Rok 2016
-
Influence of Nitriding and Laser Remelting on Properties of Austenitic Stainless Steel Type X10CrNi18-8 and Cavitation Erosion Resistance
PublikacjaThe paper presents properties of surface layers. Surface layers were obtained by using low temperature glow–discharge nitriding process and laser remelting carried out on austenitic stainless steel type X10CrNi18-8. Investigations were done by using an Ultra Nanoindentation Tester (UNHT) in the Warsaw Institute of Fundamental Technological Research. The influence of the above mentioned...
Rok 2013
-
Wpływ azotowania jarzeniowego i laserowego nadtapiania na odporność kawitacyjną stali X5CrNi18-10
PublikacjaNierdzewne stale austenityczne charakteryzują się doskonałą odpornością korozyjną, aczkolwiek niskimi właściwościami mechanicznymi. W wielu przypadkach ogranicza to ich eksploatację w warunkach przemysłowych. Ponadto, nierdzewne stale austenityczne są wrażliwe na korozję lokalną w obecności jonów halogenkowych. Technologie materiałowe, które dają potencjalne możliwości otrzymywania korzystnego wpływu na właściwości mechaniczne...
Rok 2012
-
Cavitation Erosion Resistance of Austenitic Stainless Steel after Glow-Discharge Nitriding Process
PublikacjaThis paper presents investigation of cavitation erosion resistance of nitrided austenitic stainless steel X5CrNi18-10. The diffusion layers were produced by using different parameters of atmosphere (N2:H2). The microstructure, chemical composition and phase identification of the modified layer were examined using scanning electron microscopy, glow-discharge optical emission spectrometer and X-ray diffractometry, respectively. Cavitation...
-
Comparision of mechanical properties of nitrided cases and remelted layers of austenitic stainless steel
Publikacja -
The Influence of Gas Mixture in the Glow-Discharge Nitriding Process of Austenitic Stainless Steel on Characteristic of Nitrided Cases
PublikacjaAustenitic stainless steels characterize with excellent corrosion resistance, although low mechanical properties. In many cases that limits their exploitation in industrial applications. Moreover, austenitic stainless steel is susceptible to local corrosion in the presence of halide ions. In present works, it was emphasized that the nitriding of austenitic stainless steels gives some potential abilities to obtain beneficial effect...
Rok 2011
-
Influence of the laser remelting parameters on the thickness of surface layers created on the stainless steel X5CrNi18-10
PublikacjaIn this work the surface of austenitic stainless steel type X5CrNi18-10 was treated by using laser. Laser remelting was done by means of laser MLT 2500 CO2 with different parameters of treatment: P - power beam (800 [W], 1000 [W], 1100 [W], 1200 [W]); v - scanning velocity (6 [mm/s], 7 [mm/s], 8 [mm/s]); diameter of laser beam (1.4 [mm], 1.6 [mm]). The influence of these parameters on the thickness and shape of layers in manufacturing...
-
Polyethylene as a small vessel's building material
PublikacjaThe most common use of polyethylene we can notice nowadays are areas like water supply systems, gas industry (esp. gas piping), food industry, small-scale, light and consumer goods industries. That material has far more applications. One of them is shipbuilding - especially small inland or offshore vessels.
Rok 2010
-
Assessment of FSW Welds Made of Aluminum Alloy AW7075-T651.
PublikacjaThis paper summarizes the results of experimental studies in which the aluminum alloy AW7075-T651 was friction stir welded (FSW) using various combinations of process parameters (rotational - R and travel speed - T). Mechanical properties of the test welds were assessed by using static tensile test and Vickers hardness measurement. The temperature of the welded plates was monitored during welding by means of thermocouples placed...
-
The Characteristic of Surface Layers on Austenitic Stainless SteelAfter Glow-discharge Nitriding Process.
PublikacjaThis paper presents investigation of surface layers. The diffusion layers were produced by using different parameters of reactive atmosphere (N2:H2). The research of the surface layers was performed using scanning electron microscope (SEM). The results of energy dispersive X-ray (EDX) analysis and X-ray diffraction (XRD) analysis are presented. Research reveals the influence of chemical constitution of reactive atmosphere on the...
Rok 2008
-
Difficulties with evaluating resistance of materials to cavitation.
PublikacjaW pracy dokonano analizy wyników Międzynarodowego Testu Erozji Kawitacyjnej (ICET), któremu koordynował Instytut Maszyn Przepływowych Polskiej Akademii Nauk (IMP PAN) w Gdańsku. Kluczowe parametry wpływające na zmianę przebiegu krzywych erozji uzyskanych na stanowiskach badawczych zostały wskazane. Wykazano konieczność przeprowadzenia badań w zakresie oceny wpływu efektu skali. Zaprezentowano wyniki uzyskane na stanowiskach magnetostrykcyjnych...
Rok 2007
-
Hardness measurements for assessment of cavitation intensity
PublikacjaArtykuł opisuje możliwość zastosowania pomiarów teardości erodowanego materiału do oceny natężenia zjawiska kawitacji. Proponowana metoda zakłada, że cała energia implodujących pęcherzyków kawitacyjnych zamieniana jest na przyrost twardości warstwy wierzchniej materiału
Rok 2006
-
Wpływ stanu warstwy wierzchniej na mikrostrukturę i właściwości korozyjne stopu SUPERSTON = Influence of the state of surface layer on microstructure and corrosion properties of SUPERSTON alloy
PublikacjaW artykule przedstawiono rezultaty nadtapiania laserowego w warunkach kriogenicznych stopu SUPERSTON. Dokonano oceny mikrostruktury powierzchni i przekroju stopu SUPERSTON po obróbce laserowej. Określono właściwości stopu, które porównano ze stanem powierzchni po nadtapianiu oraz nadtapianiu i szlifowaniu.
-
Znaczenie objętości początkowej materiału w przebiegu krzywych erozji kawitacyjnej = Importance of initial volume of material for cavitation erosion curve
PublikacjaW pracy przedstawiono rozważania na temat wpływu wielkości początkowej objętości materiału niszczonego pod wpływem obciążeń kawitacyjnych, na przebieg krzywych erozji tj. ubytku objętości materiału w czasie. Zaproponowano model matematyczny opisu krzywych erozji kawitacyjnej z uwzględnieniem tego wpływu.