The XRD diffraction patterns of Ce0.8La0.2O2 and CeO2 prepared using soft template method
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s and CeO2-s nanopowders (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC, centrifuged...
-
The SEM images of Ce0.8La0.2O2 nanopowder prepared using soft template method
Dane BadawczeThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed...
-
The XRD diffraction patterns of Ce0.8La0.2O2/Ni prepared using soft template method and impregnation
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s nanopowders (nanoparticles,nanocatalyst) prepared using soft template method and further impregnated with 10wt.%Ni using aqueous nitrate solution.
-
The SEM images of Ce0.8La0.2O2 nanocatalyst infiltrated with 10wt.% Ni prepared using soft template method
Dane BadawczeThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method and infiltrated to 10wt.% Ni in the catalyst. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 25xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method - 50xCMC
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 50xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using modified Pechini/EDTA method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using modified Pechini method consisting of CA (citric acid), PEG (propylene glycol) and EDTA. Exact amount of metal nitrates were dissolved in water followed by addition of gelling agents and heated to 100C. Obtained gel was calcined at 600C for 4h. The powder...