Filtry
wszystkich: 3293
wybranych: 500
-
Katalog
- Publikacje 2048 wyników po odfiltrowaniu
- Czasopisma 42 wyników po odfiltrowaniu
- Konferencje 1 wyników po odfiltrowaniu
- Wydawnictwa 1 wyników po odfiltrowaniu
- Osoby 105 wyników po odfiltrowaniu
- Wynalazki 3 wyników po odfiltrowaniu
- Projekty 12 wyników po odfiltrowaniu
- Zespoły Badawcze 1 wyników po odfiltrowaniu
- Kursy Online 71 wyników po odfiltrowaniu
- Wydarzenia 25 wyników po odfiltrowaniu
- Dane Badawcze 984 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: LITY SPECTRP
-
Photoluminescence spectra of TiO2
Dane BadawczeThese data contain photoluminescence spectra of TiO2 measured at the temperature of liquid nitrogen. There is a comparison of the photoluminescence spectra of TiO2 heat treated at 400-600oC in the ambient (Ar) and reduced (H2) atmospheres. These emission spectra were recorded after TiO2 excitation with a wavelength of 290 nm
-
Raman spectra of CPMH and CPMD
Dane BadawczeThese data contains Raman spectra of CPMH and CPMD. Raman scattering was measured with a RenishawmicroRaman spectrometer (785 nm). Sample abbreviations (CPMH, CPMD) are in agreement with the markings used in the linked publication.
-
Raman spectra of MXenes catalysts
Dane BadawczeData contain results from Raman spectroscopy of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios. ...
-
FTIR spectra of V2O5 nanostructures
Dane BadawczeThe DataSet contains FTIR spectra of vanadium pentaoxide nanostructures obtained by the sol-gel with different annealing temperatures under synthetic air.
-
Calibration images under different lighting conditions vol. 2
Dane BadawczeDataset description: Calibration images under different lighting conditions vol. 1
-
Calibration images under different lighting conditions - static for feature localisation
Dane BadawczeDataset description: Calibration images under different lighting conditions - static mode for feature detection
-
Raman spectra for pyrolized natural compounds
Dane BadawczeThe presented data showcases the results of Raman spectroscopy analysis conducted on pyrolyzed natural compounds both with and without the inclusion of graphene. The study delved into four specific compounds: methylcellulose with lysine (ML), methylcellulose with lysine-graphene composite (MLG), algae (A), and algae-graphene composite (AG). Raman spectra...
-
Emission spectra of UV and fluorescent lamps
Dane BadawczeData contain emision spectra of two different UV lamps: Special "TL"E 22W/10 Black light (Philips) and Semilac UV, 36 W and also Fluorescent lamp: L22W/840 Circular Cool White, Lumilux (Osram). These spectra were recorded by USB4000 Fiber Optic Spectrometer.
-
The 3d Ce XPS spectra of Ce0.9M0.1O2
Dane BadawczeThe dataset consists of 3d Ce XPS of Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons were excited by an...
-
The XPS spectra of LSCNT sintered at 1200C
Dane BadawczeThe dataset includes XPS spectra of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini). The XPS spectra were collected for all species.
-
Electrochemical cell impedance spectra at Eoc
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Electron energy-loss spectra of isoxazole
Dane BadawczeThe data set contains numeric values of electron energy-loss spectra measured in isoxazole in the excitation energy range 3.5−10 eV. The data have been published in graphical form (figure 3 and figure 4) in the following paper:Ireneusz Linert, Mariusz Zubek "Excited states of isoxazole molecules studied by electron energy-loss spectroscopy"Journal...
-
Electron energy-loss spectra of pyridazine
Dane BadawczeThe data set contains numeric values of electron energy-loss spectra measured in pyridazine in the excitation energy range 2.5−10 eV. The data have been published in graphical form (figures 3 - 6) in the following paper:
-
FTIR spectra of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the FTIR spectra of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
UAV Survey Images - orthophotomap - Zukowo City
Dane BadawczeDataset description: Raw images from photogrammetric survey.Location: Żukowo, Pomorskie, Kartuski County, PolandDrone type: DJI Mavic Pro.Flight plan: Single gridTarget Product: OrthophotomapDate: 22.04.2018Direct georeferencing: yesMetadata data: yes/GPSGCP: yes (description and location in file)\GCP: RTK Camera Name: DJI FC220Model type: PerspectiveImage...
-
Electrochemical cell impedance spectra at Eoc+100mV
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Electrochemical cell impedance spectra at Eoc+200mV
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Methane (CH4) calibration set of FTIR spectra
Dane BadawczeThe calibration spectra for CH4 concentration calibration were supplied with this dataset
-
Electrochemical cell impedance spectra at Eoc-100mV
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
The 2p XPS spectra of transition metals in Ce0.9M0.1O2
Dane BadawczeThe dataset consists of 2p XPS spectra of transition metals in Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons...
-
Electrochemical cell impedance spectra at Eoc-200mV
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CLO catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Ce0.8La0.2O2 nanocatalyst. The specatra were collected every 1 minute.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using alumina catalyst - blank
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of blank sample Al2O3 for dry reforming of biogas (60/40 CH4-CO2). The specatra were collected every 1 minute.
-
FTIR spectra of Ce0.9M0.1O2 synthesised by reverse microemulsion method
Dane BadawczeThe dataset consist of the FTIR spectra of Ce0.9M0.1O2 synthesised by reverse microemulsion method, after calcination at 500 degrees.
-
X-ray diffraction spectra of the NiCo2O4 modified by carbon
Dane BadawczeThis dataset comprises XRD results for NiCo2O4 modified with carbon, varying according to the amount of carbon. In this context, the XRD data provide insights into the crystalline structure and phase composition of the NiCo2O4 material as it is modified with varying quantities of carbon. This investigation is valuable for understanding how the presence...
-
Carbon dioxide (CO2) calibration set of FTIR spectra
Dane BadawczeThe calibration spectra for CO2 concentration calibration were supplied with this dataset
-
The XPS spectra of Ce0.8Ni0.2O2 prepared using microemulsion method
Dane BadawczeThe dataset includes XPS spectra of Ce0.8Ni0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
Electrochemical impedance spectra and CV curves of V2O5 nanocrystals
Dane BadawczeThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanocrystals obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz...
-
The XPS spectra of Ce0.8Cu0.2O2 prepared using microemulsion method
Dane BadawczeThe dataset includes XPS spectra of Ce0.8Cu0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
Electrochemical impedance spectra and CV curves of V2O5 nanorods
Dane BadawczeThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanorods obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz for...
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CLO/Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Ce0.8La0.2O2+10wt.%Cu nanocatalyst. The specatra were collected every 1 minute.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CeO2/Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using CeO2+10wt.%Cu nanocatalyst. The specatra were collected every 1 minute.
-
Collective angst and collective action for progressive city policies: study4
Dane BadawczeWe conducted this study before the second term of the presidential election in Poland in 2020. Conservative-nationalist President Andrzej Duda’s rival was Rafał Trzaskowski, the liberal Mayor of Warsaw supported by Civic Platform [pol. Platforma Obywatelska] party. 456 residents of Gdańsk participated in the study (313 women, 3 non-binary) with M age...
-
Collective angst and collective action for progressive city policies: study1
Dane BadawczePaweł Adamowicz, the liberal mayor of Gdańsk, died on January 14, 2019, after being stabbed by a man who rushed onstage during a charity event. Three studies were carried out to analyze the predictors of willingness to engage in collective action for the support of the progressive city policies he initiated. In this study 1 (N = 214), the questionnaire,...
-
Collective angst and collective action for progressive city policies: study3
Dane BadawczePaweł Adamowicz, the liberal mayor of Gdańsk, died on January 14, 2019, after being stabbed by a man who rushed onstage during a charity event. Three studies were carried out to analyze the predictors of willingness to engage in collective action for the support of the progressive city policies he initiated. We conducted Study 3 to test the model with...
-
Collective angst and collective action for progressive city policies: study2
Dane BadawczePaweł Adamowicz, the liberal mayor of Gdańsk, died on January 14, 2019, after being stabbed by a man who rushed onstage during a charity event. Three studies were carried out to analyze the predictors of willingness to engage in collective action for the support of the progressive city policies he initiated. Since we assumed that the time after the...
-
XPS-Ni foam as received, after photocatalysis and after oxidation at 500_C.
Dane BadawczeThis dataset contains XPS spectra recorded for nickel foam as received from supplier, after photocatalytic process and after oxidation at 500C. Each set contains: survery spectrum, O1, C1s, Ni2p. The detailed equipment and measurement data was described in "readme XPS.txt" file
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using Al2O3/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using AlOOH/1%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CeO2/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using CeO2/5%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
Comparison of XPS spectra of Ag3d for silver nanostructures and bulk material
Dane BadawczeAg nanostructures were prepared on borosilicate glass (Corning 1737F) and Si substrates. In both cases, the substrateswere cleaned with acetylacetone and then rinsed in ethanol. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The...
-
Measurements of absorption and emission spectra of tryptophan in solutions of different pH
Dane BadawczeInvestigations of the absorption and fluorescence spectra of tryptophan in different environments were carried out, controlling the pH of the environment and the concentration of tryptophan.
-
Carbon (II) oxide (CO) calibration set of FTIR spectra
Dane BadawczeThe calibration spectra for CO concentration calibration were supplied with this dataset
-
Raman spectra and electrochemical data of carbon nanowall with tailored defects
Dane BadawczeThis dataset comprises of Raman spectra aquired with different excitation laser sources and the electrochemical data of defect-induced carbon nanowall electrodes (CNW).
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using Al2O3/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Al2O3 (TMDAR)/5%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
Raman data of deuterium and hydrogen grown boron-doped diamond
Dane BadawczeRaman spectra were recorded at room temperature using a micro-Raman spectrometer (Invia, Renishaw) equipped with an edge filter with different excitation wavelengths and lasers: UV λ = 325 nm (HeCd), blue λ = 488 nm (Ar+), green λ = 514 nm (Ar+), and IR λ = 785 nm (IR diode) and 50× microscope objective. To avoid sample heating, the radiation power...
-
XPS (X-ray photoelectron spectroscopy) survey spectra of CPMD and CPMH
Dane BadawczeXPS (X-ray photoelectron spectroscopy) survey spectra of CPMD and CPMH. XPS spectra were obtained using Al Kɑ (hv=1486.6 eV) radiation with a Prevac system equipped with a Scienta SES 2002 electron energy analyzer operating at constant transmission energy (Ep=50 eV). Sample abbreviations (CPMD, CPMH) are in agreement with the markings used in the linked...
-
Impedance spectra of ZnO varistor type 440 model A ver. M
Dane BadawczeThe impedance spectrum of high-voltage ZnO varistor obtained using FRA EIS impedance spectrosocpy measurement method. The 1V sinusoidal excitation was used. The frequency range was chosen from 10 kHz down to 100 uHz. The object under test and the measuring instrument were placed in a Faraday cage due to high impedance of the object. The data was acquired...
-
XRD (X-ray diffraction) spectra of bulk boron and obtained borophene
Dane BadawczeThis dataset includes XRD (X-ray diffraction) spectra of bulk boron and borophene obtained during sonication process, giving the information on the phase composition and crystallinity of materials.
-
Impedance spectra of ZnO varistor type 280 model A ver. M
Dane BadawczeThe impedance spectrum of high-voltage ZnO varistor obtained using FRA EIS impedance spectrosocpy measurement method. The 1V sinusoidal excitation was used. The frequency range was chosen from 10 kHz down to 100 uHz. The object under test and the measuring instrument were placed in a Faraday cage due to high impedance of the object. The data was acquired...
-
Impedance spectra of RC model as a result of testing pulse excitation measurement method
Dane BadawczeThe impedance spectrum of RC model object obtained using pulse excitation EIS impedance spectrosocpy measurement method. The 1V voltage pulse excitation duration was set to 0.1s and the total acqusition time was set to 1000s. The object under test was built using RC components connected as Baunier model of anticorrosion coating with the following components...