Abstrakt
Formation of plasmonically active silver, copper and composite silver-copper nanostructures were studied in this paper. Metallic nanostructures were fabricated by thermal disintegration, so called dewetting, of the thin films in an argon atmosphere. The formation process of the nanostructures was in-situ observed by a novel method, based on resistance measurements. The influence of the material and thickness of the initial thin film on temperature of their disintegration was investigated. Electrical measurements were validated by scanning electron microscopy observations, while metallic the behavior of nanostructures was studied by XPS method. The formation of silver-copper nanocomposite structures was confirmed by UV–vis spectroscopy. Plasmon resonance with two characteristic peaks for nanocomposite structures was observed.
Cytowania
-
3
CrossRef
-
0
Web of Science
-
3
Scopus
Autorzy (7)
-
-
Piotr Winiarz
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1038/s41598-023-37343-2
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Scientific Reports
nr 13,
ISSN: 2045-2322 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Łapiński M., Kozioł R., Skubida W., Winiarz P., Mahjoub Yahia Elhassan R., Sadowski W., Kościelska B.: Transformation of bimetallic Ag–Cu thin films into plasmonically active composite nanostructures// Scientific Reports -Vol. 13,iss. 1 (2023), s.10107-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1038/s41598-023-37343-2
- Źródła finansowania:
-
- IDUB
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 94 razy