Influence of processing conditions on crystal structure of BiNbO 4 ceramics
PublikacjaBismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. It belongs to the bismutocolumbite oxides with similarly to scheelite-like stibiotantalite structure (SbTaO4) A3+B5+O4. Aim of the present research was to fabricate BiNbO4 ceramics by solid state reaction route from the mixture of simple oxides viz. Bi2O3, and Nb2O5, and study its phase composition as well as...
-
X-RAY DIFFRACTION STUDY OF BISMUTH LAYER-STRUCTURED MULTIFERROIC CERAMICS
PublikacjaGoal of the present research was to apply a solid state reaction route to fabricate bismuth layer-structured multiferroic ceramics described with the formula Bi5FeTi3O15 and reveal the influence of processing conditions on its crystal structure and phase composition. Simple oxide powders Bi2O3, TiO2 and Fe2O3 were used to fabricate Aurivillius-type bismuth layer-structured ferroelectrics. Pressureless sintering in ambient air was...
-
Influence of dopants on structure of polycrystalline bismuth niobate
PublikacjaBismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. BiNbO4 ceramics was fabricated by mixed oxide method and sintered at temperature T<1000˚C. As the sintering aids a small amount of CuO oxide was used. The crystalline structure of the ceramic samples was examined by X-ray diffraction method at room temperature. The Rietveld refinement method was used for analysis...
-
X-Ray Diffraction, Mössbauer Spectroscopy and Magnetoelectric Effect Studies of Multiferroic Bi5Ti3FeO15 Ceramics
PublikacjaBi5Ti3FeO15 ceramics belongs to multiferroic class of materials. In this work it was prepared by solid-state sintering method and investigated by X-ray diffraction, Mössbauer spectroscopy, and magnetoelectric effect measurements. As it was proved by X-ray diffraction studies the single-phase Bi5Ti3FeO15 compound was obtained. The Mössbauer investigations revealed paramagnetic character of the compound at room temperature as well...
-
X-Ray Structure Analysis Online
Czasopisma -
Comparative X-ray diffraction and Mössbauer spectroscopy studies of BiFeO3 ceramics prepared by conventional solid-state reaction and mechanical activation
PublikacjaThe aim of this work was to prepare BiFeO3 by modified solid-state sintering and mechanical activation processes and to investigate the structure and hyperfine interactions of the material. X-ray diffraction and Mössbauer spectroscopy were applied as complementary methods. In the case of sintering, BiFeO3 phase was obtained from the mixture of precursors with 3 and 5 % excess of Bi2O3 during heating at 1023 K. Small amounts of...
-
The structure of vanadate glass-ceramics containing BaTiO3 measured with X-ray diffraction method
Dane BadawczeThe structure of vanadate glass-ceramics doped with BaTiO3 was measured by XRD. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
The structure of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing Bi2VO5.5 nanocrystallites was measured by XRD.
-
The structure of strontium–borate glass-ceramics containing crystalites of Bi2VO5.5. measured with X-ray diffraction and SEM methods
Dane BadawczeThe structure of strontium–borate glass-ceramics containing Bi2VO5.5 crystallites was measured by XRD and SEM.
-
The structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by XRD.
-
Synthesis and structure of Bi 5 FeTi 3 O 15 ceramics
PublikacjaAim of the present research was to fabricate and study crystal structure and phase composition of Bi5FeTi3O15 (BTFO) ceramics exhibiting Aurivillius - type structure. By means of simultaneous thermal analysis and X-ray diffraction analysis the process of synthesis of BTFO ceramics has been studied. Mixed oxide method followed by pressureless sintering was used for ceramics preparation. Three endothermic thermal effects have been...
-
Influence of Processing Conditions on Crystal Structure of Bi6Fe2Ti3O18 Ceramics
PublikacjaAim of the present research was to apply a solid state reaction route to fabricate Aurivillius-type ceramics described with the formula Bi6Fe2Ti3O18 (BFTO) and reveal the influence of processing conditions on its crystal structure. Pressureless sintering in ambient air was employed and the sintering temperatures were 850 and 1080 °C. It was found that the fabricated BFTO ceramics were multiphase ones. They consisted of two Bim+1Fem-3Ti3O3m+3...
-
Fabrication and Study of BiNbO4 Ceramics
PublikacjaAim of the present research was to fabricate and study crystalline structure as well as dielectric properties of BiNbO4 ceramics. In the present study BiNbO4 ceramics was fabricated by solid state reaction from the mixture of simple oxides viz. Bi2O3, and Nb2O5. Stoichiometric mixture of the powders was thermally analyzed so parameters of the thermal treatment were determined. The EDS measurements proved conservation of the chemical...
-
The structure of Bi2VO5.5 ceramic prepared by 3 different ways measured with X-ray diffraction
Dane BadawczeThe structure of Bi2VO5.5 ceramics was measured by XRD.
-
The structure of 70(2Bi2O3-V2O5) - 30SrBO7 measured with X-ray diffraction and SEM methods
Dane BadawczeThe structure changes of 70(2Bi2O3-V2O5)-30SrB4O7 glass occurred during increase in temperature was measured by XRD and SEM.
-
The structure of 50(2Bi2O3-V2O5)-50SrB4O7 measured with X-ray diffraction method during heating
Dane BadawczeThe structure changes of 50(2Bi2O3-V2O5)-50SrB4O7 glass occurred during increase in temperature was measured by XRD.
-
Structure evolution of V2O5 thin films deposited on silicon substrate - High-Temperature X-ray Diffraction
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 thin films deposited on silicon substrates (111). The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The sol was deposited on the silicon substrate. The structure was measured in-situ during heating between 50-800°C under...
-
Structure evolution of V2O5 thin films deposited on quartz glass substrate - High-Temperature X-ray Diffraction
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 thin films deposited on guartz glass. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The sol was deposited on the quartz glass substrate. The structure was measured in-situ during heating between 50-800°C under synthetic...
-
Jarosław Chojnacki prof. dr hab. inż.
OsobyUrodzony w 1961 w Bydgoszczy, absolwent Technikum Chemicznego im. I. Łukasiewicza w Bydgoszczy. Studia chemiczne ukończył na Wydziale Chemicznym Politechniki Gdańskiej w 1986 roku, broniąc pracy dotyczącej elektrod jonoselektywnych. Późniejsze badania związane były z syntezą organiczną i krzemoorganiczną a od 2002 roku z krystalografią. Praca doktorska dotyczyła silanotiolanów miedziowców, a dysertacja habilitacyjna (2010) opisywała...
-
STUDY OF CuO AND V2O5 EFFECT ON IR SPECTRA OF POLYCRYSTALLINE BISMUTH NIOBATE
PublikacjaBismuth niobate (BiNbO4) ceramics were fabricated by mixed oxide method and sintered by presureless sintering method. BiNbO4 ceramics doped with V2O5 additive in amount 0.125 wt%, 0.250 wt% and 1 wt% of was sintered at T = 910°C whereas BiNbO4 ceramics doped with 2 wt% of CuO additive was sintered at T = 890°C and T = 910°C. It was found that V2O5 additive improved morphology of the ceramic samples. However, the chemical composition...