High temperature corrosion evaluation and lifetime prediction of porous Fe22Cr stainless steel in air in temperature range 700–900 °C
Abstrakt
This work describes a high temperature corrosion kinetics study of ~30% porous Fe22Cr alloys. The surface area of the alloy (~0.02 m2 g-1) has been determined by tomographic microscopy. The weight gain of the alloys was studied by isothermal thermogravimetry in the air for 100 hours at 700 - 900 °C. Breakaway oxidation was observed after oxidation at 850 °C (~100 hours) and 900 °C (~30 hours). The lifetime prediction shows the investigated porous alloy can be used for >3000 hours at temperatures <700 °C. At temperatures ≥700 °C, the lifetime of the porous alloy is limited by the available chromium reservoir.
Cytowania
-
3 7
CrossRef
-
0
Web of Science
-
2 5
Scopus
Autorzy (6)
-
Małgorzata Makowska Dr.
-
F. Marone
Cytuj jako
Pełna treść
pobierz publikację
pobrano 113 razy
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
CORROSION SCIENCE
nr 189,
ISSN: 0010-938X - Język:
- angielski
- Rok wydania:
- 2021
- Opis bibliograficzny:
- Koszelow D., Makowska M., Karczewski J., Jasiński P., Marone F., Molin S.: High temperature corrosion evaluation and lifetime prediction of porous Fe22Cr stainless steel in air in temperature range 700–900 °C// CORROSION SCIENCE -Vol. 189, (2021), s.109589-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.corsci.2021.109589
- Źródła finansowania:
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 153 razy