The effect of nitrogen on the structure and thermal properties of beryllium-containing Na-(Li)-Si-O-N glasses
Abstrakt
Two oxynitride glass series with the composition of 35Na2O-5BeO-(60-x)SiO2-xSi3N4 and 9Li2O- 27Na2O-5BeO-(59-x)SiO2-xSi3N4, were prepared. The glasses' topography and structure were studied by Scanning Electron Microscopy and Raman spectroscopy. The composition was analyzed by Inductively Coupled Plasma Optical Emission Spectrometer, SEM-EDS and nitrogen and oxygen elemental analyzer. Na-(Li)-Be-silicate glasses were found to contain up to approximately 3.4 (or 5.2 for EDS measurements) at.% of N, respectively. The samples were homogenous in their topography and compositions of their cross-sections. The presence of three-fold coordinated nitrogen atoms in Na-Be-Si-O-N glasses results in higher degree of polymerization as was observed by Raman spectroscopy. The spectrum of analogous glasses with lithium did not show a significant decrease in Q2 units but exhibit the presence of Q4 units which also indicates a polymerization of the network. The incorporation of nitrogen in these glasses leads to the increase of the glass transition temperature and thermal stability.
Cytowania
-
7
CrossRef
-
0
Web of Science
-
7
Scopus
Autorzy (7)
-
B Jonson
- Linnaeus University Department of Building and Energy Technology
-
D Möncke
- Alfred University Inamori School of Engineering
-
E Kamitsos
- National Hellenic Research Foundation
-
H Segawa
- National Institute for Materials Science
-
S Ali
- Linnaeus University Department of Building and Energy Technology
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jnoncrysol.2019.119585
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
JOURNAL OF NON-CRYSTALLINE SOLIDS
nr 522,
strony 1 - 8,
ISSN: 0022-3093 - Język:
- angielski
- Rok wydania:
- 2019
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jnoncrysol.2019.119585
- Źródła finansowania:
-
- SA, BJ and NAW acknowledge the financial support from the Crafoord Foundation (Grant No: 20160900). SA also acknowledges support from the Vinnova (Grant No. 2015-04809). DM thanks the Knowledge Foundation, Sweden (Grant No. 68110029) for financing her stay at Linnæus University. EIK acknowledges the project “National Infrastructure in Nanotechnology, Advanced Materials and Micro-/Nanoelectronics” (MIS 5002772) which is implemented under the Action “Reinforcement of the Research and Innovation Infrastructure”, funded by the Operational Programme “Competitiveness, Entrepreneurship and Innovation” (NSRF 2014-2020) and co-financed by Greece and the European Union (European Regional Development Fund).
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 111 razy
Publikacje, które mogą cię zainteresować
Influence of synthesis conditions on glass formation, structure and thermal properties in the Na 2 O-CaO-P 2 O 5 system doped with Si 3 N 4 and Mg
- N. A. Wójcik,
- B. Jonson,
- D. Möncke
- + 6 autorów
Investigation of the structural and thermal properties of aluminum-rich Ca–Al–Si–O–N glasses
- S. Ali,
- J. Ryl,
- A. S. Hakeem
- + 2 autorów
The influence of Be addition on the structure and thermal properties of alkali-silicate glasses
- N. A. Wójcik,
- S. Ali,
- D. Möncke
- + 5 autorów