Slurry Erosion -Design of Test Devices
PublicationDegradation of material caused by impacts of a solid particle (erodent) suspended in a liquid is called slurry erosion and is a major problem in the hydropower and maritime industry. Slurry erosion depends on many factors, e.g. liquid and erodent velocity, size, shape, angle of impact, hardness and number of erodents, and strength of a target material. The various types of test devices have been designed to investigate an effect...
-
Effect of annealing temperature on slurry erosion resistance of ferritic X10CrAlSi18 steel
PublicationIn the present work, the slurry erosion tests were carried out to investigate the influence of heat treatment on slurry erosion process of ferritic X10CrAlSi18 stainless steel using a slurry pot test rig. X10CrAlSi18 stainless steel was tested in as-received condition and after annealing at three different temperatures: 600°C, 800°C and 1000°C. Degradation of materials due to slurry erosion depends on many factors connected with...
-
An Influence of Factors of Flow Condition, Particle and Material Properties on Slurry Erosion Resistance
PublicationThe degradation of materials due to slurry erosion is the serious problem which occurs in the power industries. The paper presents actual knowledge about an influence of individual factors connected with flow conditions, particles and material properties on the slurry erosion resistance. Among the factors connected with operating conditions, an influence of impact angle, and velocity of impact, particle concertation and liquid...
-
Effect of Thermal Treatment and Erosion Aggressiveness on Resistance of S235JR Steel to Cavitation and Slurry
PublicationS235JR steel is used in many applications, but its resistance to the erosion processes has been poorly studied. To investigate this resistance, cavitation, and slurry erosion tests were conducted. These tests were carried out at different erosion intensities, i.e., different flow rates in the cavitation tunnel with a system of barricades and different rotational speeds in the slurry pot. The steel was tested as-received and after...
-
Erosion under turbulent slurry flow: An experimental determination of particle impact angle, impact direction, and distribution thereof by image processing
Publication -
Results of abrasive slurry dosage in lapping process
PublicationPrzedstawiono wyniki badań dawkowania zawiesiny ściernej w docieraniu powierzchni płaskich elementów ceramicznych. Analizowano wpływ dawkowania na podstawowe parametry chropowatości powierzchni ceramiki Al2O3 i Al2O3-ZrO2.
-
Bacteriophage-mediated reduction of Salmonella Enteritidis in swine slurry
Publication -
Degradation of ferritic X10CrAlSi18 stainless steel caused by slurry
PublicationThe slurry erosion tests of ferritic X10CrAlSi18 steel were carried out using a slurry pot device. In order to investigate the erosion process, two series of tests were performed: first one with a constant impact velocity of 5 m/s, 7 m/s and 9 m/s and the second one, during which the impact velocity was changed after every exposure. During each test, an influence of test conditions on volume loss, surface hardness and roughness...
-
Study of abrasive slurry dosage in flat surfaces lapping process
PublicationPrzedstawiono wyniki badań dozowania pasty i zawiesiny ściernej w procesach docierania powierzchni płaskich. Badano wpływ wielkości dawki ścierniwa na podstawowe parametry chropowatości powierzchni elementów miedzianych i ceramicznych. Docierano miedź betlenową MOOB oraz ceramikę Al2O3 i Al2O3-ZrO2 mikroziarnami węglika krzemu i węglika boru.
-
Influence of abrasive slurry dosage on flat surface lapping effects
PublicationPrzedstawiono wyniki badań dawkowania zawiesiny ściernej w obróbce powierzchni płaskich na docierarce jednotarczowej. Analizowano wpływ dawki ścierniwa na wydajność i jakość obróbki elementów ceramicznych i miedzianych.
-
Isolation of multidrug resistant coliforms and their bacteriophages from swine slurry
Publication -
An Experimental Investigation of Pressure Wave Celerity During the Transient Slurry Flow
PublicationTransportation of slurries in pressure pipelines is an example of a complex flow due to specific parameters of transported medium. For practitioners, the economy of designing and maintenance is usually the most important factor. For this reason, most of hydrotransport installations are fairly simple; however, they become more vulnerable to negative effects of the transient flow which can occur in pressure pipelines. As the consequence,...
-
Slurry Surfacing Mixes on the Basis of Bitumen Modified with Phenol-Cresol-Formaldehyde Resin
PublicationSlow-breaking monophase cationic bitumen emulsions have been produced on the basis of bitumen modified with phenol-cresol-formaldehyde resin (PhCR-F). Bitumen emulsions were used as a binder for thin-layer coatings with slurry surfacing mixes (SSM). Physical and technical parameters of modified and unmodified emulsions were determined and analyzed. The optimal compositions of SSM were selected according to the breaking criterion....
-
Tests for lapping of flat surfaces of ceramic elements with forced dosing of abrasive slurry
PublicationPrzedstawiono zagadnienia dotyczące systemu wymuszonego dawkowania zawiesiny ściernej w docieraniu jednotarczowym powierzchni płaskich. Opisano zalety takiego systemu dozowania płynnej zawiesiny ściernej. Omówiono wybrane wyniki badań docierania elementów z ceramiki technicznej. Analizowano wpływ podstawowych warunków dawkowania zawiesiny na ubytek liniowy próbek.
-
Influence of ethylene glycol on CaCO3 particles formation via carbonation in the gas-slurry system
PublicationStrącanie węgalnu wapnia przebiegało w układzie gaz-zawiesina w reakcji wodorotlenku wapnia z dwutlenkiem węgla. Proces precypitacji był prowadzony w obecności glikolu etylenowego. Użyty dodatek organiczny zmieniał lepkość mieszaniny reakcyjnej oraz rozpuszczalność dwutlenku węgla i węgalnu wapnia, co miało wpływ na warunki precypitacji CaCO3. Wzrost stężnia glikolu etylenowego w mieszaninie reakcyjnej powodował większe zużycie...
-
Enhanced visible light photocatalytic activity of Pt/I-TiO2 in a slurry system and supported on glass packing
PublicationHighly photoactive I/TiO2, Pt/I-TiO2 nanocomposites were obtained using a hydrothermal and wet impregnation method. The incorporation of iodine and modification with 0.05 mol% of platinum leads to enhanced photocatalytic activity as compared to singly doped TiO2 due to the presence of impurity energy level in the structure of TiO2. X-ray diffraction, TEM microscopy, UV–Vis spectroscopy, X-ray photoelectron spectroscopy and BET...
-
Standard and modified falling mass impact tests on preplaced aggregatefibrous concrete and slurry infiltrated fibrous concrete
PublicationAlthough several studies have been conducted to evaluate the impact response of concrete using theAmerican Concrete Institute (ACI) 544-2R falling mass impact test, the variations in test results are themain drawback of this testing method. This study aims to reduce the variations in experimental impacttest results by introducing two simple test setup modifications; (1) using coarse or fine aggregate bed-ding as an alternative...
-
Numerical investigation on distribution characteristics of oxidation air in a lime slurry desulfurization system with rotary jet agitators
PublicationRotary jet agitator is an effective device for mixing, dispersing, dissolving, and suspending dispersed phases in liquid, and is particularly advantageous to the homogenization of oxygen-enriched air within the lime slurry desulfurization system. The distribution of oxygen-enriched air in agitators is vital for the process of gypsum crystallization and the homogeneous and sufficient oxygen-enriched air can promote the formation...
-
Time dependent slurry viscosity of finegrained silicon dioxide particles.Second International Conference on Engineering Rheology ICER 2003.
PublicationCząstki dwutlenku krzemu otrzymywano w wyniku reakcji chemicznej krzemianu sodowego z gazowym dwutlenkiem węgla. Krzemian sodowy był rozpuszczony w wodnym roztworze glikolu trójetylenowego. Dwutlenek węgla wprowadzano do strefy wznoszenia reaktora airlift z wewnętrzną cyrkulacją. Obserwowano położenie maksimów na krzywych zależności lepkości zawiesiny reakcyjnej od czasu.
-
Gas hold up and time dependent slurry viscosity during the the precipitation of fine grained silicon dioxide particles.
PublicationBadano zmiany stopnia zatrzymania gazu i lepkości zawiesiny podczas precypitacji dwutlenku krzemu z krzemianu sodowego za pomocą dwutlenku w reaktorze airlift z wewnętrzną cyrkulacją. Badano wpływ parametrów procesowych na akumulację mikropęcherzy w zawiesinie.
-
Cavitation Erosion – Phenomenon and Test Rigs
PublicationThe cavitation and cavitation erosion phenomenon have been shortly presented. The main four types of test rigs to investigate the cavitation erosion resistance have been shown. Each type of test design is described and an example of a design is shown. A special attention has been payed to the designs described in the International ASTM Standards: a vibratory design and a cavitating jet cell. There was shown that the design of a...
-
Scale effects in cavitation erosion of materials
PublicationW pracy przedstawiono wpływ wielkości objętości erodowanego materiału na przebieg krzywych erozyjnych. Przedstawiono również niektóre wyniki Międzynarodowego Testu Kawitacyjnego.
-
Erosion of privacy in computer vision systems
PublicationW pracy przedstawiono problemy, które mogą wystąpić, gdy technologia komputerowego wzroku zostanie zaimplementowana w urządzeniach wykorzystywanych w codziennym życiu. Przeprowadzono także dyskusję socjologicznych konsekwencji stosowania biometrii, automatycznego śledzenia ruchu i interpretacji obrazu. Omówiono też problemy wynikające z połączenia komputerowego wzroku z możliwościami oferowanymi przez Internet.
-
Estimation of cavitation erosion resistance of materials
PublicationW pracy przedstawiono ocenę odporności kawitacyjnej 17 materiałów. Do opisu odporności kawitacyjnej zaproponowano nowy wskaźnik liczbowy uwzględniający długość okresu inkubacji, maksymalną prędkość niszczenia oraz czas po którym wystąpi maksymalna prędkość niszczenia materiału. Zaproponowany wskaźnik porównano ze wskaźnikiem δcav, który reprezentuje całą krzywą erozji kawitacyjnej materiału.
-
Cavitation erosion degradation of Belzona® coatings
PublicationIn hydrocarbon and maritime industry there is a constant need of materials and coatings withstanding severe conditions. One of adverse phenomena present there is cavitation erosion. The paper presents evaluation of cavitation resistance of three different steel coatings. Belzona 2141 (ACR-Fluid Elastormer), 1321 (Ceramic S-Steal) and 5831 (ST-Barrier) were deployed on P110 steel and subjected to ultrasound cavitation in distilled...
-
The resistance of S235JR steel to cavitation erosion
PublicationThe erosion resistance of S235JR steel to flow cavitation was investigated. In order to understand an influence of steel properties and cavitation intensities on the degradation mechanisms, low-carbon S235JR steel was tested in the as-received state and after thermal treatment (annealing) under four different flow velocities. Annealing decreased steel hardness, which made S235JR steel less resistant to cavitation erosion. The performed...
-
On the importance of volume of eroded material for cavitation erosion
PublicationW pracy przedstawiono model matematyczny opisujący wpływ objętości erodowanego materiału na przebieg krzywych erozji kawitacyjnej
-
Cavitation Erosion Resistance Influence of Material Properties
PublicationThe cavitation erosion is the phenomena that causes degradation of fluid flow machinery components due to repetitive implosion of cavitation bubbles adjacent to the solid surface. Cavitation erosion is a complex phenomenon, which includes not only hydrodynamic factors of liquid, but also properties of erodible material e.g. microstructure, hardness or Young modulus. In order to reduce the negative impact of erosion on machine components,...
-
Mathematical description and evaluation of cavitation erosion resistance of materials.
PublicationPrzedstawiono matematyczny opis erozji kawitacyjnej materiałów. Model opisuje wpływ własności mechanicznych materiału takich jak: względna odporność na plastyczne odkształcanie powierzchni a także współczynnika intensywności naprężeń wzmocnionej warstwy wierzchniej na przebieg erozji kawitacyjnej. Zaproponowano również nowy współczynnik opisujący ilościowo odporność kawitacyjną materiałów jako funkcję czasu inkubacji maksymalnej...
-
Mathematical description and evaluation of cavitation erosion resistance of materials.
PublicationW pracy przedstawiono matematyczny model opisujący erozję kawitacyjną materiałów oparty o rozkład prawdopodobieństwa Weibulla. Model oposuje wpływ własności mechanicznych materiału na przebieg krzywych erozji kawitacyjnej.
-
Cavitacion erosion, influence of electrochemical corrosion on cavitation - a review
PublicationZjawisko kawitacji polega na narastaniu, a następnie zapadaniu się i implozji pęcherzy wypełnionych gazem lub parami. Zachodzi ono niemalże we wszystkich układach hydrodynamicznych np. w pompach, zaworach, na śrubach okrętowych, turbinach, hydropłatach itp. na skutek lokalnej, gwałtownej zmiany ciśnienia. W większości przypadków jest to zjawisko niepożądane, ponieważ siły generowane podczas implozji pęcherzy kawitacyjnych są tak...
-
Cavitation Erosion of P110 Steel in Different Drilling Muds
PublicationThe P110 steel specimens were subjected to ultrasonic cavitation erosion in different compositions of drilling muds and surfactant additive. The test procedure was based on ASTM-G-32 standard recommendations. API 5CT-P110 steel is used for pipes in oil and gas industry. The harsh environment and high velocity of flows poses corrosive and erosive threat on materials used there. The composition of drilling fluid influences its rheological...
-
Cavitation Erosion of Nodular Cast Iron - Microstructural Effects
PublicationThe paper deals with susceptibility of nodular cast iron with ferritic-pearlitic matrix on cavitation erosion. Cavitation tests were carried out with the use of a cavitation erosion vibratory apparatus employing a vibration exciter operated at frequency of 20 kHz. The study allowed to determine the sequence of subsequent stages in which microstructure of cast iron in superficial regions is subject to degradation. The first features...
-
Sutry Jezusa – pierwsze syntezy chrystologiczne Dalekiego Wschodu
Publication -
On the importance of initial volume of eroded material for cavitation erosion curve
PublicationW pracy przedstawiono rozważania na temat wpływu początkowej objętości erodowanego materiału na przebieg krzywych erozyjnego niszczenia
-
Analysis of water erosion processes using terrestrial laser scanning
Publication -
Assessment of cavitation erosion damage of laser remelted the SUPERSTON alloy
PublicationW artykule przedstawiono wpływ obróbki laserowej w warunkach kriogenicznych na mikrostrukturę stopu SUPERSTON po badaniach kawitacyjnych. Badania odporności kawitacyjnej przeprowadzono na stanowisku z wirującą tarczą w IMP PAN Gdańsk. Określono kinetykę ubytku masy próbek podczas testu kawitacyjnego dla stopu odlanego i nadtopionego laserowo.
-
The degradation mechanisms of a nanobainitic steel under cavitation erosion conditions
Publication -
Cavitation Erosion Resistance of Austenitic Microstructure Created byLaser Beam
PublicationPraca przedstawia własności kawitacyjne różnych mikfrostruktur austenitycznych tworzonych za pomocą wiązki lasera na stalach X5CrNi18-10 oraz C45. Stal X5CrNi18-10 była laserowo stopowana węglikiem TiC oraz stopowana Ni, Mn, Cr i Nb. Jako żródło mocy stosowany był laser CO2. Własności kawitacyjne oceniane były na stanowisku z wirującą tarczą. Badania ujawniły różną podatność struktury austenicycznej do odkształceń plastycznych...
-
Damage Development on the Surface of Nickel Coating in the Initial Period of Erosion
PublicationThe common occurrence of the phenomenon of cavitation in many industries and the multitude of factors affecting the resistance to cavitation erosion of used materials contribute to the search for methods and appropriate parameters of coating application that are able to minimize the effects of erosion. To determine the validity of the developed application parameters and the method used, cavitation studies and microscopic observations...
-
Simplified Numerical Model for Transient Flow of Slurries at Low Concentration
PublicationRapid transients are particularly dangerous in industrial hydro-transport systems, where solid-liquid mixtures are transported via long pressure pipelines. A mathematical description of such flow is difficult due to the complexity of phenomena and difficulties in determining parameters. The main aim of the study was to examine the influence of the simplified mixture density and wave celerity description on satisfactory reproduction...
-
Cavitation erosion of heterogeneous thin coatings produced by means of laser cladding
PublicationPrzedstawiono badania odporności kawitacyjnej cienkich heterogenicznych warstw nakładanych metodami laserowymi na stal 45. Wykazano dobrą przyczepność i wysoką odporność kawitacyjną wykonanych powłok.
-
Cavitation erosion of steels processed by CO2 laser beams of various parameters.
PublicationPrzedstawiono wpływ parametrów przetapiania stali za pomocą wiązki lasera CO2 na jej własności kawitacyjne. Do badań użyto stali 45, 2H13 i OH18N9. Wyniki badań wskazują na znaczny wpływ parametrów przetapiania na poziom odporności kawitacyjnej stali.
-
Technique for reducing erosion in large-scale circulating fluidized bed units
PublicationThis paper presents a methodology, implemented for a real industrial-scale circulating fluidized bed boiler, to mitigate the risk of heating surfaces exposed to an intensive particle erosion process. For this purpose, a machine learning algorithm was developed to support the boiler reliability management process. Having a tool that can help mitigate the risk of uncontrolled power unit failure without expensive and technically complex...
-
Cavitation erosion of X5CrNi18-10 austenitic stainless steel alloyed with TiC
PublicationPraca prezentuje zmianę odporności kawitacyjnej stali X5CrNi18-10 po laserowym stopowaniu jej warstwy wierzchniej węglikiem TiC. Laserowe stopowanie przeprowadzono dla 2 wariantów. W pierwszym przypadku stal stopowano do zawartości 1,55 TiC a w drugim do zawartości 3,97% TiC. Uzyskane rezultaty wskazują że przy zawartości 3,97 TiC nastopiło znaczące zwiększenie odporności na plastyczne odkszyałcenie warstwy wierzchniej pod wpływem...
-
Coastal cliff erosion as a source of toxic, essential and nonessential metals in the marine environment
PublicationDue to the rising environmental awareness, emissions and releases of pollutants, including metals, have been considerably reduced in the last decades. Therefore, the remobiliza-tion of natural and anthropogenic contaminants is gaining importance in their biogeochemical cycle. In the marine coastal zone, this process occurs during the erosion of a shore, especially the most vulnerable cliffs. The research was conducted in the...
-
Impedance monitoring of carbon steel cavitation erosion under the influence of corrosive factors
PublicationW pracy przedstawiono wyniki badań degradacji stali węglowych na skutek oddziaływania erozji-korozji kawitacyjnej. Do analizy wykorzystano technikę Dynamicznej Elektrochemicznej Spektroskopii Impedancyjnej oraz funkcję ubytku masy powszechnie stosowaną do oceny odporności kawitacyjnej materiałów. Oszacowanie stopnia degradacji powierzchni, a także wpływu erozji na odporność korozyjną jest możliwe po zastosowaniu odpowiedniego elektrycznego...
-
Cavitation erosion of some alloys manufactured on steel and iron surfaces by laser beam.
PublicationPrzedstawiono badania odporności kawitacyjnej stali węglowej 45 odpornej na korozję 2H13 i technicznego żelaza po ich obróbce laserowej. Warstwę wierzchnią wybranych stali wzbogacono w różne pierwiastki stopowe i badano odporność kawitacyjną na stanowisku z wirującą tarczą. Stwierdzono niską odporność kawitacyjną dla warstw o obniżonej zdolności do utwardzania pod wpływem obciążeń kawitacyjnych oraz silną zależność odporności...
-
Cavitation erosion of some laser-produced iron-base corrosion-resistance alloys
PublicationW pracy przedstawiono badania kawitacyjne stali C45, X20Cr13 oraz X5CrNi18-10 po laserowym stopowaniu ich warstwy wierzchniej proszkami Mn, Cr, Ni, Si, Ti, Co, Al, Mo, B. Badania kawitacyjne prowadzono na stanowisku z wirującą tarczą. Zniszczenia powierzchni w okresie inkubacji oceniano metodą optyczną. Przedstawiono związek pomiędzy uzyskaną mikrostrukturą obrabianej warstwy i jej odpornością kawitacyjną.
-
Cavitation erosion of chromium-manganese and chromium-cobalt coatings processed by laser beam
PublicationPrzedstawiono wyniki badań erozji kawitacyjnej napoin wykonanych za pomocą elektrod chromowo-manganowych i chromowo-niklowych oraz obrobionych wiązką lasera CO2 o mocy 1000 W. Próbki poddawano obciążeniom kawitacyjnym na stanowisku z wirującą tarczą. Zaobserwowano wzrost odporności kawitacyjnej napoin, w których dokonano przetopienia ich powierzchni promieniowaniem lasera.