Semiconducting Na2O-V2O5-TeO2 glasses with various Na2O contents were melted and subjected to controlled heating to improve conductivity. Topography analysis were performed using confocal microscopy and scanning electron microscopy on both as-quenched and heat-treated samples. X-ray diffraction confirmed the amorphous nature of the samples post-melting, with subsequent heating resulting in the formation of nanocrystallites primarily composed of vanadium ions. The Na2O addition caused progressive depolymerization of the tellurite-vanadate network, as evidenced by IR spectroscopy, although heating exhibited an opposing effect, particularly noticeable in vanadate-related bands. Thermal properties revealing a decrease in the glass transition temperature, crystallization process, and thermal stability with increasing sodium ion concentration. Electrical properties were investigated using impedance spectroscopy, which enabled determination of DC conductivity values, polaron jump energies, and disturbance energies in the samples. The electrical conductivity mechanisms were described as mixed ionic-polaronic, with polaron hopping predominating. Heat treatment significantly enhanced polaron conductivity and altered its nature.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (7)
-
Sharafat Ali profesor
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach dostępnych w wersji elektronicznej [także online]
- Opublikowano w:
-
CERAMICS INTERNATIONAL
ISSN: 0272-8842 - Język:
- angielski
- Rok wydania:
- 2024
- Opis bibliograficzny:
- Wanat M., Okoczuk P., Łapiński M., Kościelska B., Wolff S., Ali S., Wójcik N., Optimizing conductivity in Na-V-Te-O glass through controlled heat treatment, CERAMICS INTERNATIONAL, 2024,10.1016/j.ceramint.2024.11.228
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ceramint.2024.11.228
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 19 razy