Abstrakt
The aim of the conducted research was to develop hybrid nanostructures formed from MnCo2O4 and exfoliated graphite. Carbon added during the synthesis allowed for obtaining a well-distributed MnCo2O4 particle size with exposed active sites contributing to the increased electric conductivity. The influence of the weight ratios of carbon to a catalyst for hydrogen and oxygen evolution reactions was investigated. The new bifunctional catalysts for water splitting were tested in an alkaline medium with excellent electrochemical performance and very good working stability. The results for hybrid samples show better electrochemical performance compared to the pure MnCo2O4. The highest electrocatalytic activity was for sample MnCo2O4/EG (2/1), where the value of the overpotential was 1.66 V at 10 mA cm−2, and also for this sample a low value of Tafel slope (63 mV dec−1) was denoted.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (6)
-
Malgorzata Skorupska
-
Kinga Kowalska
-
Magdalena Tyc
-
Anna Ilnicka
-
Jerzy P. Lukaszewicz
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1039/D3RA00589E
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
RSC Advances
nr 13,
strony 10215 - 10220,
ISSN: 2046-2069 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Skorupska M., Kowalska K., Tyc M., Ilnicka A., Szkoda M., Lukaszewicz J. P.: Exfoliated graphite with spinel oxide as an effective hybrid electrocatalyst for water splitting// RSC Advances -,iss. 15 (2023), s.10215-10220
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1039/d3ra00589e
- Źródła finansowania:
-
- COST_FREE
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 29 razy
Publikacje, które mogą cię zainteresować
Synergistic effects of nitrogen-doped carbon and praseodymium oxide in electrochemical water splitting
- P. Grabowska,
- M. Szkoda,
- M. Skorupska
- + 2 autorów
Powering the Future by Iron Sulfide Type Material (FexSy) Based Electrochemical Materials for Water Splitting and Energy Storage Applications: A Review
- A. Farhan,
- W. Qayyum,
- U. Fatima
- + 7 autorów
Bismuth-based nanomaterials-assisted photocatalytic water splitting for sustainable hydrogen production
- Z. Saddique,
- M. Imran,
- A. Javaid
- + 5 autorów