Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 613 K was measured by impedance spectroscopy method.
-
Sea ice floe size and shape data from a very high resolution satellite image (Knox Coast, East Antarctica)
Dane BadawczeThis dataset contains floe size distribution data from a very high resolution (pixel size: 0.3 m) optical satellite image of sea ice, acquired on 16. Feb. 2019 off the Knox Coast (East Antarctica). The image shows relatively small ice floes produced by wave-induced breakup of landfast ice between the Mill Island and Bowman Island. The ice floes are...
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 annealed glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 473 K for 3h and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 fully crystallized glass at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 partially crystallized glass at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 partially crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Bricks images dataset
Dane BadawczeThe set contains 200 images of various wooden bricks of various shapes and colors placed on a background (blanket) with some heart shaped patterns. Each photo is available in 300x300 and 224x224 pixels size in PNG format. Photos are divided in 10 classes – 8 types of bricks photographed form various angles + 2 additional classes (multiple bricks at...
-
AVHRR Level1CD covering Baltic Sea area year 2006
Dane BadawczeThe product level is the NOAA AVHRR Level 1C that is result of processing the AVHRR data from the HRPT stream based on ancillary information like sensing geometry and calibration data. Then converted into geophysical variables: top-of-the atmosphere (TOA) albedo or brightness temperature. Additionally, information like geolocation has been added. Other...
-
AVHRR Level1CD covering Baltic Sea area year 2010
Dane BadawczeThe product level is the NOAA AVHRR Level 1C that is result of processing the AVHRR data from the HRPT stream based on ancillary information like sensing geometry and calibration data. Then converted into geophysical variables: top-of-the atmosphere (TOA) albedo or brightness temperature. Additionally, information like geolocation has been added. Other...
-
AVHRR Level1CD covering Baltic Sea area year 2007
Dane BadawczeThe product level is the NOAA AVHRR Level 1C that is result of processing the AVHRR data from the HRPT stream based on ancillary information like sensing geometry and calibration data. Then converted into geophysical variables: top-of-the atmosphere (TOA) albedo or brightness temperature. Additionally, information like geolocation has been added. Other...
-
AVHRR Level1CD covering Baltic Sea area year 2011
Dane BadawczeThe product level is the NOAA AVHRR Level 1C that is result of processing the AVHRR data from the HRPT stream based on ancillary information like sensing geometry and calibration data. Then converted into geophysical variables: top-of-the atmosphere (TOA) albedo or brightness temperature. Additionally, information like geolocation has been added. Other...
-
AVHRR Level1CD covering Baltic Sea area year 2012
Dane BadawczeThe product level is the NOAA AVHRR Level 1C that is result of processing the AVHRR data from the HRPT stream based on ancillary information like sensing geometry and calibration data. Then converted into geophysical variables: top-of-the atmosphere (TOA) albedo or brightness temperature. Additionally, information like geolocation has been added. Other...
-
AVHRR Level1CD covering Baltic Sea area year 2008
Dane BadawczeThe product level is the NOAA AVHRR Level 1C that is result of processing the AVHRR data from the HRPT stream based on ancillary information like sensing geometry and calibration data. Then converted into geophysical variables: top-of-the atmosphere (TOA) albedo or brightness temperature. Additionally, information like geolocation has been added. Other...
-
AVHRR Level1CD covering Baltic Sea area year 2009
Dane BadawczeThe product level is the NOAA AVHRR Level 1C that is result of processing the AVHRR data from the HRPT stream based on ancillary information like sensing geometry and calibration data. Then converted into geophysical variables: top-of-the atmosphere (TOA) albedo or brightness temperature. Additionally, information like geolocation has been added. Other...
-
AVHRR Level1CD covering Baltic Sea area year 2001
Dane BadawczeThe dataset contains data derived from recordings of the AVHRR/3 radiometer operating on board the NOAA POES (Polar Orbiting Environmental Satellites) Series - 5th Generation Satellites covering the Baltic Sea area. The satellite data was recorded in the years 2000-2012 directly by the HRPT station installed at the University of Gdańsk. The registration...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-002)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-Con)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-004)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-006)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Acoustic emission studies of the 7075 aluminium alloy pitting corrosion process
Dane BadawczeThe dataset contains the cyclic polarization studies and corresponding acoustic emission measurements, revealing the pitting corrosion process of the passive layer at the surface of the 7075 aluminum alloy in the borate buffer with different chloride ions concentrations, in the range between 0.05 and 25 mM.
-
Long term measurements of PM1, PM2.5, PM10 and NO2 in open-air at Gdansk (Poland) area using low-cost sensors together with the reference results
Dane BadawczeThe measurements results of open-air measurements made using the following low-cost sensors: particulate matter (PM) sensor SPS30 from Sensirion, NO2 electrochemical sensor SGX-7NO2 from SGX Sensortech, NO2 electrochemical sensor 7E4-NO2 from SemaTech, compact MOS air quality sensor MiCS 2714 from SGX Sensortech, BME280 (Bosch) environmental sensor...
-
AVHRR Level1CD covering Baltic Sea area year 2005
Dane BadawczeThe dataset contains data derived from recordings of the AVHRR/3 radiometer operating on board the NOAA POES (Polar Orbiting Environmental Satellites) Series - 5th Generation Satellites covering the Baltic Sea area. The satellite data was recorded in the years 2000-2012 directly by the HRPT station installed at the University of Gdańsk. The registration...
-
AVHRR Level1CD covering Baltic Sea area year 2004
Dane BadawczeThe dataset contains data derived from recordings of the AVHRR/3 radiometer operating on board the NOAA POES (Polar Orbiting Environmental Satellites) Series - 5th Generation Satellites covering the Baltic Sea area. The satellite data was recorded in the years 2000-2012 directly by the HRPT station installed at the University of Gdańsk. The registration...
-
AVHRR Level1CD covering Baltic Sea area year 2003
Dane BadawczeThe dataset contains data derived from recordings of the AVHRR/3 radiometer operating on board the NOAA POES (Polar Orbiting Environmental Satellites) Series - 5th Generation Satellites covering the Baltic Sea area. The satellite data was recorded in the years 2000-2012 directly by the HRPT station installed at the University of Gdańsk. The registration...
-
AVHRR Level1CD covering Baltic Sea area year 2002
Dane BadawczeThe dataset contains data derived from recordings of the AVHRR/3 radiometer operating on board the NOAA POES (Polar Orbiting Environmental Satellites) Series - 5th Generation Satellites covering the Baltic Sea area. The satellite data was recorded in the years 2000-2012 directly by the HRPT station installed at the University of Gdańsk. The registration...
-
Mechanical properties of VL E27 steel for shipbuilding – fracture toughness test in 0°C
Dane BadawczeOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Mechanical properties of VL E27 steel for shipbuilding – fracture toughness test in 20°C
Dane BadawczeOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....