Elctrochemical oxidation and corrosion resistance of the Ti13Nb13Zr alloy
PublikacjaThis paper presents the results of oxidation and corrosion tests carried out on titanium alloy Ti13Nb13Zr. The oxide film was prepared by electrochemical environment 2M H3PO4 for 30 min and 1 h, at a constant voltage 40V. The tests of corrosion resistance were performed by potentiostatic method in Ringer's solution at different pH values: 7, 5 and 3. The change in an appearance of surface and the increase in corrosion resistance...
-
Hydroxyapatite deposition on the laser modified Ti13Nb13Zr alloy
PublikacjaThe Ti13Nb13Zr alloy was subjected to laser modification with the Nd:YAG laser provided that such treatment would increase the surface roughness followed improved adhesion of hydroxyapatite (HAp) coatings The hydroxyapatite was deposited by electrophoretic method in suspension of 0.5 g HA powder and 100 ml ethyl alcohol. The deposition was carried out for 10 min at 10 V voltage followed by drying at room temperature for 24 h and...
-
Properties of Composite Oxide Layers on The Ti13Nb13Zr Alloy
PublikacjaThe development of composite oxide layers on the Ti13Nb13Zr alloy, their structure and properties have been demonstrated. Two subsequent methods were applied to prepare the composite layers. During the first stage gas oxidation produced a solid oxide layer, and subsequently oxide nanotubes were produced by using an electrochemical method. Scanning electron microscopy (SEM), chemical analysis, energy dispersive X-ray spectroscopy...
-
Surface treatment of porous Ti13Nb13Zr alloy for biomedical applications
PublikacjaPrzeprowadzono badania materiału porowatego, przeznaczonego na implanty ortopedyczne, wytworzonego metodą metalurgii proszków ze stopu Ti13Nb13Zr. Proszki z badanego stopu uzyskano metodą rozpylania plazmowego. Otrzymano próbki o otwartej porowatej strukturze, stopniu porowatości do 68% i średniej wielkości porów w przedziale 30-150 mikrometrów. Obróbka próbek porowatych - utlenianie termiczne, chemiczne i/lub elektrochemiczne...
-
Preparation of nano-tubular oxide layers on titanium alloy Ti13Nb13Zr
PublikacjaThe article presents results of oxidation tests and corrosion investigations of titanium alloy Ti13Nb13Zr preformed at different conditions. The oxide layers have been formed using electrochemical method in 2M H3PO4 + 0,3% HF solution for 30 min. and 1h at 20V constant voltage. The corrosion tests heve been made with poteniodynamic method in Ringer's solution at pH ranged 3 and 7. It has been shown that the nano-oxide films, which...
-
Nanotubular oxide layers and hydroxyapatite coatings on porous titanium alloy Ti13Nb13Zr
PublikacjaThe surface condition of an implant has a significant impact on response occurring at the implant-biosystem border. The knowledge of physical-chemical and biological processes allows for targeted modification of biomaterials to induce a specified response of a tissue. The present research was aimed at development of technology composing of obtaining the nanotube oxide layers on a porous titanium alloy Ti13Nb13Zr, followed by the...
-
Mechanical and Corrosion Properties of Laser Surface-Treated Ti13Nb13Zr Alloy with MWCNTs Coatings
Publikacja: Titanium and its alloys is the main group of materials used in prosthetics and implantology. Despite their popularity and many advantages associated with their biocompatibility, these materials have a few significant disadvantages. These include low biologic activity—which reduces the growth of fibrous tissue and allows loosening of the prosthesis—the possibility of metallosis and related inflammation or other allergic reactions,...
-
Microstructure and mechanical properties of laser surface-treated Ti13nb13zr alloy with MWCNTs coatings
PublikacjaLaser surface modification of titanium alloys is one of the main methods of improving the properties of titanium alloys used in implantology. This study investigates the microstructural morphology of a laser-modified surface layer on a Ti13Nb13Zr alloy with and without a carbon nanotube coating deposited by electrophoretic deposition. Laser modification was performed for samples with and without carbon nanotube coating for two...
-
Mechanical Behavior of Bi-Layer and Dispersion Coatings Composed of Several Nanostructures on Ti13Nb13Zr Alloy
PublikacjaTitanium implants are commonly used because of several advantages, but their surface modification is necessary to enhance bioactivity. Recently, their surface coatings were developed to induce local antibacterial properties. The aim of this research was to investigate and compare me-chanical properties of three coatings: multi-wall carbon nanotubes (MWCNTs), bi-layer composed of an inner MWCNTs layer and an outer TiO2 layer, and...
-
THE EVALUATION OF THE ABRASIVE WEAR OF THE TI13Nb13ZR ALLOY IMPLANTED BY NITROGEN IONS FOR FRICTION COMPONENTS OF THE HIP JOINT ENDOPROSTHESES
PublikacjaZ uwagi na potrzeby społeczne, a zwłaszcza rosnące zapotrzebowanie na endoprotezy stawów biodrowego i kolanowego oraz uwzględniając fakt, że procesy tribologiczne odgrywają wiodącą rolę w procesie utraty stabilności endoprotez ortopedycznych i decydują o ich trwałości, uznano za celowe przeprowadzenie oceny wpływu implantacji jonowej na zużycie ścierne biostopu Ti13Nb13Zr. Do badań wykorzystano pary trące: nieimplantowany stop...
-
Mechanical Properties and Wear Susceptibility Determined by Nanoindentation Technique of Ti13Nb13Zr Titanium Alloy after “Direct Laser Writing”
PublikacjaLaser treatment has often been applied to rebuild the surface layer of titanium and its alloys destined for long-term implants. Such treatment has always been associated with forming melted and re-solidified thin surface layers. The process parameters of such laser treatment can be different, including the patterning of a surface by so-called direct writing. In this research, pulse laser treatment was performed on the Ti13Nb13Zr...
-
Effect of hybrid modification by ceramic layer formation in MAO process and laser remelting on the structure of titanium bio-alloy Ti13Nb13Zr
PublikacjaTo improve the biological properties of titanium alloy Ti13Nb13Zr, hybrid modifications involving micro-arc oxidation (MAO) and Nd: YAG laser remelting were carried out in two combinations. The first consisted of laser modification before the production of the ceramic layer by the micro-arc oxidation process, and the second combination involved Nd: YAG laser modification after the MAO process. The creation of developed surface...
-
Osteoblast and bacterial cell response on RGD peptide‐functionalized chitosan coatings electrophoretically deposited from different suspensions on Ti13Nb13Zr alloy
PublikacjaMetallic materials for long-term load-bearing implants still do not provide high antimicrobial activity while maintaining strong compatibility with bone cells. This study aimed to modify the surface of Ti13Nb13Zr alloy by electrophoretic deposition of a chitosan coating with a covalently attached Arg-Gly-Asp (RGD) peptide. The suspensions for coating deposition were prepared in two different ways either using hydroxyacetic acid...
-
The Influence of Laser Alloying of Ti13Nb13Zr on Surface Topography and Properties
PublikacjaThe laser alloying is a continually developing surface treatment because of its significant and specific structuration of a surface. In particular, it is applied for Ti alloys, being now the most essential biomaterials` group for load-bearing implants. The present research was performed on the Ti13Nb13Zr alloy subject to laser modification in order to determine the treatment effects on surface topography and its some mechanical...
-
Formation of High Corrosion Resistant Nanotubular Layers on TitaniumAlloy Ti13Nb13Zr
PublikacjaThis paper presents results of oxidation tests and corrosion investigations of titanium alloy Ti13Nb13Zr performed at different conditions. The oxide layers have been formed by electrochemical method in 2M H3PO4 + 0.3% HF solution for 30 min. and 1 h at 20 V constantvoltage. The corrosion tests have been made by potentiodynamic method in Ringer`s solution at pH ranged between 3 and 7. It has been shown that the nano-oxide films,...
-
Wytwarzanie nanowarstwy tlenku tytanu na stopie tytanu Ti13Nb13Zr
PublikacjaW pracy przedstawiono wyniki badań utleniania stopu Ti13Nb13Zr. Warstwę tlenkową wytworzono metodą elektrochemiczną w środowisku 1M H3PO4 + 0,3 % HF w czasie 30 min , przy stałym napięciu 30V. Utlenione próbki poddano analizie na skaningowym mikroskopie elektronowym. Stwierdzono obecność nanorurkowych warstw tlenkowych o średnicach wewnętrznych 60-100 nm.
-
Formation of High Corrosion Resistant Nanotubular Layers on TitaniumAlloy Ti13Nb13Zr
PublikacjaThis paper presents results of oxidation tests and corrosion investigations of titanium alloy Ti13Nb13Zr performed at different conditions. The oxide layers have been formed by electrochemical method in 2M H3PO4 + 0.3% HF solution for 30 min. and 1 h at 20 V constantvoltage. The corrosion tests have been made by potentiodynamic method in Ringer`s solution at pH ranged between 3 and 7. It has been shown that the nano-oxide films,...
-
Wpływ modyfikacji laserowej stopu Ti13Nb13Zr na mikrostrukturę powłok hydroksyapatytowych
PublikacjaDotychczasowe badania powierzchni wszczepów tytanowych dla chirurgii kostnej wykazały, że osteointegracja na powierzchniach rozwiniętych jest znacznie szybsza niż na powierzchniach gładkich, co za tym idzie chropowatość powierzchni implantu ma bardzo duży wpływ na adhezję składników środowiska biologicznego. W artykule przedstawiono wstępne wyniki badań dotyczące wpływu chropowatości powierzchni stopu Ti13Nb13Zr o bardzo małym...
-
Ocena odporności na zużycie ścierne stopów Ti na elementy pary trącej endoprotez stawu kolanowego
PublikacjaNajczęściej stosowanym biomateriałem tytanowym na elementy endoprotez stawu kolanowego jest stop Ti6Al4V. Z uwagi na zawartość wanadu, zaliczanego do pierwiastków o dużej toksyczności podejmowane są działania w kierunku zastąpienia wskazanego stopu - stopami bezwanadowymi. Jednym z najbardziej obiecujących jest stop Ti13Nb13Zr zawierający w swoim składzie jedynie pierwiastki witalne, niewywołujące stanów zapalnych i odczynów...
-
Modyfikacja powierzchni stopu Ti13Nb13Zr metodą implantacji jonowej w aspekcie zastosowania na elementy trące w endoprotezach ortopedycznych
PublikacjaW celu określenia wpływu wybranych czynników tribologicznych na intensywność zużycia ściernego pary trącej złożonej z nowoczesnego stopu tytanu Ti13Nb13Zr oraz PE-UHMW, przeprowadzono badania tribologiczne. Uzyskane wyniki badań wykazały zbyt niską odporność na zużycie ścierne stopu tytanu Ti13Nb13Zr. Stosunkowo niska trwałość badanego stopu tytanu, wskazuję na potrzebę modyfikacji jego powierzchni w celu zwiększenia twardości....