Wyniki wyszukiwania dla: high pressure at subzero temperature
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of water cooled materia
Dane BadawczeThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of reference material materia (transverse direction)
Dane BadawczeThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of reference material materia (longitudinal direction)
Dane BadawczeThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - microstructure of naturally colled material
Dane BadawczeThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - microstructure of water cooled material
Dane BadawczeThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - microstructure of reference material
Dane BadawczeThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of naturally cooled material
Dane BadawczeThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Imaging of ferroelectric properties of sinter by means of Piezoresponse Force Microscopy
Dane BadawczeFerroelectricity is a property of certain materials [1], characterized by a spontaneous electrical polarization that can be reversed by applying an external electric field. Ferroelectric properties can be used to make capacitors with adjustable capacity. The permeability of ferroelectrics is not only regulated, but usually also very high, especially...
-
The luminescence study of Sr0.98Li2.5 + zAl1.5 – zO3 + 2zN1 – 2z:0.02Eu coumpounds.
Dane BadawczeEu2+-doped UCr4C4-type oxynitride phosphors are emerging innovative materials to replace oxide and nitride phosphors for high-end light-emitting devices. A series of Sr0.98Li2.5 + zAl1.5 – zO3 + 2zN1 – 2z:0.02Eu phosphors were synthesized by collaborators from the National Taiwan University by precursor engineering, and these products showed an unexpected...
-
Long-term measurements from a photovoltaic power plant and meteorological stations at the Laboratory LINTE^2 of Gdańsk University of Technology
Dane Badawcze1) The Laboratory LINTE^2 is a large research infrastructure operated by the Faculty of Electrical and Control Engineering at Gdańsk University of Technology, to be found in Gdańsk, Poland (54.3690 N, 18.6130 E). 2) The measurements have been collected from a photovoltaic power plant located on the roof of the laboratory, having total capacity...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #5.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #5. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #10.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #10. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #9.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #9. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 1281 mA. Sample J51, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 1098 mA. Sample J51, experiment run #2. The current is extremely high for this type of sample to accelerate ageing processes.The images were taken...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #6.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #6. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #12.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #12. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #4.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #4. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #11.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103, experiment run #11. Continuation of experiment at high voltage to accelerate the ageing process.The images were taken with thermographic...