Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 534 mA. Sample J53, run #4.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 534 mA. Sample J53, experiment run #4. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,2 V at 420 mA. Sample 103.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,2 V and discharged to 10 mV by constant current 420 mA. Sample 103. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM V50. The sample...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,8 V at 420 mA. Sample 103.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,8 V and discharged to 10 mV by constant current 420 mA. Sample 103. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM V50. The sample...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 1098 mA. Sample J51.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 1098 mA. Sample J51.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 480 mA. Sample 103.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 480 mA. Sample 103. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 915 mA. Sample J51.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 915 mA. Sample J51.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 420 mA. Sample 103, run#2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #2. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 108 mA. Sample J51.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 108 mA. Sample J51.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 549 mA. Sample J51.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 549 mA. Sample J51.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,5 V at 420 mA. Sample 103.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,5 V and discharged to 10 mV by constant current 420 mA. Sample 103. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM V50. The sample...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 420 mA. Sample 103, run#1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #1. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 102 mA. Sample 51, run #3.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 102 mA. Experiment run #3. This experiment was preceded by experiment 10.34808/m9mn-yy02. The images were taken with thermographic camera VigoCAM V50....
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 204 mA. Sample 51, run #3.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 204 mA. Experiment run #3. This experiment was preceded by experiment 10.34808/jf84-x137. The images were taken with thermographic camera VigoCAM V50....
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 102 mA. Sample 51, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 102 mA. Experiment run #2. This experiment was preceded by experiment 10.34808/v2hs-b595. The images were taken with thermographic camera VigoCAM V50....
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 204 mA. Sample 51, run #4.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 204 mA. Experiment run #4. This experiment was preceded by experiment 10.34808/jf84-x137. The images were taken with thermographic camera VigoCAM V50....
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 189 mA. Sample 61.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 189 mA. Sample 61.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Dane BadawczeElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 204 mA. Sample 51, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 204 mA. Experiment run #2. This experiment was preceded by experiment 10.34808/av2f-rb57The images were taken with thermographic camera VigoCAM V50....
-
Linear impedance of strontium–borate glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
-
Linear impedance of 1SiO2–99(40Na2O-20CaO-40P2O5) glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of 1SiO2–99(40Na2O-20CaO-40P2O5) glass was measured by impedance spectroscopy method.
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 534 mA. Sample J53, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 534 mA. Sample J53, experiment run #2. The period of images is 30 minutes in order to observe slow temperature fluctuations.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 534 mA. Sample J53, run #5.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 534 mA. Sample J53, experiment run #5. The period of images is 30 minutes in order to observe slow temperature fluctuations.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #5.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #5. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #10.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #10. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,0 V at 420 mA. Sample 103, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,0 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #2. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 534 mA. Sample J52.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 534 mA. Sample J52. The period of images is 30 minutes in order to observe slow temperature fluctuations. The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #9.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #9. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,3 V at 420 mA. Sample 103, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,3 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #2. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 1281 mA. Sample J51, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 1098 mA. Sample J51, experiment run #2. The current is extremely high for this type of sample to accelerate ageing processes.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #6.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #6. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #12.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #12. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #4.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #4. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #11.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #11. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #1. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,4 V at 420 mA. Sample 103, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,4 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #2. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #8.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #8. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 1281 mA. Sample J51, run #3.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 1098 mA. Sample J51, experiment run #3. The current is extremely high for this type of sample to accelerate ageing processes.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #7.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #7. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,0 V at 420 mA. Sample 103, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,0 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #1. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,9 V at 420 mA. Sample 103, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,9 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #2. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,9 V at 420 mA. Sample 103, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,9 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #1. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 534 mA. Sample J53, run #3.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 534 mA. Sample J53, experiment run #3. The period of images is 30 minutes in order to observe slow temperature fluctuations.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 1281 mA. Sample J51, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 1098 mA. Sample J51, experiment run #1. The current is extremely high for this type of sample to accelerate ageing processes.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 534 mA. Sample J53, run #7.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 534 mA. Sample J53, experiment run #7. The period of images is 30 minutes in order to observe slow temperature fluctuations.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,9 V at 420 mA. Sample 103, run #3.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,9 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #3. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 534 mA. Sample J53, run #6.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 534 mA. Sample J53, experiment run #6. The period of images is 30 minutes in order to observe slow temperature fluctuations.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #3.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #3. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,4 V at 420 mA. Sample 103, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,4 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #1. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #2. Voltage was increased to accelerate the ageing process.The images were taken with thermographic camera VigoCAM...
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Dane BadawczeElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...