In this study, polyurethanes (PU) were synthesized from oligomeric dihydroxy(etylene-butylene adipate), poly(ethylene glycol) (PEG), hexamethylene diisocyanate (HDI), 1,4-butanediol (BDO) as chain extender and stannous octoate as catalyst. PEG due to its hydrophilic character influences physical and chemical properties of PU. For testing were used PU having the following weigh contents of PEG: 0%, 7%, and 14%. Porous scaffolds were prepared by the method of solvent casting and particulate leaching. The materials were subjected to miscoscopic analysis. Porosity and pore morphology were evaluated. Based on the results from experimental data, it was found that PEG influences the pore's morphology of the obtained scaffold. The scaffold containing 7% wt. of PEG showed optimal properties for tissue engineering.
Cytowania
-
2
CrossRef
-
0
Web of Science
-
0
Scopus
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja monograficzna
- Typ:
- rozdział, artykuł w książce - dziele zbiorowym /podręczniku w języku o zasięgu międzynarodowym
- Język:
- angielski
- Rok wydania:
- 2019
- Opis bibliograficzny:
- Kucińska-Lipka J., Janik H., Sulowska A., Haryńska A., Szarlej P.: The Influence of PEG on Morphology of Polyurethane Tissue Scaffold// / : , 2019, s.323-331
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1201/9780429425301
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 118 razy