Hydroxyapatite deposition on the laser modified Ti13Nb13Zr alloy

Abstrakt

The Ti13Nb13Zr alloy was subjected to laser modification with the Nd:YAG laser provided that such treatment would increase the surface roughness followed improved adhesion of hydroxyapatite (HAp) coatings The hydroxyapatite was deposited by electrophoretic method in suspension of 0.5 g HA powder and 100 ml ethyl alcohol. The deposition was carried out for 10 min at 10 V voltage followed by drying at room temperature for 24 h and heating at 800°C for 1 h in vacuum. The thickness of the HAp coatings was found as of about 4.06 µm to 9.05 µm. The examinations of surfaces were carried out at each stage of the experiment with the ultra-high resolution scanning electron microscope. The measurements of surface roughness after laser treatment and after HAp deposition were performed with the Hommel Etamic Waveline profilograph.

Cytowania

  • 1 0

    CrossRef

  • 1 2

    Web of Science

  • 0

    Scopus

Cytuj jako

Pełna treść

pobierz publikację
pobrano 68 razy
Wersja publikacji
Accepted albo Published Version
Licencja
Creative Commons: CC-BY-NC-ND otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
Opublikowano w:
Advances in Materials Science nr 17, wydanie 4, strony 5 - 13,
ISSN: 1730-2439
Język:
angielski
Rok wydania:
2017
Opis bibliograficzny:
Jażdżewska M., Majkowska-Marzec B.: Hydroxyapatite deposition on the laser modified Ti13Nb13Zr alloy// Advances in Materials Science. -Vol. 17., iss. 4 (2017), s.5-13
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1515/adms-2017-0017
Bibliografia: test
  1. Zielinski A., Sobieszczyk S., Seramak T., Serbinski W., Swieczko-Zurek B., Ossowska A.: Biocompatibility and bioactivity of load-bearing metallic implants, Adv. Mater. Sci. 10 (2011) 21-31. otwiera się w nowej karcie
  2. Wang D., Wu G., Lin X. Liu Y.: Surface coating and modification of metallic biomaterials (2015) 345-358. otwiera się w nowej karcie
  3. Palanivelu R., Kalainathan S., Kumar A.: Characterization studies on plasma sprayed (AT/HA) bi-layered nanoceramics coating on biomedical commercially pure titanium dental implant, Ceram. Int. 40 (2014) 7745-7751. otwiera się w nowej karcie
  4. Vasilescu C., Drob P., Vasilescu E., Demetrescu I., Ionita D., Prodana M., Drob S.: Characterization and corrosion resistance of the electrodeposited hydroxyapatite and bovine serum albumin/hydroxyapatite films on Ti-6Al-4V-1Zr alloy surface, Corros. Sci. 53 (2011) 992-999. otwiera się w nowej karcie
  5. Barry J. N., Twomey, B., Cowley, A., O'Neill, L., McNally, P.J., Dowling, D.P.: Evaluation and comparison of hydroxyapatite coatings deposited using both thermal and non-thermal techniques, Surface and Coatings Technology 226 (2013) 82 -91. otwiera się w nowej karcie
  6. Mohseni E., Zalnezhad E., Bushroa A. R.: Comparative investigation on the adhesion of hydroxyapatite coating on Ti-6Al-4V implant, International Journal of Adhesion & Adhesives 48 (2014) 238 -257. otwiera się w nowej karcie
  7. Fernandez-Pradas J.M. et all.: Characterization of calcium phosphate coatings deposited by Nd:YAG laser ablation at 355 nm; influence of thickness, Biomaterials 23 (2002) 1989 -1894. otwiera się w nowej karcie
  8. Kwok C.T. et al.: Characterization and corrosion behavior of hydroxyapatite coatings on Ti6Al4V fabricated by electrophoretic deposition, Applied Surface Science 255 (2009) 6736- 6744. otwiera się w nowej karcie
  9. Meng X., Tae-Yub Kwon T.-Y., Kim K.-H.: Hydroxyapatite coating by electrophoretic deposition at dynamic voltage, Dental Materials Journal 27(5) (2008) 666 671. otwiera się w nowej karcie
  10. Bartmanski M., Cieslik B., Glodowska J., Kalka P., Pawlowski L, Pieper M., Zielinski A.: Electrophoretic deposition (EPD) of nanohydroxyapatite -nanosilver coatings on Ti13Zr13Nb alloy, Ceramics International 43 (15) (2017) 11820-11829. otwiera się w nowej karcie
  11. Bartmanski M., Berk A., Wojcik A.: Advances in Materials Science 16 No. 3 (49) (2016) 56 -66. otwiera się w nowej karcie
  12. Wennerberg A., Albrektson T.: Effects of titanium surface topography on bone integration: a systematic review, Clin. Oral Implants Res. 20 (4) 2009) 172 -184. otwiera się w nowej karcie
  13. Le Guéhennec L., Soueidan A., Layrolle P., Amouriq Y.: Surface treatments of titanium dental implants for rapid osseointegration. Dent. Mater. 23 (2007) 844 -854. otwiera się w nowej karcie
  14. Schuler M., Owen G.R., Hamilton D.W., de Wild M., Textor M., Brunette D.M., Tosatti S.G.: Biomimetic modification of titanium dental implant model surfaces using the RGDSP-peptide sequence: a cell morphology study, Biomaterials 27 (21) (2006) 4003 -4015. Brought to you by | Gdansk University of Technology otwiera się w nowej karcie
  15. Zieliński A., Jażdżewska M., Łubiński J., Serbiński W.: Effects of laser remelting at cryogenic conditions on microstructure and wear resistance of the Ti6Al4V alloy applied in medicine, Solid State Phenomena 183 (2012) 215 -224. otwiera się w nowej karcie
  16. Majkowska B., Jażdżewska M., Wołowiec E., Piekoszewski W., Klimek L., Zieliński A.: The possibility of use of laser-modified Ti6Al4V alloy in friction pairs in endoprostheses, Archives of Metallurgy and Materials 60 (2) (2015) 755-758. otwiera się w nowej karcie
  17. Oliver W.C., Pharr G.M.Ł: Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology, Journal of Materials Research 19 (2004) 3 -20. otwiera się w nowej karcie
  18. Feng B., Weng J., Yang B.C., Qu S.X., Zhang X.D.: Characterization of surface oxide films on titanium and adhesion of osteoblast, Biomaterials 24 (2003) 4663-4670. otwiera się w nowej karcie
  19. Gross K.A., Babovic M.: Influence of abrasion on the surface characteristics of thermally sprayed hydroxyapatite coatings, Biomaterials 23 (2002) 4731-4737. otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

wyświetlono 99 razy

Publikacje, które mogą cię zainteresować

Meta Tagi