Microstructure, mechanical properties, and flame retardancy of nanoclay-incorporated polyurethane flexible foam composites
Abstrakt
The present work seeks to investigate microstructure, mechanical properties, and flame retardancy of polyurethane/nanoclay flexible foam composites. In this regard, we prepared various nanocomposites with and without nanoclay and observed the resulting morphologies to correlate them with the other corresponding characteristics. The results provided support for the fact that tensile strength and compression set will increase with nanoclay content, while elongation at break and tear strength decrease to some extent. Flame-retardancy test results showed that the introduction of nanoclay into the polyurethane flexible foam causes an almost optimal trend in the flame retardancy over clay content. The microcellular-properties correlations were established on account of changes in microcell architecture.
Cytowania
-
9
CrossRef
-
0
Web of Science
-
1 1
Scopus
Autorzy (4)
-
Hadi Rastin
- College of Engineering, University of Tehran, P.O. Box 11155-4563, Tehran, Iran School of Chemical Engineering
-
Zahed Ahmadi
- Amirkabir University of Technology, 15875-4413, Tehran, Iran Color and Polymer Research Center
-
Mohammad Saeb
- Institute for Color Science and Technology, P.O. Box 16765-654, Tehran, Iran Department of Resin and Additives
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF VINYL & ADDITIVE TECHNOLOGY
nr 22,
wydanie 4,
strony 415 - 422,
ISSN: 1083-5601 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Rastin H., Ahmadi Z., Saeb M., Formela K.: Microstructure, mechanical properties, and flame retardancy of nanoclay-incorporated polyurethane flexible foam composites// JOURNAL OF VINYL & ADDITIVE TECHNOLOGY. -Vol. 22, iss. 4 (2016), s.415-422
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1002/vnl.21464
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 100 razy