND APPLIED FRACTURE MECHANICS
nr 121,
ISSN: 0167-8442 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Rozumek D., Lewandowski J., Lesiuk G., Marciniak Z., Correia J. A., Macek W.: The energy approach to fatigue crack growth of S355 steel welded specimens subjected to bending// THEORETICAL AND APPLIED FRACTURE MECHANICS -Vol. 121, (2022), s.103470-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.tafmec.2022.103470
- Źródła finansowania:
-
- COST_FREE
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 48 razy
Publikacje, które mogą cię zainteresować
Kinetics of Intermetallic Phase Precipitation in Manual Metal Arc Welded Duplex Stainless Steels
- M. Orłowska,
- K. Pańcikiewicz,
- A. Świerczyńska
- + 1 autorów
On the use of the cumulative strain energy density for fatigue life assessment in advanced high-strength steels
- R. Branco,
- R. F. Martins,
- J. A. Correia
- + 3 autorów
Rheology of Variable Viscosity‐Based Mixed Convective Inclined Magnetized Cross Nanofluid with Varying Thermal Conductivity
- A. Darvesh,
- T. Sajid,
- W. Jamshed
- + 6 autorów