Nonlinear and linear impedance of bismuth vanadate ceramics and its relation to structural properties
PublicationThe nonlinear and linear electrical properties, topography, and microstructure of bismuth-vanadate ceramics, were studied. The structurewas observed with the use of X-ray diffraction (XRD), scanning electronmicroscopy (SEM), atomic force microscopy (AFM) and confocal microscopy methods. The obtained results showed that ceramic is porous. Two phase transitionswere determinedwith the use of DSC measurements. The linear and nonlinear ac...
-
Nonlinear impedance of as-quenched Bi2VO5.5 glass-ceramic was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of as-quenched Bi2VO5.5 glass-ceramic was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Open Research DataNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Open Research DataNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 613 K was measured by impedance spectroscopy method.
-
Właściwości elektryczne szkło-ceramiki zawierającej ferroelektryczną fazę BiV
PublicationKompozyty szklano - ceramiczne zawierające nanokryształy posiadają właściwości fizyczne, które nie są możliwe do uzyskania w innych materiałach. Dzięki możliwości wytworzenia szkło - ceramik posiadających kryształy o różnej wielkości (nano, mikro...) i różnorodnego typu, można w istotny sposób kontrolować właściwości elektryczne takich materiałów. Stała dielektryczna faz ferroelektrycznych jest bardzo wrażliwa na zmiany rozmiarów...
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Mixed ionic-electronic conductivity and structural properties of strontium-borate glass containing nanocrystallites of Bi2 VO5.5
PublicationSamples of strontium borate glass containing bismuth vanadate nanocrystallites were prepared. Nanocomposites containing up to 45mol% of the Bi2VO5.5 phase exhibit electrical properties closer to the strontium-borate glass than to the ferroelectric Bi2VO5.5 ceramic. The glass matrix still may contain some part of bismuth and vanadium ions even after crystallization process and there is too little of crystalline phase to observe...
-
Nonlinear electrical properties of glass-ceramics nanocomposites containing ferroelectric nanocrystallites of Bi2VO5.5
PublicationNonlinear A.C. impedance measurements were conducted in the 50BiV-50SrBAlO nanocomposite as a function of frequency, temperature and A.C. voltage. This material is ferroelectric below temperature of 730 K, and above 730 K is a good ion-conductor. For this nanocomposite a low A.C. voltage of 1 V rms is enough to observe high nonlinearities. The origin of these nonlinear effects depends on the temperature and frequency. In the high...
-
Electrochemical and photoelectrochemical characterization of photoanodes based on titania nanotubes modified by a BiVO4 thin film and gold nanoparticles
PublicationTitania nanotubes (TNT) modified with thin films of bismuth vanadate (BiVO4) and gold nanoparticles (GNP) were photoelectrochemically characterized as photoanodes for water photooxidation. Presence of bismuth vanadate enhanced efficiency of photocurrent generation in comparison with pristine TNTs under visible light illumination. Besides an extended range of absorbed light, the presence of both BiVO4 and GNP reduced the charge...
-
Dielectric Properties of BiNbO<sub>4</sub>-Based Ceramic-Polymer Composites with 0-3 Connectivity
PublicationIn the present study two-phase BiNbO4//PVDF composites with 0-3 connectivity were studied by impedance spectroscopy within the frequency range Δν=100Hz-1MHz at room temperature. Polyvinylidene fluoride (PVDF) acted as a matrix whereas bismuth niobate (BiNbO4) powder acted as a dispersed phase. The volume fraction of the ceramic phase was cV=2, 4, 6, 8, 10, 16 and 20vol%. Analysis of the impedance data registered for composites...
-
Fabrication and Study of BiNbO4 Ceramics
PublicationAim of the present research was to fabricate and study crystalline structure as well as dielectric properties of BiNbO4 ceramics. In the present study BiNbO4 ceramics was fabricated by solid state reaction from the mixture of simple oxides viz. Bi2O3, and Nb2O5. Stoichiometric mixture of the powders was thermally analyzed so parameters of the thermal treatment were determined. The EDS measurements proved conservation of the chemical...
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 473 K for 3h and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Electronic and ionic relaxations in strontium-borate glass and glass-ceramics containing bismuth and vanadium oxides
PublicationThe topography, microstructure and electrical properties of strontium-borate glass and SBO glass containing bismuth and vanadium oxides, were studied. The structure was measured using X-ray diffraction (XRD), Energy Dispersive X-ray Spectrometer (EDS) and Scanning electron microscope (SEM) methods. The A.C. complex conductivity was investigated as a function of temperature and frequency. The influence of the quantity of bismuth...
-
Nanostructure and dielectric behavior of vanadate glasses containing BaTiO3
PublicationThe ac and dc electrical conductivity of barium titanate doped bismuth-vanadate as-quenched and heat-treated materials was measured in the frequency range from 1 mHz to 1 MHz and in the temperature range from 153 K to 423 K with the impedance spectroscopy method. The microstructure was investigated by means of XRD, scanning electron microscopy (SEM), atomic force microscopy (AFM) and confocal microscopy. The obtained results showed...
-
Characterization of Bi6Fe2Ti3O18 Ceramics with Impedance Spectroscopy
PublicationIn the present research the tool of impedance spectroscopy was utilized to characterize dielectric behavior of Aurivillius-type ceramics of Bi6Fe2Ti3O18 composition fabricated by hot pressing method from the stoichiometric mixture of oxides Bi2O3, TiO2 and Fe2O3. Impedance spectroscopy was applied to characterize dielectric response of bulk, grain boundary, and material/electrode interfaces of the fabricated polycrystalline ceramic...
-
Dielectric Spectroscopy Studies and Modelling of Piezoelectric Properties of Multiferroic Ceramics
PublicationCompounds and solid solutions of bismuth ferrite (BiFeO3)—barium titanate (BaTiO3) system are of great scientific and engineering interest as multiferroic and potential high-temperature lead-free piezoelectric materials. In the present paper, the results of research on the synthesis and characterisation of 0.67Bi1.02FeO3–0.33BaTiO3 (67BFBT) ceramics in terms of crystal structure and dielectric and piezoelectric properties are reported....
-
Selection of excitation signals for high-impedance spectroscopy
PublicationA method of fast impedance spectroscopy of technical objects with high impedance (|Zx| > 1 GOhm) is evaluated in this paper. An object is excited with a signal generated by a digital-to-analog converter (DAC) located on the U2531A DAQ module. Response signals proportional to current flowing through and voltage across the measured object are sampled by analog-to-digital converters (ADC) in the DAQ module. The object impedance spectrum...
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Open Research DataThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Application of dynamic impedance spectroscopy to scanning probe microscopy.
PublicationDynamic impedance spectroscopy, designed for measuring nonstationary systems, was used in combination with scanning probe microscopy. Using this approach, impedance mapping could be carried-out simultaneously with topography scanning. Therefore, correlation of electrical properties with particular phases of an examined sample was possible. The sample used in this study was spheroidal graphite cast iron with clearly defined phases...
-
Fast High-Impedance Spectroscopy Method Using SINC Signal Excitation
PublicationIn this paper the method of fast impedance spectroscopy of technical objects with high impedance (|Zx| > 1 Gohm) is evaluated by means of simulation and practical experiment. The method is based on excitation of an object with a sinc signal and sampling response signals proportional to current flowing through and voltage across the measured impedance. The object impedance spectrum is obtained with use of continuous Fourier transform...
-
The electrochemical impedance spectroscopy studies of the anode material based on polymer and starch derived ceramic for lithium ion batteries
PublicationThe anode materials derived of preceramic polymer poly(1,2-dimethylsilazane) (PSN) and starch was study. Commercially available polysilazane (poly(1,2-dimethylsilazane (PSN 2M01 Gelest) was mixed with commercially available starch (POCH Gliwice). The ratio polymer/starch (PSN/starch) was 1/1 or 3/7. The polysialazane/starch blend was cross-linked at 230 ºC for 2 h followed by heating to the final temperature (500 ºC, 700 ºC and...
-
Evaluation of the fast impedance spectroscopy method in the laboratory measurement system
PublicationIn this paper the method for fast impedancespectroscopy of technical objects with very high impedance(|Zx| ≥ 1 GΩ) is evaluated by means of simulation and practicalexperiment. The method is based on excitation of an object, witha square pulse and measurements of voltage and currentresponses with DAQ card. The object impedance spectrum isobtained with use of continuous Fourier transform. Someimprovements of the method concerned...
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Open Research DataThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Linear impedance of Bi2VO5.5 glass-ceramic measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 glass-ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Local electrochemical impedance spectroscopy in dynamic mode of galvanic coupling
PublicationA novel method that combines local electrochemical impedance spectroscopy and mapping in dynamicmode is proposed. Method was validated over two galvanic couplings, namely zinc/copper and cad-mium/copper. Impedance spectrum response for all measuring points was obtained by means ofsimultaneous implementation of selected range of frequencies. Proposed method allows the measure-ment in a more time-efficient manner, at the same time...
-
Application of Impedance Spectroscopy for Bi1−xNdxFeO3 Ceramics Characterization
PublicationIn the present paper the synthesis conditions for fabrication of Bi1−xNdxFeO3 ceramics are reported. The single phase polycrystalline samples of Bi1−xNdxFeO3 were prepared by standard solid state reaction method from the mixture of oxides viz.: Bi2O3, Fe2O3 and Nd2O3. The samples were characterized by impedance spectroscopy in the frequency range 10Hz – 1MHz at room temperature.
-
Validity of impedance spectra obtained by dynamic electrochemical impedance spectroscopy verified by Kramers-Kronig transformation.
PublicationArtykuł przedstawia weryfikację wiarygodności widm impedancyjnych otrzymanych za pomocą niedawno wprowadzonej techniki eksperymentalnej - Dynamicznej Elektrochemicznej Spektroskopii Impedancyjnej (Dynamic Electrochemical Impedance Spectroscopy, DEIS). Technika ta zakłada, że badany system jest pseudostacjonarny jeśli czas pomiaru jest odpowiednio krótki. Czas potrzebny na otrzymanie pojedynczego spektrum zależy od długości okna...