Substrate characterization in a electrochemically derived Manganium-Cobaltium thin films
Open Research DataManganium-Cobaltium thin films were electrochemically deposited on a Ni foams subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
Mn-Co nanofilms on nickel foam measured by XPS mehod
Open Research DataManganium-Cobaltium based thin films were electrochemically deposited on a Ni based subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
Ultrasonic wave propagation and digital image correlation measurements of steel bars under 3-point bending
Open Research DataThe DataSet contains the results of the mechanical behaviour of a bar under a 3-point bending test. The bar was made of steel and had a cross-section of 5.96 × 5.96 mm2 and a length of 200 mm. The three-point bending test was performed using a Zwick/Roell Z10 universal testing machine (UTM), with a distance between supports of 12 cm. The parameters...
-
Validation of polyurethane-wood composites properties
Open Research DataThis study focuses on the development of the PU-WC manufacturing method, the determination of properties of this type of composite, and the indication of its potential application. The mechanical properties of PU-WC were characterized by flexural tests. To determine the thermal properties, dynamic mechanical analysis (DMA) and thermogravimetric analysis...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #3)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #1)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #4)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #2)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Displacements of bones during bending test of first metatarsophalangeal joint after arthrodesis with medially or dorsally positioned locking plate and lag screw.
Open Research DataThe Dataset contains the values of displacements of bone control points during the bending test of first metatarsophalangeal (MTP1) joint specimens after arthrodesis.
-
Mechanical studies of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains mechanical tests carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was dynamic mechanical analysis (DMA). The measurements...