Topography of barium-vanadate glasses
Dane BadawczeThe topography of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was performed...
-
Microstructure of barium-vanadate glasses
Dane BadawczeThe structure of barium-vanadate glasses was measured by SEM and XRD techniques. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar....
-
Dielectric properties of barium-vanadate glasses
Dane BadawczeThe linear impedance of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was...
-
Detection of the Ag nanoparticles in Te-Bi-Ba-Oa glass
Dane BadawczeThe influence of the manufacturing parameters of tellurium-bismuth-barium glasses on the presence of silver nanoparticles was investigated. Glasses were annealed at 330, 335, 340, 345 and 350 degrees Celsius for 24 and 48 hours. Presence of the Ag nanoparticles was measured by XPS method. The growth of nanoparticles was observed along with the extension...
-
Study of the chemical state of Gd in a Ba-La-Gd-Co based ceramic
Dane BadawczeBarium, Lanthanum, Gadolinium and Cobaltium precursors were used for production of ceramic materials. Samples were produced by standard solid state reaction. Samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing on a Gadolinum were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology....
-
Influence of the annealing condictions on the chemical structure of LaBaGdCo ceramics
Dane BadawczeCeramic samples based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by solid state reaction. After sintring in a furnance, samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology. XPS analysis...
-
Lanthanum investigations in ceramics annealed in a dry and wet atmosphere
Dane BadawczeCeramics based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by standard solid state reaction from oxides and carbonate powders. After sintring, samples were annealed for 2 hours or 72 hours at 300 Celsius degree in a both: wet and dry atmosphere. Results of annealing on a chemical composition and valence state of lanthanum were observed...
-
XRD patterns of TeOx-BaO-BiO powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx-BaO-BiO powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor), barium carbonate, and bismuth carbonate with thetraetylene glycol, water, ethanol, and acetic acid. (Samples molar concentration: 73TeO2-4BaO-3Bi2O3 and 73TeO2-3BaO-4Bi2O3)....