Open Research Data
Filters
total: 878
Open Research Data
-
The XRD diffraction patterns of Sr1.9Fe1.5Mo0.5O6 powder calcined at 1200oC in air
Open Research DataThe dataset includes XRD patterns of Sr1.9Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr1.7Fe1.5Mo0.5O6 powder calcined at 1200oC in air
Open Research DataThe dataset includes XRD patterns of La0.3Sr1.7Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr2Al0.1FeMoO6 powder calcined at 1200oC in air
Open Research DataThe dataset includes XRD patterns of La0.3Sr2Al0.1FeMoO6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
X-ray diffractometry results of the SrTi0.50Fe0.50O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.50Fe0.50O3-d (STF50) powder after ball milling. The phase composition of the investigated STF50 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.35Fe0.65O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.35Fe0.65O3-d (STF35) powder after ball milling. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.30Fe0.70O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.30Fe0.70O3-d (STF70) powder after ball milling. The phase composition of the investigated STF70 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
The TPR reduction profile of CeO2/10wt.%Ni with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Cu with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Co with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using alumina catalyst - blank
Open Research DataThe dataset contains the FTIR spectra collected during the catalytic measurements of blank sample Al2O3 for dry reforming of biogas (60/40 CH4-CO2). The specatra were collected every 1 minute.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CLO catalyst
Open Research DataThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Ce0.8La0.2O2 nanocatalyst. The specatra were collected every 1 minute.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CLO/Cu catalyst
Open Research DataThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Ce0.8La0.2O2+10wt.%Cu nanocatalyst. The specatra were collected every 1 minute.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s powder calcined at 800oC in H2
Open Research DataThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 800oC for 12 h in H2. Pure perovskite phase was formed
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CeO2/Cu catalyst
Open Research DataThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using CeO2+10wt.%Cu nanocatalyst. The specatra were collected every 1 minute.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s powder calcined at 800oC in air
Open Research DataThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 800oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1W0.45Mo0.45O3-s precursor calcined under air atmosphere
Open Research DataThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1W0.45Mo0.45O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s precursor calcined under air atmosphere
Open Research DataThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1W0.9O3-s precursor calcined under air atmosphere
Open Research DataThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1W0.9O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
Dilatometry results of SrTi0.65Fe0.35O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.65Fe0.35O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.65Fe0.35O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.50Fe0.50O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.50Fe0.50O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.50Fe0.50O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.30Fe0.70O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.30Fe0.70O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Raw data of AuAg nanoalloy plasmon resonances used for machine learning method
Open Research DataRaw data used for machine learning process. UV-vis measurements of AuAg alloyed nanostructures created from thin films. Plasmonic band position dependence on fabrication parameters. Small presentation reviewing achieved structures and their properties.
-
The electrical properties mesurements of SOFC with Ce0.9Cu0.1O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.9Cu0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of SOFC with Ce0.8Co0.15Cu0.05O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Co0.15Cu0.05O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Cu0.2O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Cu0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with CeO2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with CeO2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The SEM images of Ce0.8La0.2O2 nanopowder prepared using soft template method
Open Research DataThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed...
-
The electrical properties mesurements of SOFC with Ce0.9Co0.1O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.9Co0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Ni0.2O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Ni0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Fe0.2O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Fe0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Mn0.2O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Mn0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Co0.2O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Co0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of SOFC with Ce0.8Co0.1Cu0.1O2-s functional layer
Open Research DataThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Co0.1Cu0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The SEM images of CeO2 nanopowder prepared using soft template method
Open Research DataThe dataset includes SEM images of CeO2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed several...
-
The SEM images of Ce0.8La0.2O2 nanocatalyst infiltrated with 10wt.% Ni prepared using soft template method
Open Research DataThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method and infiltrated to 10wt.% Ni in the catalyst. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate...
-
The XRD diffraction patterns of Ce0.8La0.2O2 and CeO2 prepared using soft template method
Open Research DataThe dataset includes XRD patterns of Ce0.8La0.2O2-s and CeO2-s nanopowders (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC, centrifuged...
-
The XPS spectra of Ce0.8Cu0.2O2 prepared using microemulsion method
Open Research DataThe dataset includes XPS spectra of Ce0.8Cu0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
The XPS spectra of Ce0.8Ni0.2O2 prepared using microemulsion method
Open Research DataThe dataset includes XPS spectra of Ce0.8Ni0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
The XRD diffraction patterns of Ce0.8La0.2O2/Ni prepared using soft template method and impregnation
Open Research DataThe dataset includes XRD patterns of Ce0.8La0.2O2-s nanopowders (nanoparticles,nanocatalyst) prepared using soft template method and further impregnated with 10wt.%Ni using aqueous nitrate solution.
-
The EDS elemental maps of reduced LSCNT (SEM)
Open Research DataThe dataset includes elemental maps of La, Ce, Ti, O, Sr, Ni in La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s produced using Pechini method sintered at 1200oC under air atmosphere and reduced at 900 for 12 h in wet H2.
-
The TEC measurement of LSCNT (dilatometry) in air
Open Research DataThe dataset includes dilatometry results for La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s measured in air from 100 to 800C using Netzsch DIL 402 PC.
-
The XRD diffraction patterns of Ce(Gd,Pr)O2-s samples
Open Research DataThe dataset includes XRD diffraction patterns of Ce0.8Gd0.2O2-s and Ce0.8Pr0.2O2-s sintered at 600oC under air atmosphere for 4 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
The reductivity of the transition metals - calculations
Open Research DataThe dataset includes the reduction enthalpy and Gibbs energy simulated for Co, Cu, Fe, La, Mo, Ni, Sr, Ti, and W from oxide form into metallic form in hydrogen. Simulations were performed using HSC Chemistry software.
-
SEM images of 8YSZ sintered using flash sintering programme
Open Research DataThe dataset contains the SEM images of 8YSZ (8mol% Y2O3-ZrO2) sintered using the flash technique in the muffle furnace. The programme was as follows: 3oC/min to 1000C - 1h hold- 3oC/min 1100C - 1h hold- 3oC/min 1200C - 2h hold- 3oC/min 1400- 30 min hold- 5oC/min 1200C - 15h hold- 4oC/min RT
-
The XRD diffraction patterns of reduced LSCNT prepared using two methods and two sintering temperatures
Open Research DataThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s produced using two methods, namely organic (citrate assisted) and Pechini sintered at 1000 or 1200oC under air atmosphere and reduced at 900 for 12 h in wet H2.
-
FTIR spectra of SOFC with LSCNT layer fueled by biogas mixture at 750 C (pure)
Open Research DataThe dataset contains the FTIR spectra collected during the electrical measurements DIR-SOFC with LSCNT layer. The SOFC was reduced at 800degC in H2 prior to mesurements. The spectra were collected every 10 min.
-
Electrical performance measurement of reference and SOFC with LSCNT layer fueled by H2 and 20ppm H2S/biogas mixture at 750 C - cyclic measurements (12h per cycle)
Open Research DataThe dataset contains the electrical IV measurements collected during the cyclic measurements of H2S poisoning in DIR-SOFC with/-out LSCNT layer. The H2S poisoning and H2 regenrating cycles were 12 h each. The spectra were collected every 10 min.
-
FTIR spectra of SOFC with LSCNT layer fueled by H2 and 20ppm H2S/biogas mixture at 750 C - cyclic measurements (12h per cycle)
Open Research DataThe dataset contains the FTIR spectra collected during the cyclic measurements of H2S poisoning in DIR-SOFC with LSCNT layer. The H2S poisoning and H2 regenrating cycles were 12 h each. The spectra were collected every 10 min.
-
FTIR spectra of reference SOFC fueled by H2 and 20ppm H2S/biogas mixture at 750 C - cyclic measurements (12h per cycle)
Open Research DataThe dataset contains the FTIR spectra collected during the cyclic measurements of H2S poisoning in DIR-SOFC without LSCNT layer. The H2S poisoning and H2 regenrating cycles were 12 h each. The spectra were collected every 10 min.
-
Electrical power measurement of reference SOFC fueled by biogas mixture at 750 C
Open Research DataThe dataset contains the electrical measurements of IV curves for SOFC without La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s layer working under biogas and H2 feeding stream. The SOFC was reduced at 900C and conditioned for 12 h under H2 prior the measurements. The measurements were performed using Gamry potentiostat/galvanostat