Fabrication of anti-corrosion nitrogen doped graphene oxide coatings by electrophoretic deposition
PublicationThis work assesses anti-corrosion properties of graphene and N-doped graphene coatings deposited on copper by an electrophoretic method. Graphene oxide (GO) precursor was synthesized by an improved Hummers' method, whereas N-doping was performed hydrothermally in the presence of ammonia. After nitrogenation, doped graphene oxide samples (NGO) contained a reduced amount of oxygen and about 9% w/w nitrogen as pyridinic, pyrrole,...
-
Fabrication of anti-corrosion nitrogen doped graphene oxide coatings by electrophoretic deposition
Publication -
Applying of Doped Graphene Oxide Coatings for Corrosion Prevention
PublicationINTRODUCTION Graphene is a carbonaceous material characterized by extraordinary properties (high electron mobility, high surface area, high mechanical strength of 1100 GPa, very dense network hindering the passage of even the smallest helium atoms) [1]. Therefore, it found many applications, also as an anti-corrosive layer [2]. Electrophoretic Deposition (EPD) is one of the methods to deposit coatings. However, due to slight solubility...
-
Synergistic effects of nitrogen-doped carbon and praseodymium oxide in electrochemical water splitting
PublicationHybrid materials featuring perovskite-type metal oxide in conjunction with heteroatom-doped graphene hold immense promise as alternatives to costly noble metal catalysts for electrochemical water splitting, facilitating the generation of environmentally friendly hydrogen. In this study, perovskite-type oxide containing praseodymium, barium, strontium, cobalt, and iron atoms dispersed in a carbon matrix as a catalyst is synthesized...
-
Effect of Functionalization of Reduced Graphene Oxide Coatings with Nitrogen and Sulfur Groups on Their Anti-Corrosion Properties
PublicationElectrophoretic production of anticorrosion carbonaceous coatings on copper could be successfully performed by anodic oxidation of negatively charged graphene platelets suspended in an aqueous solution. The various platelets were synthesized by Hummer’s method followed by a hydrothermal reduction in the presence of NH4SCN which was expected to substitute some parts of graphene structure with nitrogen and sulfur groups. X-ray photoelectron...
-
Efficient removal of dyes and proteins by nitrogen-doped porous graphene blended polyethersulfone nanocomposite membranes
Publication -
Core-shell cobalt particles Co@CoO loaded on nitrogen-doped graphene for photocatalytic water-splitting
Publication -
Electrochemical determination of neurotransmitter serotonin using boron/nitrogen co-doped diamond-graphene nanowall-structured particles
PublicationElectrode fouling is a major issue in biological detection due to the adhesion of the protein itself and polymerization of biomolecules on the electrode surface, impeding the electron transfer ability and decreasing the current response. To overcome this issue, the use of anti-fouling material, especially boron-doped diamond (BDD) electrode, is an alternative way. However, the electrocatalytic activity of BDD is inadequate compared...
-
Nitrogen‐Doped Porous Graphene‐Based Aerogels toward Efficient Heavy Metal Ion Adsorption and Supercapacitor Applications
Publication -
X-ray diffraction spectra of nitrogen-doped carbon in hybrid materials containing praseodymium oxide
Open Research DataX-ray powder diffraction patterns of samples were carried out by Philips X’Pert diffractometer, which was radiated by graphite monochromatized Cu Kα (l equal 1.540598). The operating voltage was maintained at 40 kV, the current was maintained at 30 mA and analyzed in the range from 20° to 90°. The data presented confirmed the presence of the PrBSCF...
-
Graphene oxide thin films deposited on a PCB board - chemical analysis
Open Research DataGraphene oxides based films were measured by X-ray photoemission spectroscopy (XPS) method. TheXPS measurements were carried out with the Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The...
-
XPS analysis of the GO based materials
Open Research DataGraphene oxides samples were measured by XPS method. The X-ray photoemission spectroscopy measurements were carried out with Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The photoelectrons...
-
Study of the NO2 sensing mechanism of PEDOT-RGO film using in situ Raman Spectroscopy
PublicationIn this work, the mechanism of the NO2 reaction with PEDOT-RGO composite film has been investigated via in situ Raman spectroscopy. Reduced graphene oxide (RGO), poly(3,4-ethylenedioxytiophene)-reduced graphene oxide (PEDOT-RGO) and poly(3,4-ethylenedioxytiophene)/ClO4− (PEDOT/ClO4−) films were fabricated using an electrodeposition method and used as resistance sensors of gaseous nitrogen dioxide. The experimental results indicate...
-
Stable Field Electron Emission and Plasma Illumination from Boron and Nitrogen Co‐Doped Edge‐Rich Diamond‐Enhanced Carbon Nanowalls
PublicationSuperior field electron emission (FEE) characteristics are achieved in edge-rich diamond-enhanced carbon nanowalls (D-ECNWs) grown in a single-step chemical vapor deposition process co-doped with boron and nitrogen. The structure consists of sharp, highly conductive graphene edges supplied by a solid, diamond-rich bottom. The Raman and transmission electron microscopy studies reveal a hybrid nature of sp3-diamond and sp2-graphene...
-
Obrony prac doktorskich na Wydziale Chemicznym
EventsDn. 26.04.2022 r. o godz. 8.30 w Audytorium 1.4 Wydziału Chemicznego PG (budynek nr 5) odbędzie się w trybie hybrydowym obrona pracy doktorskiej mgr inż. Karoliny Grajewskiej.
-
N-doped mesoporous carbon nanosheets obtained by pyrolysis of a chitosan–melamine mixture for the oxygen reduction reaction in alkaline media.
PublicationBy simple thermal decomposition of low-cost precursors (chitosan, melamine) in an inert atmosphere, nitrogen-doped porous carbonaceous materials were prepared. The samples pyrolyzed at 700 C are composed of mainly mesoporous nitrogen-doped carbon nanosheets and partially graphitized carbon. The nanosheets contain a disordered area due to the strain imposed by the presence of nitrogen and/or oxygen groups in their structure. Some...
-
Photoelectrochemically Active N‐Adsorbing Ultrathin TiO2 Layers for Water‐Splitting Applications Prepared by Pyrolysis of Oleic Acid on Iron Oxide Nanoparticle Surfaces under Nitrogen Environment
PublicationHighly performing photocatalytic surfaces are nowadays highly desirable in energy fields, mainly due to their applicability as photo water‐splitting electrodes. One of the current challenges in this field is the production of highly controllable and efficient photoactive surfaces on many substrates. Atomic layer deposition has allowed the deposition of photoactive TiO2 layers over wide range of materials and surfaces. However,...
-
Enhanced gas sensing by graphene-silicon Schottky diodes under UV irradiation
PublicationThe effect of ultraviolet (UV) or blue irradiation on graphene/n-doped silicon Schottky junctions toward gas sensing was investigated. Schottky diodes were subjected to oxidizing nitrogen dioxide (NO2, 1–3 ppm) and reducing tetrahydrofuran (THF, 50–200 ppm), showing significantly different responses observed on the currentvoltage (I-V) characteristics, especially under UV light (275 nm). NO2 affected the resistive part of the forward region...
-
Graphene oxide, reduced graphene oxide and composite thin films NO2 sensing properties
PublicationA graphene oxide (GO), reduced graphene oxide (RGO) and poly(3,4-ethylenedioxytiophene)-reduced graphene oxide (PEDOT-RGO composite) gas sensors were successfully fabricated using an electrodeposition method. The electrodeposition was carried out in aqueous GO dispersions. To obtain RGO and PEDOT-RGO, the electrochemical reduction of GO and PEDOT-GO was carried out in 0.1 M KCl at a constant potential of −0.85 V. The GO, RGO and PEDOT-RGO...
-
Graphene oxide, reduced graphene oxide and composite thin films NO2 sensing properties
PublicationA graphene oxide (GO), reduced graphene oxide (RGO) and poly(3,4-ethylenedioxytiophene)- reduced graphene oxide (PEDOT-RGO composite) gas sensors were successfully fabricated using an electrodeposition method. The electrodeposition was carried out in aqueous GO dispersions. In order to obtain RGO and PEDOT-RGO, the electrochemical reduction of GO and PEDOT-GO was carried out in 0.1 M KCl at constant potential of −0.85 V. The GO, RGO...