Wyniki wyszukiwania dla: BIMETALLIC (AG/AU) NANOPARTICLES
-
Optical properties of MnO-B2O3 based glass
Dane BadawczeMnO-B2O3 based glass with Au nanoparticles samples were annealing for a various time (in a range of 24-96 hours) at various temperatures (from 340 up to 350 deg.). Presence of silver nanoparticles was detected by UV-VIS measurements. On the basis of change optical bandgap, Ag NPs was detected.
-
Depth profile of the gold-silver bimetallic structures
Dane BadawczeSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
Plasmon resonance in gold-silver nanoalloys
Dane BadawczeSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
TEM imaging of Ag-Au nanoalloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of metal thin layers (Au/Ag or Ag/Au) followed by annealing under 550 Celsius degree in an argon atmosphere. The basic single layer thickness was usually ca. 3 nm. For investigations two samples wih 50% Au and 50% Ag were selected and samples 1/3 Ag - 2/3 Au and 2/3 Ag - 1/3...
-
Depth profile of the chemical composition of the Au-Ag multilayers
Dane BadawczeSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
Detection of the Ag nanoparticles in Te-Bi-Ba-Oa glass
Dane BadawczeThe influence of the manufacturing parameters of tellurium-bismuth-barium glasses on the presence of silver nanoparticles was investigated. Glasses were annealed at 330, 335, 340, 345 and 350 degrees Celsius for 24 and 48 hours. Presence of the Ag nanoparticles was measured by XPS method. The growth of nanoparticles was observed along with the extension...
-
Electrical and noise responses of Graphene-Silicon Schottky diodes decorated with Au nanoparticles for light-enhanced sensing of organic gases
Dane BadawczeGraphene-Silicon Schottky junctions decorated with Au nanoparticles were used for light-enhanced detection of organic tetrahydrofuran and chloroform. Au nanoparticles exhibited localized surface plasmon resonance (LSPR) in the range of yellow light; thus yellow LED (wavelength of 592 nm) was utilized to induce the plasmonic effect, that increased the...
-
Chemical analysis of the Au-Ag nanoaloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Au nanoparticles identifiction with the use of AFM Volta potential mapping
Dane BadawczeThe specific physical, chemical and electrochemical electrical properties of gold nanoparticles have led to their extensive use as high-performance chemical and biochemical sensors. The described properties relate to surface plasmon resonance, fluorescence quenching or enhancement, high electrical conductivity and light scattering. The described nanoparticles...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Dane BadawczeThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed to force the exsolution process of bimetallic nanoparticles.
-
The electrochemical response to Au electrode modification steps towards viral electrochemical immunosensor preparation
Dane BadawczeThe dataset contains the electrochemical measurements (CV/EIS) carried out for the consecutive steps of the Au electrode functionalization, in separate subfolders, as described. The cyclic voltammetry (CV) was conducted using a Palmsens 4 potentiostat/galvanostat system (Methrom, Autolab, Netherlands) in the standard three-electrode configuration, with...
-
The electrochemical response to glassy carbon electrode modification steps towards viral electrochemical immunosensor preparation
Dane BadawczeThe dataset contains the electrochemical measurements (CV/EIS) carried out for the consecutive steps of the glassy carbon GC electrode functionalization, in separate subfolders, as described. The cyclic voltammetry (CV) was conducted using a Palmsens 4 potentiostat/galvanostat system (Methrom, Autolab, Netherlands) in the standard three-electrode configuration,...