Chemical analysis of the Au-Ag nanoaloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Electrochemical studies of Boron-Doped Diamond enriched Laser Induced Graphene structures
Dane BadawczeThis dataset contains electrochemical studies aimed to evaluate the capability of the utilization of laser-induced graphene (LIG) with incorporated boron-doped diamond nanowall (BDNW) hybrid nanostructures for microsupercapacitors. Selected results from this dataset were published in Advanced Functional Materials journal: https://doi.org/10.1002/adfm.202206097
-
DSC measurments of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the thermal behavior of the ammonium vanadate nanostructures obtained by the hydrothermal method with different conditions. Differential scanning calorimetry (DSC) measurement was carried out under an argon atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The results reveal the differences...
-
Rate performance of (NH4)2V10O25·8H2O as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the ammonium vanadate nanostructures obtained by the hydrothermal method under an initial pressure of 50 bar ((NH4)2V10O25·8H2O). The battery tests of the samples were performed using the ATLAS 0961 MBI multichannel battery testing system with different current densities in the voltage...
-
Depth profile of the gold-silver bimetallic structures
Dane BadawczeSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
Rate performance of mixture (NH4)2V6O16 and (NH4)2V10O25·8H2O as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the ammonium vanadate nanostructures obtained by the hydrothermal method without initial pressure (mixture (NH4)2V6O16 and (NH4)2V10O25·8H2O). The battery tests of the samples were performed using the ATLAS 0961 MBI multichannel battery testing system with different current densities...
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
SEM images of dewetted gold films
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. as a result of dewetting process. Thin golds films were deposited using a table-top dc magnetron sputtering coater under pure Ar plasma conditions . The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness...
-
X-ray Photoelectron Spectroscopy studies of ammonium vanadate
Dane BadawczeThe DataSet contains the high-resolution XPS studies of the ammonium vanadate nanostructures obtained by the hydrothermal method. XPS analyses were carried out with an X-ray photoelectron spectrometer (Omicron NanoTechnology) with a 128-channel collector. The measurements were performed at room temperature in an ultra-high vacuum condition (below 1.1x10-8...
-
Thermal behaviour of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the thermal behavior of the ammonium vanadate nanostructures obtained by the hydrothermal method with different conditions. Thermogravimetric analysis (TG) was carried out under an argon atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
AFM and SSRM investiagtion of carbon nanowalls properties
Dane BadawczeStructures with limited dimensionality are of great interest in modern nanotechnology. The properties of these objects are used, among others, for the construction of modern displays or as a base for quantum computers. Carbon nanowalls, which are the subject of the imaging results contained in this collection, are also considered interesting building...
-
Colvolutional calibration of AFM probe
Dane BadawczeAtomic force microscopy is based on the interaction of the examined surface with a probe of a pyramidal shape, tipped with a sharp end with a radius of curvature ranging from single nanometers to hundreds of nanometers. The resolution of the obtained image is of course dependent on the above-mentioned geometric size, and the resulting image is a convolutional...
-
Chemical composition of V2O5 nanorods
Dane BadawczeThe DataSet contains the chemical compositions of the V2O5 nanorods on a silicon substrate. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The As-prepared thin films were annealed at 600C under a synthetic air atmosphere.