The purpose of this investigation was to conduct the failure analysis of 501 AISI furnace tubes places before distillation column in fractional distillation unit. The investigated furnace tubes were planned to work for ten years however after just two years of exploitation <30% of the material left. The observed corrosion process had the intense and complex character. The well-adhered shiny black deposits and deep, round pits were present after 2 years of exploitation. There is no direct explanation in the norms and standards for such abnormal intense corrosion taking place in described petroleum unit. The study based on the visual, optical and electron microscopy with chemical analysis via SEM and EDX of deposits was performed. Too high allowable operating temperature was identified as a main cause of such intense corrosion. The same measurements were performed for parallel working furnace tubes which was not subjected to premature degradation and were collected after 10 years of its normal operation in the installation. The performed measurements allowed us to determine that metal dusting as a the source of catastrophical corrosion. The work includes also an appropriate action in order to avoid the described corrosion threat.
Cytowania
-
6
CrossRef
-
0
Web of Science
-
5
Scopus
Autorzy (5)
-
Jan Dampc
- Grupa LOTOS S.A.
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
ENGINEERING FAILURE ANALYSIS
nr 91,
strony 108 - 114,
ISSN: 1350-6307 - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Orlikowski J., Jażdżewska A., Darowicki K., Karczewski J., Dampc J.: Metal dusting phenomena of 501 AISI furnace tubes in refinery fractional distillation unit// ENGINEERING FAILURE ANALYSIS. -Vol. 91, (2018), s.108-114
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.engfailanal.2018.04.021
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 120 razy
Publikacje, które mogą cię zainteresować
Effect of wet Hydrogen Sulfide on Carbon Steels Degradation in Refinery Based on Case Study
- J. Orlikowski,
- A. Jażdżewska,
- İ. Uygur
- + 3 autorów