Wyniki wyszukiwania dla: nanocrystallines
-
Hemocompatibility of nanocrystalline diamond layers
Dane BadawczeThe biocompatibility of the diamond films were investigated with whole human blood samples. Blood used in this study was drawn from 10 healthy human patients of different age, sex, and blood group. A 2 ml samples were collected into standard tubes with EDTA anticoagulation agent. Blood was used within 6 hours from the collection time. A reference blood...
-
The structure of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
The structure of lead-borate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and...
-
The morphology of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
SEM micrographs of boron-doped nanocrystalline diamond-carbon nanospikes
Dane BadawczeThis dataset contains the Scanning Electron Microscopy (SEM) micrographs taken for rich boron-doped carbon crystalline nanospikes/nanograss structures, at different magnifications, encoded in the labels of the images. The micrographs were made using Hitachi S-3400N SEM microscope in secondary electron mode under 20 kV accelerating voltage. No additional...
-
The topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with SEM method
Dane BadawczeThe topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by SEM.
-
Thermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by DSC.
-
The structure of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing Bi2VO5.5 nanocrystallites was measured by XRD.
-
XRD investigations of the lithium titanate thin films
Dane BadawczeNanocrystalline thin films with 800 nm thickness were prepared by sol–gel method. To examine the influence of the annealing temperature on as-prepared films crystallization, the coatings were heated at temperature from 500 °C up to 600 °C for 20h. Structure of manufactured thin films was investigated using X-ray diffraction (XRD). The most visible...
-
Optical measurements of lithium titanate sol-gel derived thin films
Dane BadawczeNanocrystalline thin films with 800 nm thickness were prepared by sol–gel method. To examine the influence of the annealing time on as-prepared films crystallization, the coatings were heated at 550 °C for 10, 20 and 80 h. On the basis of transmission characteristic optical properties were calculated. It was found that transmission through the thin...
-
The luminescence study of CsPbI3 nanoparticles embedded in Cs4PbI6 crystals.
Dane BadawczeCs4PbI6, as a rarely investigated member of the Cs4PbX6 (X is a halogen element) family, has been successfully synthesized atlow temperatures by collaborators from National Taiwan University. Strong red to near-infrared (NIR) emission properties have been detected, and its optical emission centers have been identified to be numerous embedded perovskite-type...