Lanthanum investigations in ceramics annealed in a dry and wet atmosphere
Dane BadawczeCeramics based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by standard solid state reaction from oxides and carbonate powders. After sintring, samples were annealed for 2 hours or 72 hours at 300 Celsius degree in a both: wet and dry atmosphere. Results of annealing on a chemical composition and valence state of lanthanum were observed...
-
Valence state of Manganium in a MnCoO ceramics
Dane BadawczeManganium -cobalt based ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. In order to determine valence states of the Mn, X-Ray photoemission...
-
Investigations of the valence state of Co in a MnCoO ceramics
Dane BadawczeMcCoO ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. Chemical behaviour of the Cobaltium was measured by XPS method. The analyses were...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials synthesized via the solid state reaction method
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
Study of the chemical state of Gd in a Ba-La-Gd-Co based ceramic
Dane BadawczeBarium, Lanthanum, Gadolinium and Cobaltium precursors were used for production of ceramic materials. Samples were produced by standard solid state reaction. Samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing on a Gadolinum were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology....
-
The XAS spectra of O-K edges, Fe-L edges in pristine, La-, and Nb-doped SFM in 3 states: as-prepared, reduced and reoxidized
Dane BadawczeThis dataset contains the normalized and exported to *.txt spectra for x-ray absorption spectroscopy. The samples analyzed were strontium ferrite molybdate based, doped with lanthanum and niobium. The powders were measured in as-prepared state (denoted in filename as AP), reduced (red) and reoxidized (reox). The filenames are written accordingly: Edge_(optional:...
-
Influence of the annealing condictions on the chemical structure of LaBaGdCo ceramics
Dane BadawczeCeramic samples based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by solid state reaction. After sintring in a furnance, samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology. XPS analysis...
-
SEM images of SFM, LSFM and SFMNb in as-prepared state and reduced
Dane BadawczeThis dataset contains SEM images taken for pristine strontium ferrite molybdate, as well as ones doped with lanthanum or niobium. Materials were characterized in powder, under high vacuum in secondary electron mode. The images are divided into folders for as-prepared samples and reduced (H2, 800 deg, 4 h) ones.
-
X-Ray photoemission spectroscopy measurements of the Nb-V-Sr-O ceramics
Dane BadawczeNiobium doped strontium vanadate based perovskite SrV1-xNbxO3-δ materials were prepared via conventional solid state reaction (SSR) method. For comparison, different samples with a various amount of niobium dopant in the structure were synthesized; x = 0; 0,2; 0,5; 0,8 and 1. Samples were sintered by two-steps: first under a pure hydrogen (purity >99.999%)...
-
Analysis of the properties of the YSTF ceramics materials before and after reduction
Dane BadawczeThe valence of titanium in reduced YSTF ceramics materials was investigated. Ceramics were reduced by annealing in a hydrogen atmosphere. For comparison unreduced sample was also measured. Valance state was measured by XPS method.
-
SPTNO ceramics measured by XPS method
Dane BadawczeSPTNO (Sr-Pr-Ti-Ni-O) ceramic were manufactured by solid state reaction, from oxides compounds. Synthesis conducted in air atmosphere at temperature in a range of 800-900 deg. Chemical composition of prepared materials were measured by XPS (X-Ray photoemision spectroscopy) method. UHV OmicronNanotechnology system with 128 channel Argus hemispherical...
-
Chemical composition of La-Sr-Ce-Ni-Ti ceramics material measured by XPS method
Dane BadawczeLa-Sr-Ce-Ni-Ti (LSCNT) based ceramics sample was manufactured by standard solid state reaction.Prepared powder was pressed into pilled and sintered in a furnace in air atmosphere for 10h. Annealing temperature was 1200 Celsius degree. To calculate chemical composition and determine valence states of the elements, X-Ray photoemission spectroscopy (XPS)...
-
X-ray diffraction patterns of BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Dane BadawczeThe dataset consists of three raw X-ray diffraction (XRD) files collected using a Phillips X’Pert Pro diffractometer (CuKα radiation (𝜆 = 1.541 Å), under 40 kV and 30 mA). The diffraction patterns of BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were collected at room temperature. Collected...
-
The structure of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing Bi2VO5.5 nanocrystallites was measured by XRD.
-
The luminescence study of (C10H16N)2MnBr4 Organic–Inorganic Hybrid
Dane BadawczeOrganic–inorganic hybrid metal halides have recently attracted attention in the global research field for their bright light emission, tunable photoluminescence wavelength, and convenient synthesis method. This study reports the detailed properties of (C10H16N)2MnBr4, which emits bright green light with a high photoluminescence quantum yield. Results...
-
Chemical composition analysis of the LSNO ceramics
Dane BadawczeThe chemical composition of a series of La-Sb-Nb-O ceramics manufactured by the solid-phase reaction method was analyzed. The samples with a various antimony content were measured by XPS method (OmicronNanotechnology UHV system). Analysis confirmed presence of elements: La, Sb, Nb.
-
The luminescence study of Sr2TiO4:Sm3+ coumpounds.
Dane BadawczeA luminescent material based on the strontium orthotitanate (Sr2TiO4) matrix doped with 1% of a mole of samarium was obtained using the typical solid-state synthesis method under a neutral atmosphere of nitrogen. The sample was investigated using powder X-ray diffraction (XRD) and several luminescence techniques to study the phase composition, luminescence...
-
The topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with SEM method
Dane BadawczeThe topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by SEM.
-
XPS analysis of strontium titanate ceramics
Dane BadawczeThe chemical composition of the strontium titanite doped with yttrium and iron ceramic samples was investigated. Samples of Y0.07Sr0.93Ti0.8Fe0.2 were prepared by solid phase reaction and sintered for 24 and 48 hours. Chemical composition was measured by UHV OmicronNanotechnology XPS system. The analysis confirmed the chemical composition of the ceramics...
-
Thermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by DSC.