Wyszukiwarka
Nie znaleźliśmy wyników w zadanych kryteriach!
Ale mamy wyniki w innych katalogach.Filtry
wszystkich: 4269
-
Katalog
- Publikacje 3240 wyników po odfiltrowaniu
- Czasopisma 151 wyników po odfiltrowaniu
- Osoby 128 wyników po odfiltrowaniu
- Projekty 4 wyników po odfiltrowaniu
- Aparatura Badawcza 2 wyników po odfiltrowaniu
- Kursy Online 16 wyników po odfiltrowaniu
- Wydarzenia 3 wyników po odfiltrowaniu
- Dane Badawcze 725 wyników po odfiltrowaniu
wyświetlamy 1000 najlepszych wyników Pomoc
Wyniki wyszukiwania dla: nanotubular layers
-
Self-Organized Nanotubular Oxide Layers on Ti and Ti Alloys
PublikacjaTo improve bioactivity of titanium and titanium, the implant surface modification by formation of self-organized TiO2 nanotube arrays with electrochemical techniques is presented. The influence of electrolyte composition and deposition parameters during anodization is characterized. The enhancement of phosphates deposition by titanium nanotubular structure is discussed. The calcium phosphate ceramics is shown to be uniformly deposited...
-
Formation of High Corrosion Resistant Nanotubular Layers on TitaniumAlloy Ti13Nb13Zr
PublikacjaThis paper presents results of oxidation tests and corrosion investigations of titanium alloy Ti13Nb13Zr performed at different conditions. The oxide layers have been formed by electrochemical method in 2M H3PO4 + 0.3% HF solution for 30 min. and 1 h at 20 V constantvoltage. The corrosion tests have been made by potentiodynamic method in Ringer`s solution at pH ranged between 3 and 7. It has been shown that the nano-oxide films,...
-
Formation of High Corrosion Resistant Nanotubular Layers on TitaniumAlloy Ti13Nb13Zr
PublikacjaThis paper presents results of oxidation tests and corrosion investigations of titanium alloy Ti13Nb13Zr performed at different conditions. The oxide layers have been formed by electrochemical method in 2M H3PO4 + 0.3% HF solution for 30 min. and 1 h at 20 V constantvoltage. The corrosion tests have been made by potentiodynamic method in Ringer`s solution at pH ranged between 3 and 7. It has been shown that the nano-oxide films,...
-
Morphology and properties of nanotubular oxide layer on the Ti13Zr13Nb alloy
PublikacjaThe Ti13Zr13Nb alloy in solid and porous form was oxidised. The constant voltage 20 V, oxidation time 0.5 and 1 h, and 1 M H3PO4 (orthophosphoric acid) with addition of HF (hydrofluoric acid) as a test solution were applied. SEM (Scanning Electron Microscope) examinations of surface, EDS (Energy Dispersive X-ray Spectroscopy) chemical analysis, nanohardness and nano-scratch tests, and corrosion potentiokinetic tests at various...
-
Nanotubular Ti Oxide Layers for Enhancement of Bone-Implant Bonding and Bioactivity
PublikacjaAbstrakt artykułu pt. ''Nanotubular Ti Oxide Layers for Enhancement of Bone-Implant Bonding and Bioactivity''. The paper describes techniques to improve the bioactivity of titanium and ehnahnce the bone-implant bonding ability by the electrochemical anodization to fabricate titania nanotubular oxide layer.
-
Nanotubular oxide layers and hydroxyapatite coatings on porous titanium alloy Ti13Nb13Zr
PublikacjaThe surface condition of an implant has a significant impact on response occurring at the implant-biosystem border. The knowledge of physical-chemical and biological processes allows for targeted modification of biomaterials to induce a specified response of a tissue. The present research was aimed at development of technology composing of obtaining the nanotube oxide layers on a porous titanium alloy Ti13Nb13Zr, followed by the...
-
Nanotubular oxide layers and hydroxyapatite coatings on ‘Ti–13Zr–13Nb’ alloy
PublikacjaThe presented research was aimed to determine the mechanical properties of the nanotubular oxide layer covered with hydroxyapatite coating. The Ti–13Zr–13Nb alloy was oxidised in 1M phosphoric acid with an addition of 0?5% HF for HF solution at 20 V voltage. The electrochemically assisted deposition of hydroxyapatite was performed at cyclic polarisation in NH4H2PO4 and CaCl2 solution at 80uC. The mechanical properties were determined...
-
Nanotubular Titanium Oxide Layers for Enhancement of Bone-Implant Bonding and Bioactivity
PublikacjaThe present paper describes the techniques to improve the bioactivity of titanium and enhance the bone-implant bonding ability by the electrochemical anodization to fabricate titania nanotube arrays (TiO2).
-
The influence of implantation on mechanical degradation of the nanotubular oxide layer on titanium screws
Publikacja -
Nanotubular Oxide Layer Formed on Helix Surfaces of Dental Screw Implants
PublikacjaSurface modification is used to extend the life of implants. To increase the corrosion resistance and improve the biocompatibility of metal implant materials, oxidation of the Ti-13Nb- 13Zr titanium alloy was used. The samples used for the research had the shape of a helix with a metric thread, with their geometry imitating a dental implant. The oxide layer was produced by a standard electrochemical method in an environment of...