FTIR (Fourier-transform infrared spectroscopy) spectra of titanium dioxide coated nickel foams.
Dane BadawczeThis dataset contains FTIR spectra recorded on a JASCO 4200 spectrometer of nickel foams coated with titanium dioxide after heating at 400, 500 and 600 C and after photocatalytic process with NOx.
-
XRD (X-ray Diffraction) of titanium dioxide coated nickel foams
Dane BadawczeThese data include XRD patterns of titanium dioxide coated nickel foams heated at 400, 500 and 600C in argon atmosphere.
-
UV/VIS Spectroscopy of titanium dioxide coated nickel foams
Dane BadawczeThe data includes UV-Vis spectra of titanium dioxide coated nickel foams heated at 400, 500 and 600 C in Ar. Jasco V-650 Spectrophotometer was used and Spectra Measurement software.
-
XPS (X-ray photoelectron spectroscopy) of titanium dioxide coated nickel foams and heated 400,500, 600C
Dane BadawczeThis data set contains XPS spectra recorded for nickel foams coated with titanium dioxide and heated at 400, 500 and 600 degrees celcius.
-
Phototcatalytic oxidation of NO on titanium dioxide coated nickel foams
Dane BadawczeThe results of photocatalytic NO oxidation were compiled in an Excel file. The measurement was carried out using a chemiluminescence NO analyzer.
-
BET (Brunauer-Emmett-Teller) surface area analysis of titanium dioxide coated nickel foams
Dane BadawczeThe data are presented for the BET surface results of nickel foams coated with titanium dioxide and heated 400, 500 and 600 degrees Celsius in an argon atmosphere. N2 sorption was performed at 77 K pore size distribution was determined by BJH and DFT methods.
-
SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of nickel (Ni) foam as received, after photocatalysis and after oxidation at 500_C.
Dane BadawczeThis dataset contains SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of Ni (nickel) foam as received from the supplier, after photocatalytic treatment and after oxidation at 500C. The detailed equipment and measurement data was described in "readme SEM.txt" file
-
AFM (Atomic Force Microscopy) analysis of surface topography loaded with nickel nanoparticles.
Dane BadawczeThis dataset presents AFM (Atomic Force Microscopy) images depicting the surface topography loaded with nickel powdered nanoparticles. The detailed equipment and measurement data was described in "AFM readme.txt" file
-
Photocatalytic degradation of acetaldehyde in high temperature reaction chamber
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using TiO2 (titanium dioxide) as photocatalysts. It includes data on the influence of flow rate, TiO2 (titanium dioxide) filling the entire reactor, a thin layer of TiO2 (titanium dioxide) supported on KBr...
-
Photocatalytic decomposition of acetaldehyde over TiO2 (titanium dioxide) supported on nickel foam and Ni-doped (nickel-doped) TiO2
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using as photocatalytic systems TiO2 (titanium dioxide) supported on nickel foam, TiO2 supported on oxidized nickel foam and TiO2 doped by metallic nickel (Ni) powder. The detailed equipment and measurement...
-
XPS-Ni foam as received, after photocatalysis and after oxidation at 500_C.
Dane BadawczeThis dataset contains XPS spectra recorded for nickel foam as received from supplier, after photocatalytic process and after oxidation at 500C. Each set contains: survery spectrum, O1, C1s, Ni2p. The detailed equipment and measurement data was described in "readme XPS.txt" file
-
SEM-EDS images of expanded polystyrene spheres coated with silicon dioxide (SiO2) and/or titanium dioxide (TiO2)
Dane BadawczeData contain SEM and SEM-EDS images of expanded polystyrene spheres coated with silicon dioxide (SiO2) and/or titanium dioxide (TiO2). The detailed equipment and measurement data was described in measurement info.txt file.
-
Brunauer-Emmett-Teller (BET) surface analysis of titanium dioxide (TiO2) and silicon dioxide (SiO2) used for coating of expanded polystyrene spheres (EPS)
Dane BadawczeData refer to the results of BET surface area of TiO2 and SiO2 powders used for coating of expanded polystyrene spheres. The detailed measurement and equipment data was described in readme BET.txt file.TiO2 was treated firstly in autoclave at 150 C degrees for 1h, then was further heat treated in Ar at 400 C degrees. As a raw material TiO2 was used,...
-
Light transmission measurement through the fluidized bed photoreactor
Dane BadawczeDataset contains light transmission measurements through the fluidized bed photoreactor. Two sources of light were used: UV-LEDs and UV fluorescent. Measurements were performed at different air flows: 0, 80, 160 and 240 ml/min. The detailed measurement and equipment data was described in measurment info.txt file.
-
Photocatalytic ethylene decomposition with the use of fluidized bed photoreactor
Dane BadawczeData contain exported raw data recorded during decomposition of ethylene during utilization of fluidized bed photoreactor equipped with either UV-LEDs or fluorescent UV lamps as well as in either humid or dry conditions. In separate folder, the photographs of the photocatalytic system were included. As photocatalytic material, polystyrene spheres coated...
-
Ethylene photocatalytic decomposition in high temperature reaction chamber
Dane BadawczeData contain data logs of measurements performed on High Temperature Chamber "The Praying Mantis" coupled with SRI 8010 gas chromatograph. Measurement was performed for TiO2 irradiated by UV and under flowing of ethylene gas diluted in air and with the use of elevated temperature.
-
XRD-Ni foam as received and oxidised at 500_C
Dane BadawczeThese data contain XRD patterns of porous nickel foam commercial and oxidised in air at 500 C degrees for 8 hours.
-
TG analyses - content of SiO2 and TiO2 in polystyrene
Dane BadawczeTG analyses were performed for polystyrene spheres coating by SiO2 and then coating by SiO2-TiO2. Thermal analyses of polystyrene spheres only were also performed. The content of inorganic remaining was used for calculation the quantity of coating SiO2 and TiO2 in the polystyrene spheres.
-
TG-hydroxyl groups in TiO2-P25
Dane BadawczeTG analyses were performed for powdered TiO2 - commercial P25 sample, which was heat-treated from room temperature to 500 C in the nitrogen atmosphere. Mass loss at lower temperature such as 120 C was related to the physisorbed water, and that one occurring at 500 C to the chemisorbed hydroxyl groups.
-
TiO2-potential zeta in water
Dane BadawczeData contain results from measurements of zeta potential for powdered TiO2 in a diluted aqueous solution. The measurements were performed in Zetasizer Nano ZS analyser.
-
Photocatalytic decomposition of ethylene on the TiO2-polystyrene spheres
Dane BadawczeData contain results from the measurements of the photocatalytic decomposition of ethylene under UV irradiation with using TiO2 coating on the expanded polystyrene spheres (EPS). EPS-SiO2-TiO2 and EPS-TiO2 were used as the photocatalytic beds in the fluidized bed reactor. Both, stationary and fluidized beds were tested. The comparison of ethylene decomposition...
-
SEM - Expanded polystyrene coated by TiO2 or SiO2-TiO2
Dane BadawczeData contain SEM images taken in SEM Hitachi SU8000 with voltage of 5.0 kV. SEM images show expanded plystyrene spheres coated by a thin layer of TiO2 or bilayer SiO2-TiO2.
-
XRD-TiO2 and SiO2
Dane BadawczeData contain results from XRD measurements of amorphous silica and TiO2 of antase and rutile phases. The commercial TiO2 named as P25 produced by Evonik was also analyzed.
-
Analyses of sulphur in TiO2 by XRFS
Dane BadawczeData contain content of sulphur in TiO2 determined by X-ray fluorescence spectroscopy. The results were obtained by using internal pattern.
-
TiO2-TG analyses -OH groups
Dane BadawczeTG analyses of TiO2 were performed under nitrogen flow to monitor desorption of hydroxyl groups. Physisorbed weak-bonded hydroxyl groups were desorbed totally at around 120oC, whereas chemisorbed ones at around 500oC. The mass loss at these temperatures was used as concentration of hydroxyl groups on TiO2 surface. The amount of analysed TiO2 was 10...
-
XRD-TiO2 heat-treated at 400-600oC in Ar or H2
Dane BadawczeThese data contain XRD patterns of TiO2 heat-treated at 400-600oC in Ar or H2. Two pases of TiO2 were identified: anatase and rutile.
-
Photoluminescence spectra of TiO2
Dane BadawczeThese data contain photoluminescence spectra of TiO2 measured at the temperature of liquid nitrogen. There is a comparison of the photoluminescence spectra of TiO2 heat treated at 400-600oC in the ambient (Ar) and reduced (H2) atmospheres. These emission spectra were recorded after TiO2 excitation with a wavelength of 290 nm
-
EPR of TiO2 hydrogenated at 500 and 600oC
Dane BadawczeData contain EPR spectra of TiO2 (anatase phase) heat treated in H2 at 500 and 600oC. Sample heated at 500oC contained 4 wt% of rutile and that at 600oC 8 wt% of rutile.
-
SEM of TiO2 heated at 400-600oC in Ar or H2
Dane BadawczeData contain some SEM images of TiO2 taken after its heat treatment in Ar or H2 at 400-600oC. Treated TiO2 was crystalline anatase phase with 3-4 % of rutile nclei.
-
BET of TiO2 heated at 400-600 C degrees
Dane BadawczeThese data refer to the results of BET surface area of TiO2, which was treated firstly in autoclave at 150 C degrees for 1h (sample marked as A150), then was further heat treated in Ar or H2 at 400-600 C degrees. As a raw material TiO2 was used, which was a semiproduct from the industrial production of titania white by sulphur method. The raw material...
-
TiO2-zeta potential
Dane BadawczeData contain results from the measurements of zeta potential of TiO2 versus pH. Data are saved as original files and in the format of Excel file. measurements were perfomed in Zetasizer Nano ZS with using Multi-Purpose Titrator MPT-2.
-
Emission spectra of UV and fluorescent lamps
Dane BadawczeData contain emision spectra of two different UV lamps: Special "TL"E 22W/10 Black light (Philips) and Semilac UV, 36 W and also Fluorescent lamp: L22W/840 Circular Cool White, Lumilux (Osram). These spectra were recorded by USB4000 Fiber Optic Spectrometer.
-
Ethylene decomposition on TiO2 - UV and Fluorescence lamp
Dane BadawczeData contain chromatograms recorded during decomposition of ethylene flowing over TiO2 through the quartz tubular shape reactor. TiO2 was coated onto glass plates with dimension of 2cmx2cm, in total 3 plates were used and placed inside reactor. Reactor was irradiated by UV (Special 'TL'E, Philips) or fluorescent (Lumilux, OSRAM) 3 ring-shaped lamps,...
-
Ethylene decomposition on TiO2 under UV
Dane BadawczeData contain chromatograms recorded during decomposition of ethylene over TiO2 in a flow reactor under UV irradiation. Semilac UV lamp with total power of 72 W was used as a source of UV light. Chromatograms were recorded in Trace GC Ultra chromatograph equipped in FID detector. Sampling was realised via the dosing sample loop. TiO2 was coated on the...
-
FTIR in situ - ethylene decomposition on TiO2
Dane BadawczeThese data contain FTIR spectra recorded in FTIR spectrometer Nicolet iS50 coupled with High Temperature Chamber "The Praying Mantis". These spectra were measured for TiO2 irradiated by UV and under flowing of ethylene gas diluted in air. FTIR spectra were measured in situ during the photocatalytic process of ethylene decomposition. In order to identify...
-
UV-Vis-DR-TiO2 heated at 400-600oC in Ar or H2
Dane BadawczeThese data contain UV-Vis/DR spectra of TiO2 heated at 400-600oC in Ar or H2. Transformation of spectra to Kubelka-Munk function was performed together with determination of band gap.
-
FTIR-TiO2 heated at 400-600oC in Ar or H2
Dane BadawczeData contain FTIR diffuse eflectance spectra of TiO2, which was heat-treated at 400-600oC in Ar or H2. Hydrogen reduced TiO2 revealed new bands due to the adsorption of some species on the titania oxygen vacancy sites.
-
XPS-TiO2 heated in H2
Dane BadawczeThese XPS spectra were recorded for TiO2 heat-treated at 450-600oC in H2. Surface oxygen groups were determined. Deconvolution of Ti 2p peak allowed to determine Ti3+ on the titania surface.