A study of the kinetics of bismuth telluride synthesis by an oxide reduction method
PublikacjaThe kinetics of a reduction of bismuth and tellurium oxides in a hydrogen atmosphere, leading to the formation of thermoelectric bismuth telluride is investigated. The evaluation of the reaction kinetics was based on a thermogravimetric analysis performed in non-isothermal conditions. A non-parametric analysis method and the Friedman method were used for the evaluation of the data. Additionally, for a better understanding of the...
-
Detection of the Ag nanoparticles in Te-Bi-Ba-Oa glass
Dane BadawczeThe influence of the manufacturing parameters of tellurium-bismuth-barium glasses on the presence of silver nanoparticles was investigated. Glasses were annealed at 330, 335, 340, 345 and 350 degrees Celsius for 24 and 48 hours. Presence of the Ag nanoparticles was measured by XPS method. The growth of nanoparticles was observed along with the extension...
-
Influence of dopants on structure of polycrystalline bismuth niobate
PublikacjaBismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO4 ceramics was fabricated by mixed oxide method and sintered at temperature T<1000˚C. As the sintering aids a small amount of CuO oxide was used. The crystalline structure of the ceramic samples was examined by X-ray diffraction method at room temperature. The Rietveld refinement method was used for analysis...
-
Carbon-Coated Tellurium for Optical Data Storage
Publikacja -
Structure and optical parameters of Eu doped tellurium oxide thin films prepared by reactive magnetron sputtering method
PublikacjaIn this work the structural properties and photoluminescence of tellurium dioxide thin films doped by europium were described. Thin films were deposited by magnetron sputtering method and simultaneously heated at 200 °C. Presence of Eu ions and their valence states was confirmed by X-ray photoemission spectroscopy measurements. The structure of the films as well as the influence of europium dopant on crystalline structure of the...
-
Characterization of structural, thermal and mechanical properties of bismuth silicate glasses
Publikacjahe influence of heating and reduction processes on the structural, thermal and mechanical properties of bismuth-silicate glasses has been investigated. Two compositions of glasses: 40Bi2O3–60SiO2 (Bi0.57Si0.43Ox) and 27Bi2O3–73SiO2 (Bi0.43Si0.57Ox) were fabricated by a typical melt quenching technique. Then the reduction in hydrogen at 380 °C for 20, 42 or 67 h was performed. It was found that a 50 μm-thick layer was formed on...
-
Macrocyclic derivatives of imidazole as chromoionophores for bismuth(III)/lead(II) pair
Publikacja18-membered diazomacrocycles with imidazole or 4-methylimidazole residue as a part of macrocycle were used as chromoionophores in bismuth(III) and lead(II) dual selective optodes for the first time. Cellulose triacetate membranes doped with macrocyclic chromoionophores are bismuth(III) and lead(II) selective with color change from orange/red to different shades of blue and violet, respectively. Results obtained for model and real...
-
X-RAY DIFFRACTION STUDY OF BISMUTH LAYER-STRUCTURED MULTIFERROIC CERAMICS
PublikacjaGoal of the present research was to apply a solid state reaction route to fabricate bismuth layer-structured multiferroic ceramics described with the formula Bi5FeTi3O15 and reveal the influence of processing conditions on its crystal structure and phase composition. Simple oxide powders Bi2O3, TiO2 and Fe2O3 were used to fabricate Aurivillius-type bismuth layer-structured ferroelectrics. Pressureless sintering in ambient air was...
-
A study of a reduction of a micro- and nanometric bismuth oxide in hydrogen atmosphere
PublikacjaA reduction of bismuth oxide in hydrogen atmosphere was investigated. The reaction was performed with a material in various structural forms: powder: with micrometric grains, powder with nanometric grains and powder pressed into pellets. The process was performed in both isothermal and non-isothermal conditions. An activation energy of the reaction calculated with Friedman method was found to be about 85 kJ/mol for the reduction...
-
Bismuth germanate and bismuth silicate glasses in cryogenic detectors.
PublikacjaStwierdzono, że przewodnictwo elektryczne redukowanych szkieł silnie zależy od temperatury, czasu reakcji i koncentracji Bi. Zależność przewodnictwa elektrycznego od temperatury jest dobrze opisana przez funkcję ĺ~exp[-(T0/T)n,gdzie n=1/4. Współczynnik emisji wtórnej elektronów jest praktycznie niezależny od stopnia redukcji ale znacznie rośnie po domieszkowaniu szkieł alkalicznymi jonami. Badania dowiodły, że modyfikowane...