DETERMINATION OF DIFFUSIBLE HYDROGEN CONTENT IN DEPOSITED METAL OF RUTILE ELECTRODES BY GLYCERIN METHOD
PublikacjaThe presence of diffusible hydrogen in welded joints is one of the causes of formation the welding imperfections. Improvement of weldability can be achieved by reducing the hydrogen amount in welded joints. This requires, among others, the finding of sources of hydrogen. For high hydrogen processes the commonly used method of determining the diffusible hydrogen amount is the glycerin method. This paper concerns issues related to...
-
Determination of moisture resistance of covered electrodes according to PN-EN ISO 14372
PublikacjaMoisture present in the electrode covering is one of the sources of diffusible hydrogen in welded joints. In order to study the diffusible hydrogen content in deposited metal, a stand for moisturizing covered electrodes, in accordance with the PN-EN ISO 14372 standard, was built. After the stand was completed, a test of moisturizing the electrodes was carried out and measurements of the diffusible hydrogen content in deposited...
-
Diffusible hydrogen content in deposited metal of multilayer welded joints
PublikacjaThe article describes manufacturing technology of multilayer joints in terms of control the diffusible hydrogen content. Diffusible hydrogen content in deposited metal for multilayer welded joints made of covered rutile electrodes or covered cellulosic and basic electrodes was determined. It was found that after four beads, the diffusible hydrogen content decreases in the case of the first technology from 36 ml/100 g to 18 ml/100...
-
Effect of the welding environment and storage time of electrodes on the diffusible hydrogen content in deposited metal
PublikacjaIn the study the glycerin displacement method was used for determination of diffusible hydrogen content in deposited metal. Specimens were welded in the air and in the water with covered rutile electrodes. The first part of the specimens was made immediately after opening the package of the electrodes. The electrodes were then stored in opened packages in laboratory conditions that allowed for contact with the air for three years....
-
Weldability of S460ML High Strength Low Alloy Steel in Underwater Conditions
PublikacjaThe paper presents experimental evaluation of susceptibility of the high strength S460ML steel to cold cracking in the conditions of wet welding with the use of covered electrodes. From the results of Tekken tests it was found out that the investigated steel was characterised, in the conditions of the carried out experiments (underwater wet welding and air welding with rutile electrodes), of high susceptibility to cold cracking....
-
Fabrication and characterization of composite TiO2 nanotubes/ boron-doped diamond electrodes towards enhanced supercapacitors
PublikacjaThe composite TiO2 nanotubes / boron-doped diamond electrodes were deposited using Microwave Plasma Enhanced Chemical Vapor Deposition resulting in the improved electrochemical performance. This composite electrode can deliver high specific capacitance of 7.46 mF cm‐− 2 comparing to boron-doped diamond (BDD) deposited onto flat Ti plate (0.11 mF cm‐− 2).The morphology and composition of composite electrode were characterized...
-
The Effect of Welding Conditions on Diffusible Hydrogen Content in Deposited Metal
PublikacjaThe article presents the results of a literature survey and preliminary tests which set out effects of welding conditions on the amount of diffusible hydrogen in deposited metal. Experiments were conducted by using rutile coated electrodes which generate high contents of diffusible hydrogen in deposited metal. The amount of diffusible hydrogen was determined by a glycerin test.Eleven factors were considered: the electrode angle,...
-
APPLICATION POSSIBILITIES OF THE S960 STEEL IN UNDERWATER WELDED STRUCTURES
PublikacjaIn this paper, the application possibilities of the ultra-high strength (UHSS). Domex 960 steel in the underwater welded structures are analyzed. In the research, the investigated material has been tested in bead-on-plate wet welding conditions with the usage of different heat input values, namely 0.63 kJ/mm, 0.72 kJ/mm and 0.93 kJ/mm. Specimens were performed by the manual metal arc (MMA) welding method with the usage of rutile...
-
Linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2 (≥99.9%, anatase...
-
Linear impedance of 35P2O5-30Fe2O3-20Nb2O5-15TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and...
-
High temperature linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
High temperature linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
High temperature linear impedance of 35P2O5-30Fe2O3-25Nb2O5-15TiO2
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%,...
-
EPR of TiO2 hydrogenated at 500 and 600oC
Dane BadawczeData contain EPR spectra of TiO2 (anatase phase) heat treated in H2 at 500 and 600oC. Sample heated at 500oC contained 4 wt% of rutile and that at 600oC 8 wt% of rutile.
-
XRD-TiO2 heat-treated at 400-600oC in Ar or H2
Dane BadawczeThese data contain XRD patterns of TiO2 heat-treated at 400-600oC in Ar or H2. Two pases of TiO2 were identified: anatase and rutile.
-
XRD-TiO2 and SiO2
Dane BadawczeData contain results from XRD measurements of amorphous silica and TiO2 of antase and rutile phases. The commercial TiO2 named as P25 produced by Evonik was also analyzed.
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
SEM of TiO2 heated at 400-600oC in Ar or H2
Dane BadawczeData contain some SEM images of TiO2 taken after its heat treatment in Ar or H2 at 400-600oC. Treated TiO2 was crystalline anatase phase with 3-4 % of rutile nclei.
-
BET of TiO2 heated at 400-600 C degrees
Dane BadawczeThese data refer to the results of BET surface area of TiO2, which was treated firstly in autoclave at 150 C degrees for 1h (sample marked as A150), then was further heat treated in Ar or H2 at 400-600 C degrees. As a raw material TiO2 was used, which was a semiproduct from the industrial production of titania white by sulphur method. The raw material...
-
Brunauer-Emmett-Teller (BET) surface analysis of titanium dioxide (TiO2) and silicon dioxide (SiO2) used for coating of expanded polystyrene spheres (EPS)
Dane BadawczeData refer to the results of BET surface area of TiO2 and SiO2 powders used for coating of expanded polystyrene spheres. The detailed measurement and equipment data was described in readme BET.txt file.TiO2 was treated firstly in autoclave at 150 C degrees for 1h, then was further heat treated in Ar at 400 C degrees. As a raw material TiO2 was used,...
-
Topography of iron-phosphate glasses doped with niobium and titanium tested by confocal microscope
Dane BadawczeThe topography of phosphate-iron glasses containing niobium and titanium were investigated with the use of confocal miscroscope. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5, 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 and 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents...
-
Topography and microstructure of phosphate-iron glasses containing niobium and titanium
Dane BadawczeThe topography and microstructure of phosphate-iron glasses containing niobium and titanium were investigated by the means of X-ray diffraction (XRD), scanning electron microscopy (SEM). Glass samples of the composition of 35P2O5-30Fe2O3-(35-x)Nb2O5-xTiO2 where x= 0; 7.5 and 15 (in %mol) were prepared by the conventional melt quenching technique. Appropriate...