Preliminary investigations of effect of conditions of FCAW process on diffusible hydrogen content in deposited metal
PublikacjaOne of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper the state...
-
Exploring the trends in flux-cored arc welding: scientometric analysis approach
PublikacjaFlux-cored arc welding (FCAW) is a universal group of welding methods in terms of the scope of application and automation possibilities, the share of which in various industries in many countries is still increasing. The paper presents the results of bibliographic analyses (scientometric analysis with the use of VOSviewer, Bibliometrix and CitNetExplorer tools) of a data set of 993 publications indexed in the Web of Science database...
-
BADANIA JAKOŚCI BEZSZWOWYCH DRUTÓW PROSZKOWYCH
PublikacjaProces spawania drutami proszkowymi (FCAW) zyskuje coraz większą popularność w różnych dziedzinach przemysłu. Przemysł stoczniowy oraz offshore znacznie częściej wykorzystuje tę metodę przy wykonywaniu odpowiedzialnych i masywnych konstrukcji, których nie można wykonać stosując metody w pełni zautomatyzowane, np. spawanie łukiem krytym. Wzrost zainteresowania tą metodą spowodowany jest przez wysoką wydajność procesu spawania, łatwość...
-
Wpływ warunków spawania na własności złączy spawanych ze stali superduplex
PublikacjaW pracy przedstawiono charakterystykę stali duplex i superduplex koncentrując się na ich spawalności. Zaprezentowano wyniki badań własności mechanicznych złączy spawanych ze stali superduplex wykonanych metodami FCAW i SAW.
-
Znaczenie wolnego wylotu elektrody przy spawaniu drutami proszkowymi
PublikacjaW artykule przedstawiono role i mechanizm wpływu wolnego wylotu elektrody, przy spawaniu drutami proszkowymi (FCAW), na przykładzie złączy kątowych ze spoinami pachwinowymi, na pozostałe parametry, geometrię spoin i własności złączy.
-
Zależności wiążące parametry spawania drutami proszkowymi
PublikacjaW artykule przedstawiono procedury wyznaczania zależności pomiędzy trzema parametrami spawania: wolnego wylotu elektrody, prędkości podawania drutu i natężenia prądu, dla spawania drutami proszkowymi (FCAW). Obliczenia wykonano w oparciu o rotalny drugiego stopnia plan eksperymentu.
-
Corrosion behavior of hydrogen charged super duplex stainless steel welded joints
PublikacjaThe electrochemical behavior of the weld metal, heat-affected zone (HAZ), and base material of super duplex stainless steel (SDSS) welded joints, made with the application of flux-cored arc welding (FCAW) and submerged arc welding (SAW), were investigated with the use of metallographic examinations (optical microscopy and scanning electron microscopy), potentiodynamic polarization measurements and total hydrogen content determination...
-
The Effect of Welding Conditions on Mechanical Properties of Superduplex Stainless Steel Welded Joints
PublikacjaThe tests results of superduplex stainless steel welded joints made with a different heat input, using automatic submerged arc welding (SAW) and semi-automatic flux-cored arc welding (FCAW) have been presented. Metallographic examinations, the measurements of the ferrite content, the width of the heat affected zone (HAZ) and the hardness of the welds in characteristic areas have been performed. Significant differences in the amount of...
-
Effect of Linear Energy and Microstructure on the Content of Residual Hydrogen in Welded Joints made of Superduplex Steels
PublikacjaThe article presents tests concerning the content of retained hydrogen present in FCAW and SAW welded joints made of superduplex steel. The use of various welding technologies resulted in the obtainment of welds having different microstructures and ferrite contents. Measurements of retained hydrogen present in joints (performed using the complete combustion method) revealed various contents of hydrogen in the base material and...
-
The effect of pre-hydrogen charging on corrosion behaviour of superduplex stainless steel welded joints
PublikacjaThe paper presents results of research undertaken to determine the influence of hydrogen on passivity and corrosion resistance of 2507 super duplex stainless steel welded joints. Butt welded joints were made with low heat input using flux corded arc welding (FCAW) method. Coupons of 5.0 x 5.0 mm were cut from the welded joints containing weld metal (WM), heat affected zone (HAZ) and parent metal (PM). Hydrogen was introduced...
-
Niszczenie wodorowe złączy spawanych ze stali ferrytyczno - austenitycznych typu superdupleks
PublikacjaPraca dotyczy problematyki niszczenia wodorowego stali superdupleks URANUS 52N+, w szczególności złączy spawanych wykonanych z tej stali z różną ilością wprowadzonego ciepła spawania. Całość opracowania składa się z dwóch części. Część pierwsza to przegląd literatury omawiający głównie wpływ wodoru oraz spawania na strukturę i własności stali dupleks. Część druga, doświadczalna zawiera tezę i cele rozprawy, charakterystykę badanego...
-
Preliminary studies of seamless flux cored wires stored in extreme conditions
PublikacjaIn the paper preliminary experimental studies of flux cored wires moisturized under controlled conditions are described. Three seamless wires of different grades have been placed in environmental chamber and moisturized in extremely adverse conditions (temperature T = 60° C, relative humidity H = 90%) for 240 hours. During this time measurements of weight gain and observations of surface of wires have been carried out. Also diffusible...
-
Assessment of absorbability of seamless flux cored wires stored in extreme conditions
PublikacjaWater absorption tests by gravimetric method of three specimens of seamless rutile flux cored wires for flux cored arc welding were carried out. Examined wires are characterized by varied absorbability (Wg is ranged from 0.03 to 0.11% after 200 h of moisturizing).
-
Oznaczenie ilości wodoru dyfundującego w stopiwie drutów proszkowych Kobelco DW-A70L
PublikacjaNa zlecenie firmy VELTECH Konrad Matolicz wykonano pomiary ilości wodoru dyfundującego w stopiwie dwóch wytopów drutu proszkowego gatunku Kobelco DW-A70L. Ze względu na klasę badanego drutu (H5) pomiary zrealizowano metodą rtęciową, która jest zalecana przez właściwą normę regulującą badania nawodorowania stopiwa spoiw do spawania. Wyniki pomiarów ilości wodoru dyfundującego w stopiwie drutów proszkowych gatunku Kobelco DW-A70L...