Thermal behaviour of vanadium xerogel powder under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 500°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 500°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 1000°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 1000°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 400°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 400°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 700°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 700°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 800°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 800°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 600°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 600°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of NH4VO3 microcasketoids
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microcasketoids under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 nanoflowers
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate nanoflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 elongated microcrystals
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate elongated microcrystals under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass...
-
Thermal behaviour of commercial avaible NH4VO3
Dane BadawczeThe DataSet contains the results of the thermal behavior of the commercially available ammonium metavanadate (CAS 7803-55-6) under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also...
-
Thermal behaviour of NH4VO3 microflowers
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behavior of TeOx powder
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
XRD patterns of TeOx powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised to 75°C for the...
-
Depth XPS profile of Fe-S layers on a titanium substrate
Dane BadawczeDepth XPS profile of Fe-S layers on a titanium substrate was measured. Material was etched by Argon ion gun and measured by XPS method. For each sample, three times per 10 minutes each was sputtered.
-
Thermal behavior of TeOx xerogel powder under different atmospheres
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx xerogel powder measured under different atmospheres. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution...
-
Comparison of XPS spectra of Ag3d for silver nanostructures and bulk material
Dane BadawczeAg nanostructures were prepared on borosilicate glass (Corning 1737F) and Si substrates. In both cases, the substrateswere cleaned with acetylacetone and then rinsed in ethanol. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The...
-
Investigation of plasmon resonance in a silver nanoparticles
Dane BadawczeSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
Depth XPS profile of vanadium pentoxide
Dane BadawczeVanadium pentoxide sample was manufactured by sol-gel method and deposited on a substrate by spin coating technique. To determine depth profile of chemical composition of thin film, etching by Argon ion gun was used. Thin film was etched three times. Chemical composition was measured by XPS method.
-
XRD patterns of TeOx-BaO-BiO powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx-BaO-BiO powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor), barium carbonate, and bismuth carbonate with thetraetylene glycol, water, ethanol, and acetic acid. (Samples molar concentration: 73TeO2-4BaO-3Bi2O3 and 73TeO2-3BaO-4Bi2O3)....