The microstructures, water absorption as well as blistering was studied for bi- and tri- axial glass fibre vinyl ester and polyester -matrix laminates coated with gel coat layer and uncoated. The effect of manufacturing technique on water sorption characteristics was considered. It was found that water sorption characteristics of GFRP depend on manufacturing methods. The least water intake was found for specimens having perfect microstructure due to manufacturing by infusion process. Water sorption saturation value was reached after ca. 50 days of accelerated test at 70°C and was found to correspond to 250 days conditioning at 20°C. Blistering evolution was illustrated and SEM images shown corresponding to degradation of the gel coat layer and the laminate during the exposure in water.
Cytowania
-
2
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (3)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/v10077-012-0013-4
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Advances in Materials Science
nr 12,
strony 23 - 29,
ISSN: 1730-2439 - Język:
- angielski
- Rok wydania:
- 2012
- Opis bibliograficzny:
- Landowski M., Budzik M., Imielińska K.: Water sorption and blistering of GFRP laminates with varying structures// Advances in Materials Science. -Vol. 12., nr. 4 (2012), s.23-29
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/v10077-012-0013-4
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 115 razy