XPS analysis of strontium titanate ceramics
Dane BadawczeThe chemical composition of the strontium titanite doped with yttrium and iron ceramic samples was investigated. Samples of Y0.07Sr0.93Ti0.8Fe0.2 were prepared by solid phase reaction and sintered for 24 and 48 hours. Chemical composition was measured by UHV OmicronNanotechnology XPS system. The analysis confirmed the chemical composition of the ceramics...
-
Reduction of the strontium titanate doped by Ytrium ceramics observed by X-ray photoemission spectroscopy method
Dane BadawczeYtrium-doped strontium titanate (YSTF) ceramics materials were manufactured by three various methods: 1) standard solid-state reaction method from Y2O3 (Sigma Aldrich, 99,9%), TiO2 (Sigma Aldrich, 99%) and SrCO3 (Sigma Aldrich,98%), 2) Pechini method, 3) wet method.
-
XPS study of the YST ceramics
Dane BadawczeYttrium-doped strontium titanate was prepared via conventional solid-state reaction method from Y2O3 (Sigma Aldrich, 99,9%), TiO2 (Sigma Aldrich, 99%) and SrCO3 (Sigma Aldrich,98%). For comparision, two other techniques were used for synthesis: Pechini and wet methods. Both kind of samples were measured, after and before reduction process (in a hydrogen)....
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials after reduction at 900 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-preapred (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials
Dane BadawczeThe ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co)
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co) were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
Change of exhaust gases concentration for reference SOFC and SOFC with LSCNT layer fueled by biogas mixture at 750 C
Dane BadawczeThe dataset changes of exhaust gases concentrations (CH4,CO,CO2,H2) over working time for SOFC with La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s layer as well as reference SOFEC (unmodified). Concentrations were calculated based on the FTIR measurements and calibration curves presented in different dataset. Longterm measurements of SOFC were performed using in-house...
-
Electrical power measurement of LSCNT modified SOFC fueled by biogas mixture at 750 C
Dane BadawczeThe dataset contains the electrical measurements of IV curves for SOFC with La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s layer working under biogas and H2 feeding stream. The SOFC was reduced at 900C and conditioned for 12 h under H2 prior the measurements. The measurements were performed using Gamry potentiostat/galvanostat
-
The SEM images of LSCNT reduced at 900 degrees C under H2
Dane BadawczeThe dataset includes SEM image of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at 1200oC under air atmosphere for 12 h and reduced at 900oC under H2 for 10 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
FTIR spectra of SOFC with LSCNT layer fueled by biogas mixture at 750 C (pure)
Dane BadawczeThe dataset contains the FTIR spectra collected during the electrical measurements DIR-SOFC with LSCNT layer. The SOFC was reduced at 800degC in H2 prior to mesurements. The spectra were collected every 10 min.
-
The TEC measurement of LSCNT (dilatometry) in air
Dane BadawczeThe dataset includes dilatometry results for La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s measured in air from 100 to 800C using Netzsch DIL 402 PC.
-
The SEM images of LSCNT sintered at 1200 degrees C in air
Dane BadawczeThe dataset includes SEM images of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at 1200oC under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini). The grain structure can be seen on higher resolution image.
-
Electrical performance measurement of reference and SOFC with LSCNT layer fueled by H2 and 20ppm H2S/biogas mixture at 750 C - cyclic measurements (12h per cycle)
Dane BadawczeThe dataset contains the electrical IV measurements collected during the cyclic measurements of H2S poisoning in DIR-SOFC with/-out LSCNT layer. The H2S poisoning and H2 regenrating cycles were 12 h each. The spectra were collected every 10 min.
-
The XRD diffraction patterns of reduced LSCNT prepared using two methods and two sintering temperatures
Dane BadawczeThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s produced using two methods, namely organic (citrate assisted) and Pechini sintered at 1000 or 1200oC under air atmosphere and reduced at 900 for 12 h in wet H2.
-
The XRD diffraction patterns of LSCNT of different A site nonstoichiometry
Dane BadawczeThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s and La0.3Sr0.6Ce0.1Ni0.1Ti0.9O3-s sintered at 1200oC under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
The SEM images of LSCNT reduced at 800 degrees C under H2
Dane BadawczeThe dataset includes SEM images of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at 1200oC under air atmosphere for 12 h and reduced at 800oC under H2 for 10 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
Electrical power measurement of reference SOFC fueled by biogas mixture at 750 C
Dane BadawczeThe dataset contains the electrical measurements of IV curves for SOFC without La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s layer working under biogas and H2 feeding stream. The SOFC was reduced at 900C and conditioned for 12 h under H2 prior the measurements. The measurements were performed using Gamry potentiostat/galvanostat
-
FTIR spectra of SOFC with LSCNT layer fueled by H2 and 20ppm H2S/biogas mixture at 750 C - cyclic measurements (12h per cycle)
Dane BadawczeThe dataset contains the FTIR spectra collected during the cyclic measurements of H2S poisoning in DIR-SOFC with LSCNT layer. The H2S poisoning and H2 regenrating cycles were 12 h each. The spectra were collected every 10 min.
-
The SEM images of LSCNT reduced at 1000 degrees C under H2
Dane BadawczeThe dataset includes SEM images of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at 1200oC under air atmosphere for 12 h and reduced at 1000oC under H2 for 10 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
Change of exhaust gases concentration for LSCNT modified SOFC fueled by biogas mixture at 750 C
Dane BadawczeThe dataset changes of exhaust gases concentrations (CH4,CO,CO2,H2) over working time for SOFC with La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s layer. Concentrations were calculated based on the FTIR measurements and calibration files presented in coupled dataset.
-
FTIR spectra of reference SOFC fueled by H2 and 20ppm H2S/biogas mixture at 750 C - cyclic measurements (12h per cycle)
Dane BadawczeThe dataset contains the FTIR spectra collected during the cyclic measurements of H2S poisoning in DIR-SOFC without LSCNT layer. The H2S poisoning and H2 regenrating cycles were 12 h each. The spectra were collected every 10 min.
-
The EDS elemental maps of reduced LSCNT (SEM)
Dane BadawczeThe dataset includes elemental maps of La, Ce, Ti, O, Sr, Ni in La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s produced using Pechini method sintered at 1200oC under air atmosphere and reduced at 900 for 12 h in wet H2.
-
The XRD diffraction patterns of LSCNT sintered at various temperatures
Dane BadawczeThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
The XPS spectra of LSCNT sintered at 1200C
Dane BadawczeThe dataset includes XPS spectra of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini). The XPS spectra were collected for all species.