Szkoła Doktorska
Dane badawcze
Filtry
wszystkich: 55
Katalog Danych Badawczych
-
Stability of borophene dispersion in water
Dane BadawczeThis dataset contains the results of the studies of stability of borophene dispersion in water (1 µg/µL) based on the measurements of absorbance of the solution using UV-VIS spectroscopy.
-
X-ray diffraction (XRD) patterns of nickel(II) oxide (NiO) functionalized borophene and bulk boron
Dane BadawczeThese data include X-ray diffration (XRD) patterns of nickel(II) oxide (NiO) functionalized borophene before and after oxygen evolution reaction (OER), bulk boron (B), graphiic foil (GF) and nickel(II) oxide nanoparticles (NiO).
-
X-ray photoelectron spectroscopy (XPS) results for nickel(II) oxide (NiO) functionalized borophene and boron
Dane BadawczeThis dataset contain X-ray photoelectron spectroscopy (XPS) results for nickel(II) oxide (NiO) functionalized borophene before and after oxygen evolution reacion (OER) nad bulk boron.
-
AFM (atomic force microscopy) images of borophene flakes obtained during ball milling at different operating parameters
Dane BadawczeThis dataset contains atomic force microscopy (AFM) images of representative borophene flakes obtained during ball milling. The operational parameters of the ball-milling process included rotation speed (250, 450, and 650 rpm), time of ball-milling (1, 3, 6, and 12 h), and the mass loading of starting bulk boron (1, 2, 3 g).
-
AFM (atomic force microscopy) images of borophene after sonication of boron
Dane BadawczeThese data include AFM (atomic force microscopy) images of borophene obtained after sonication in aceton of boron, collected in order to estimate lateral size of the nanoflakes.
-
Electrochemical measurements of borophene functionalized with nickel(II) oxide (NiO)
Dane BadawczeThis dataset contains linear sweep voltammetry (LSV) and chronopotentiometry (CP) technique results for borophene functionalized with nickel(II) oxide (NiO) and reference samples: ruthenium(IV) oxide (RuO2), nickel(II) oxide (NiO) and pristine borophene. Linear sweep voltammetry (LSV) results show the oxygen evolution reaction permormance of the obtained...
-
Fourier-transform infrared spectroscopy (FTIR) spectra of bulk boron and borophene flakes
Dane BadawczeThese data contain Fourier-transform infrared spectroscopy (FTIR) spectra of bulk boron and borophene flakes obtained during ball milling (450 rpm, 6 h, 1 g). Spectra were acquired to investigate the chemical bonds and functional groups on the surface of the pristine boron and borophene flakes.
-
X-ray Photoelectron Spectroscopy (XPS) results of bulk boron and borophene after the ball-milling process
Dane BadawczeThese data contain X-ray Photoelectron Spectroscopy (XPS) results of boron and borophene nanoflakes induced during ball milling at rotation speed of 450 rpm, 6 h and mass loading of 1g.
-
TEM (transmission electron microscopy) images and elemental mapping EDX (energy dispersive X-ray spectroscopy) of bulk boron and borophene obtained during ball milling
Dane BadawczeThese data contain TEM (transmission electron microscopy) images with corresponding elemental mapping EDX of bulk boron and borophene flakes after the ball-milling process (450 rpm, 6 h, 1 g). The data were collected to investigate the structure and morphology of the materials.
-
X-ray diffraction (XRD) of bulk boron and borophene flakes after the ball-milling process at different operating parameters
Dane BadawczeThese data include X-ray diffraction patterns of bulk boron and borophene obtained during ball milling at different rotation speeds, time and mass loadings. The data were collected to investigate the crystal structure of the studied materials.
-
Cyclic voltammograms of WS2/userGOx (composites of tungsten disulfide and ultrafast self-expanded and reduced graphene oxide) and ex-WS2 (exfoliated tungsten disulfide)
Dane BadawczeThese data contain cyclic voltammograms of WS2/userGOx (composites of tungsten disulfide and ultrafast self-expanded and reduced graphene oxide) and ex-WS2 (exfoliated tungsten disulfide). The data were collected for samples obtained from three ex-WS2:GO dispersions - with 1:1, 1:2, and 2:1 weight ratios.
-
Galvanostatic cycling with potential limitation (GCPL) of WS2/userGOx (composites of tungsten disulfide and ultrafast self-expanded and reduced graphene oxide) and ex-WS2 (exfoliated tungsten disulfide)
Dane BadawczeThese data contain results of galvanostatic cycling with potential limitation (GCPL) of WS2/userGOx (composites of tungsten disulfide and ultrafast self-expanded and reduced graphene oxide) and ex-WS2 (exfoliated tungsten disulfide). The data were collected for samples obtained from three ex-WS2:GO dispersions - with 1:1, 1:2, and 2:1 weight ratios.
-
XRD (X-ray diffraction) patterns of WS2/userGOx (composites of tungsten disulfide and ultrafast self-expanded and reduced graphene oxide), ex-WS2 (exfoliated tungsten disulfide) and GO (graphene oxide)
Dane BadawczeThese data contain XRD (X-ray diffraction) patterns of WS2/userGOx (composites of tungsten disulfide and ultrafast self-expanded and reduced graphene oxide), ex-WS2 (exfoliated tungsten disulfide) and GO (graphene oxide). The data were collected for samples obtained from three ex-WS2:GO dispersions - with 1:1, 1:2, and 2:1 weight ratios.
-
XRD (X-ray diffraction) spectra of bulk boron and obtained borophene
Dane BadawczeThis dataset includes XRD (X-ray diffraction) spectra of bulk boron and borophene obtained during sonication process, giving the information on the phase composition and crystallinity of materials.
-
Raman spectra of WS2/userGOx (composites of tungsten disulfide and ultrafast self-expanded and reduced graphene oxide) and ex-WS2 (exfoliated tungsten disulfide)
Dane BadawczeThese data contain Raman spectra of WS2/userGOx (composites of tungsten disulfide and ultrafast self-expanded and reduced graphene oxide) and ex-WS2 (exfoliated tungsten disulfide). The data were collected for samples obtained from three ex-WS2:GO dispersions - with 1:1, 1:2, and 2:1 weight ratios.
-
SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of nickel (Ni) foam as received, after photocatalysis and after oxidation at 500_C.
Dane BadawczeThis dataset contains SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of Ni (nickel) foam as received from the supplier, after photocatalytic treatment and after oxidation at 500C. The detailed equipment and measurement data was described in "readme SEM.txt" file
-
AFM (Atomic Force Microscopy) analysis of surface topography loaded with nickel nanoparticles.
Dane BadawczeThis dataset presents AFM (Atomic Force Microscopy) images depicting the surface topography loaded with nickel powdered nanoparticles. The detailed equipment and measurement data was described in "AFM readme.txt" file
-
Photocatalytic degradation of acetaldehyde in high temperature reaction chamber
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using TiO2 (titanium dioxide) as photocatalysts. It includes data on the influence of flow rate, TiO2 (titanium dioxide) filling the entire reactor, a thin layer of TiO2 (titanium dioxide) supported on KBr...
-
Photocatalytic decomposition of acetaldehyde over TiO2 (titanium dioxide) supported on nickel foam and Ni-doped (nickel-doped) TiO2
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using as photocatalytic systems TiO2 (titanium dioxide) supported on nickel foam, TiO2 supported on oxidized nickel foam and TiO2 doped by metallic nickel (Ni) powder. The detailed equipment and measurement...
-
Ni-based compounds in multiwalled graphitic shell for electrocatalytic oxygen evolution reactions
Dane BadawczeThis study investigates Ni-based compounds (Ni, NiO, Ni3C) coated with a graphitic shell as electrocatalysts for the oxygen evolution reaction (OER). Electron paramagnetic resonance (EPR) and X-ray diffraction (XRD) are employed to identify the presence and contribution of Nickel ions (Ni0, Ni2+, Ni3+) and determine the phase composition. Electrochemical...
-
XPS-Ni foam as received, after photocatalysis and after oxidation at 500_C.
Dane BadawczeThis dataset contains XPS spectra recorded for nickel foam as received from supplier, after photocatalytic process and after oxidation at 500C. Each set contains: survery spectrum, O1, C1s, Ni2p. The detailed equipment and measurement data was described in "readme XPS.txt" file
-
Transmission electron microscope (TEM) and optical microscope images of pristine and silica-coated bismuth oxide and gadolinium oxide particles
Dane BadawczeCollection of raw transmission electron microscope (TEM) micrographs and optical microscope images used in the associated manuscript. All data in accessible *.tif format. Zip package contains:
-
SEM-EDS images of expanded polystyrene spheres coated with silicon dioxide (SiO2) and/or titanium dioxide (TiO2)
Dane BadawczeData contain SEM and SEM-EDS images of expanded polystyrene spheres coated with silicon dioxide (SiO2) and/or titanium dioxide (TiO2). The detailed equipment and measurement data was described in measurement info.txt file.
-
Brunauer-Emmett-Teller (BET) surface analysis of titanium dioxide (TiO2) and silicon dioxide (SiO2) used for coating of expanded polystyrene spheres (EPS)
Dane BadawczeData refer to the results of BET surface area of TiO2 and SiO2 powders used for coating of expanded polystyrene spheres. The detailed measurement and equipment data was described in readme BET.txt file.TiO2 was treated firstly in autoclave at 150 C degrees for 1h, then was further heat treated in Ar at 400 C degrees. As a raw material TiO2 was used,...
-
Light transmission measurement through the fluidized bed photoreactor
Dane BadawczeDataset contains light transmission measurements through the fluidized bed photoreactor. Two sources of light were used: UV-LEDs and UV fluorescent. Measurements were performed at different air flows: 0, 80, 160 and 240 ml/min. The detailed measurement and equipment data was described in measurment info.txt file.
-
BET specific surface area measurements of bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
X-ray diffraction (XRD) of silica-coated bismuth oxide/gadolinium oxide (Bi2O3+Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
BET specific surface area measurements of silica-coated bismuth oxide (Bi2O3)/gadolinium oxide (Gd2O3) core-shell structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
BET specific surface area measurements of silica-coated bismuth oxide(Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
Photocatalytic ethylene decomposition with the use of fluidized bed photoreactor
Dane BadawczeData contain exported raw data recorded during decomposition of ethylene during utilization of fluidized bed photoreactor equipped with either UV-LEDs or fluorescent UV lamps as well as in either humid or dry conditions. In separate folder, the photographs of the photocatalytic system were included. As photocatalytic material, polystyrene spheres coated...
-
Ethylene photocatalytic decomposition in high temperature reaction chamber
Dane BadawczeData contain data logs of measurements performed on High Temperature Chamber "The Praying Mantis" coupled with SRI 8010 gas chromatograph. Measurement was performed for TiO2 irradiated by UV and under flowing of ethylene gas diluted in air and with the use of elevated temperature.
-
XPS data of MXene catalyst
Dane BadawczeData contain results from XPS measurement of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using 48% HF etching agent (MXene HF). The X-ray spectroscopy (XPS) measurements were conducted using Mg Ka (hn = 1253.6 eV) radiation in a Prevac (Poland) system equipped with a Scienta SES 2002 (Sweden) electron...
-
Acid site concentrations of the MXenes samples
Dane BadawczeData contains the pH of 0.01M NaOH solution, before and after mixing with the MXenes samples.
-
Raman spectroscopy analysis of synthesized sol-gel silica coatings
Dane BadawczeThese data contains Raman spectra of silica coatings synthesized using sol-gel method A and B, which were described with publication associated with this dataset. Raman scattering was measured with a Renishaw microRaman spectrometer (830 nm).
-
GC Chromatograms for isomerization of alpha-pinene
Dane BadawczeData contain results of the catalytic tests for the isomerization of alpha-pinene for the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y,...
-
Adsorption and desorption of N2 measurement of MXenes catalysts
Dane BadawczeData contain results from adsorption and desorption of N2 measurement of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y...
-
XRD patterns of MXenes ashes obtained after TGA measurement
Dane BadawczeData contain results from XRD measurements of the product (ashes) produced after TGA of MAX Phase, MXene HF, MXene HF/HCl 1:3 and MXene HF/H2SO4 1:3 . The measurements were performed in AERIS PANalytical X-ray diffractometer with Cu-Ka radiation.
-
TGA data of MXenes catalysts
Dane BadawczeData contain results from TGA measurement of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios. ...
-
Raman spectra of MXenes catalysts
Dane BadawczeData contain results from Raman spectroscopy of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios. ...
-
XRD patterns of MXenes catalysts
Dane BadawczeData contain results from XRD measurements of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios....
-
SEM images of MXene catalysts
Dane BadawczeData contain results SEM measurements of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios. MAX...
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Dane BadawczeData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.
-
X-ray diffraction (XRD) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
X-ray diffraction (XRD) of silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
TG analyses - content of SiO2 and TiO2 in polystyrene
Dane BadawczeTG analyses were performed for polystyrene spheres coating by SiO2 and then coating by SiO2-TiO2. Thermal analyses of polystyrene spheres only were also performed. The content of inorganic remaining was used for calculation the quantity of coating SiO2 and TiO2 in the polystyrene spheres.
-
TG-hydroxyl groups in TiO2-P25
Dane BadawczeTG analyses were performed for powdered TiO2 - commercial P25 sample, which was heat-treated from room temperature to 500 C in the nitrogen atmosphere. Mass loss at lower temperature such as 120 C was related to the physisorbed water, and that one occurring at 500 C to the chemisorbed hydroxyl groups.
-
TiO2-potential zeta in water
Dane BadawczeData contain results from measurements of zeta potential for powdered TiO2 in a diluted aqueous solution. The measurements were performed in Zetasizer Nano ZS analyser.
-
Photocatalytic decomposition of ethylene on the TiO2-polystyrene spheres
Dane BadawczeData contain results from the measurements of the photocatalytic decomposition of ethylene under UV irradiation with using TiO2 coating on the expanded polystyrene spheres (EPS). EPS-SiO2-TiO2 and EPS-TiO2 were used as the photocatalytic beds in the fluidized bed reactor. Both, stationary and fluidized beds were tested. The comparison of ethylene decomposition...
-
TiO2-TG analyses -OH groups
Dane BadawczeTG analyses of TiO2 were performed under nitrogen flow to monitor desorption of hydroxyl groups. Physisorbed weak-bonded hydroxyl groups were desorbed totally at around 120oC, whereas chemisorbed ones at around 500oC. The mass loss at these temperatures was used as concentration of hydroxyl groups on TiO2 surface. The amount of analysed TiO2 was 10...
-
TiO2-zeta potential
Dane BadawczeData contain results from the measurements of zeta potential of TiO2 versus pH. Data are saved as original files and in the format of Excel file. measurements were perfomed in Zetasizer Nano ZS with using Multi-Purpose Titrator MPT-2.