Abstrakt
Cold-spray coatings were produced by FeCoCrNiMn high-entropy alloy powders deposited on carbon steel substrate. The coatings were realized at intermediate temperature and high pressure (at 1100 °C and 7 MPa). The coating microstructure was characterized by scanning electron microscopy and X-ray diffraction, revealing a very dense deposition and high flattening ratio of the splatted particles. This had a large influence on the strong adhesion of the mcoating to the substrate. The hardness and residual stress profiles were measured through nanoindentation and X-ray diffraction from the peak broadening measured layer by layer. The cyclic behavior of the coatings was evaluated through three-point bending tests performed on V-notched samples coated via cold spray. Cyclic tests were performed at different maximum strokes from 0.3 to 3.6 mm in order to monitor the crack initiation and propagation during bending tests. The fracture surface aspect was analyzed by scanning electron microscopy in order to reveal the fracture mechanisms in different deformation conditions.
Cytowania
-
5
CrossRef
-
0
Web of Science
-
4
Scopus
Autorzy (6)
-
Pasquale Cavaliere
- Department of Innovation Engineering, University of Salento
-
Angelo Perrone
- Department of Innovation Engineering, University of Salento
-
Alessio Silvello
- Thermal Spray Center CPT, Universitat de Barcelona
-
Gianni Blasi
- Department of Innovation Engineering, University of Salento
-
Irene G. Cano
- Thermal Spray Center CPT, Universitat de Barcelona
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/met12050780
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Metals
nr 12,
ISSN: 2075-4701 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Cavaliere P., Perrone A., Silvello A., Laska A., Blasi G., Cano I. G.: Fatigue Bending of V-Notched Cold-Sprayed FeCoCrNiMn Coatings// Metals -Vol. 12,iss. 5 (2022), s.780-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/met12050780
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 156 razy
Publikacje, które mogą cię zainteresować
Cyclic behavior of FeCoCrNiMn high entropy alloy coatings produced through cold spray
- P. Cavaliere,
- A. Perrone,
- A. Silvello
- + 5 autorów