Evaluation of apparent Young׳s modulus of the composite polymer layers used as sliding surfaces in hydrodynamic thrust bearings
PublikacjaHydrodynamic bearings with a polymer sliding layer are able to operate in severe conditions, mainly due to favorable properties of the polymers. The goal of this research was to evaluate apparent Young׳s modulus of two types of the polymer composite layers used for sliding surfaces in hydrodynamic bearings, as a function of temperature. The Young׳s modulus was evaluated on the basis of compression tests carried out on samples obtained...
-
Effect of low-temperature plasma on chitosan-coated PEEK polymer characteristics
Publikacja -
Effect of ground tire rubber on structural, mechanical and thermal properties of flexible polyurethane foams
PublikacjaFlexible polyurethane foams were modified with two kinds of ground tire rubber, untreated and thermo-mechanically reclaimed. A reclamation process was performed in auto-thermal conditions, which reduced the cost of the process and decreased the environmental impact of devulcanization (e.g., emission of gases). The reclamation process was carried out in a continuous manner using a co-rotating twin screw extruder. The foams were...
-
Waterborne polyesters partially based on renewable resources
PublikacjaA new experimental approach for preparing biobased, water-soluble polyesters via titanium(IV) n-butoxide-catalyzed bulk polycondensation is presented. In the described method polymers were obtained from isosorbide, maleic anhydride and poly(ethylene glycol). The chemical structure of the synthesized polyesters was confirmed using 2D NMR spectroscopy and by titration methods. Careful analysis of 2D NMR spectra viz. Correlation Spectra...
-
Preparation and characterization of rigid polyurethane-polyglycerolnanocomposite foams
PublikacjaThis work reports on the preparation of polyurethane-polyisocyanurate (PUR-PIR) foams containing different polyglycerols and layered silicate nanoclays. The rigid polyurethane foams were obtained in a laboratory scale, in a single step method, from a two-component system with a NCO to OH groups ratio equal to two. The reaction mixture consisted of the proper amounts of a commercial oligoetherpolyol, polyglycerol, catalysts, water,...
-
A comprehensive evaluation of flexible FDM/FFF 3D printing filament as a potential material in medical application
PublikacjaThe use of FDM/FFF in 3D printing for medical sciences is becoming common. This is due to the high availability and decent price of both 3D printers and filaments useful for FDM/FFF. Currently, researchers' attention is focused mainly on the study of medical filaments based on PLA, PCL or their modifications. This contributes to insufficient diversity of medical-grade filaments on the market. Moreover, due to the lack of specified...
-
Preparation and characterization of rigid polyurethane–polyglycerol nanocomposite foams
Publikacja -
Kinetics and Mechanism of Potassium Persulphate/L-Serine Initiated Polymerization of Methylmethacrylate
Publikacja -
Saturation ESR spectroscopy of PA12 polyamide
Publikacja -
Influence of modified attapulgite on silicone pressure-sensitive adhesives properties
Publikacja -
The impact of lignin addition on the properties of hybrid microspheres based on trimethoxyvinylsilane and divinylbenzene
Publikacja -
Preparation and characterization of rigid polyurethane -polyglycerol nanocomposite foams
PublikacjaThis work reports on the preparation of polyurethane–polyisocyanurate (PUR–PIR) foams containing different polyglycerols and layered silicate nanoclays. The rigid polyurethane foams were obtained in a laboratory scale, in a single step method, from a two-component system with a NCO to OH groups ratio equal to two. The reaction mixture consisted of the proper amounts of a commercial oligoetherpolyol, polyglycerol, catalysts, water,...
-
Microwave radiation in the synthesis of urethane prepolymers
PublikacjaThis paper describes the use of microwave radiation in the synthesis of urethane prepolymers in bulk (without solvent). The prepolymers were synthesized using 1,6-hexamethylene diisocyanate (HDI) and poly (ε-caprolactone) diol (PCL) at a molar ratio of 4:1. The reaction was carried out without a catalyst in the reactor with a conventional heating system (oil bath) or in the microwave reactor (MW Reactor NOVA 09) at temperatures...
-
A comparative study on selective properties of Kraft lignin–natural rubber composites containing different plasticizers
PublikacjaEffect of plasticizer type on the kraft lignin–nat- ural rubber composite microstructure and selected proper- ties was determined. The composites were prepared with addition of a commonly used naphthenic oil plasticizer to study the decomposition product of polyurethane (glyc- erolysate) and its characteristics. Kraft lignin powder was incorporated into the natural rubber matrix in amounts of 10 and 40 parts per 100 parts of natural...
-
Effect of high loading of titanium dioxide particles on the morphology and selected properties of natural rubber-based composites
PublikacjaThe aim of this work was to prepare and characterize the natural rubber vulcanizates contained different amounts of titanium dioxide particles. At first rubber mixture was prepared using a laboratory two-roll mill and then samples were vulcanized in a hydraulic press. The formulation of rubber mixture and rubber-processing technique is based on our earlier investigations. Materials were obtained at the different titanium dioxide...
-
Synthesis and characterisation of polyurethane elastomers with semi-products obtained from polyurethane recycling
PublikacjaIn this work polyurethane elastomers were synthesised by using different mixtures of a petrochemical and glycerolysate polyols and 4,4-diphenylmethane diisocyanate (MDI). Glycerolysate polyol was produced from polyurethane foam decomposition using crude glycerine as a decomposition agent. The structure and thermal properties of obtained semi-product were similar to the polyol used in the synthesis of original foam. Glycerolysate...
-
Weldability of pipe grade polyethylenes as realized from thermal and mechanical properties assessments
PublikacjaSince polyethylene (PE) has been widely accepted for the production of high-pressure fluid conveying pipelines, studies devoted to weldability of PE connections were always of major importance. In this study, two industrial PE grades designed for pipe production, namely PE80 and PE100, were injection molded, cut, and then welded as PE100-PE100, PE100-PE80, and PE80-PE80. The heat-welded joints were assessed by differential scanning...
-
Mechanical properties of PVDF-coated fabric under tensile tests
PublikacjaThis article describes the laboratory tests necessary to identify the mechanical properties of the polyvinylidene fluoride (PVDF)-coated fabrics named Precontraint 1202S and Precontraint 1302S. First, a short survey of the literature concerning the description of coated woven fabrics is presented. Second, the material parameters for PVDF-coated fabrics are specified on the basis of biaxial tensile tests. A comparison of the 1:1...
-
Curing characteristics, mechanical and thermal properties of reclaimed ground tire rubber cured with various vulcanizing systems
PublikacjaGround tire rubber was thermo-mechanical reclaimed at 120 °C using a co-rotating twin screw extruder. The effect of vulcanizing system type on curing characteristics, static mechanical properties (tensile strength, elongation-at-break, hardness and resilience), dynamic mechanical properties and thermal properties of reclaimed ground tire rubber was investigated. Reclaimed rubber was cured using different types of vulcanization...
-
Linear and branched polyester resins based on dimethyl-2,5-furandicarboxylate for coating applications
PublikacjaIn this study, novel bio-based hydroxyl-functional (co)polyesters from dimethyl-2, 5-furandicarboxylate (DMF), 2,3-butanediol, and a variety of comonomers viz. glycerol, pentaerythritol or trimethylolpropane are prepared using a solvent-free, bulk polycondensation technique. Extensive molecular and thermal characterization was performed to elucidate the properties of these materials. The materials showed suitable properties for solvent-borne...