Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #30 - #31.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #30 (upper, rotating), #31 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #20 - #21.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #20 (upper, rotating), #21 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #22 - #23.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #22 (upper, rotating), #23 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #26 - #27.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #26 (upper, rotating), #27 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Tribological test for evaluation of Natural PEEK
Open Research DataTest of PEEK natural (beige color) samples with sliding speed up to 1,2 m/s and up to 8 MPa of nominal load
-
Tribological test for evaluation of CF30 Black PEEK
Open Research DataSample numner BL03 and BL04 made of PEEK CF30 (black color) tribologicaly tested with sliding speed up to 1,8 m/s and up to 14 MPa of nominal load under water lubrication.
-
Au nanoparticles identifiction with the use of AFM Volta potential mapping
Open Research DataThe specific physical, chemical and electrochemical electrical properties of gold nanoparticles have led to their extensive use as high-performance chemical and biochemical sensors. The described properties relate to surface plasmon resonance, fluorescence quenching or enhancement, high electrical conductivity and light scattering. The described nanoparticles...
-
Measurements of radiation emission of a portable power bank with a capacity of 2600 mAh
Open Research DataThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell. The test setup was configured to measure a portable power bank...
-
Topographic AFM imaging of the leaf surface with magnification of details of its morphological structure
Open Research DataTopographic imaging of the leaf surface with magnification of details of its morphological structure. Measurements in semi-contact mode. NTEGRA Prima (NT-MDT) device. NSG 01 probe.
-
Ball on disk test AL(rf.)-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 not treated (reference).
-
Ball on disk test AL(rf.)-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 not treated (reference).
-
Ball on disk test AT4_1-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 TiN powder injected (AT4_1).
-
Ball on disk test AT4_41-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 TiN powder injected (AT4_41).
-
Ball on disk test AT3_2-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 TiN powder injected (AT3_2).
-
Ball on disk test AW4_4-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 WC powder injected (AW4_4).
-
Ball on disk test AW4_41-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 WC powder injected (AW4_41).
-
Ball on disk test AT4_11-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 TiN powder injected (AT4_11).
-
Ball on disk test AT3_21-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 TiN powder injected (AT3_21).
-
Ball on disk test AW4_1-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 WC powder injected (AW4_1).
-
Ball on disk test AT4_4-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 TiN powder injected (AT4_4).
-
Ball on disk test AW4_11-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 WC powder injected (AW4_11).
-
Measurements of radiation emission of a portable power bank with a capacity of 5200 mAh
Open Research DataThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell. The test setup was configured to measure a portable power bank...
-
Measurements of radiation emission of a portable power bank with a capacity of 10400 mAh
Open Research DataThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell (Fig. 1). The test setup was configured to measure a portable power...
-
SEM images of SFM, LSFM and SFMNb in as-prepared state and reduced
Open Research DataThis dataset contains SEM images taken for pristine strontium ferrite molybdate, as well as ones doped with lanthanum or niobium. Materials were characterized in powder, under high vacuum in secondary electron mode. The images are divided into folders for as-prepared samples and reduced (H2, 800 deg, 4 h) ones.
-
Exemplary SEM images of polished cross sections of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum mode.
-
Measurements of power supply system properties of "Magnetic SpeedLine" ultra-fast robot prototype for IML labeling
Open Research DataTests of the power supply system of "SpeedLine magnetic" ultra-fast industrial robot for IML labeling were carried out to analyze the effect of the active power filter (APF) parameters on the power quality. at the target duty cycle. Tests were performed with the target duty cycle. Linear synchronous motors with permanent magnets were used to drive...
-
Guided wave propagation signals measured on corroded stiffened panels
Open Research DataThe fundamental antisymmetric Lamb mode was excited by piezoelectric transducers attached at the pre-selected points on stiffened panels, representing typical structural ship components. The specimens were exposed to accelerated marine corrosion degradation, so the signals were collected to analyze the influence of the degree of degradation on the wave...
-
SEM images of cross sections of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrodes sintered at different temperatures
Open Research DataThis dataset contains cross sectional images of the porous Sr0.86Ti0.65Fe0.35O3 oxygen electrodes symmetric cells samples interface. Here are presented images of electrodes sintered at 950 °C, 1000 °C and 1050 °C. Images were obtained using a FEI Quanta FEG 250 Scanning Electron Microscope (SEM) with an accelerating voltage of 10 kV in a high vacuum...
-
Linear impedance of strontium–borate glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
-
The XAS spectra of O-K edges, M-L edges and Ce-M edges in Ce0.9M0.1O2
Open Research DataThe dataset consists of XAS spectra of O-K edges, M-L edges of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) synthesised by reverse microemulsion method. XAS spectra were collected at PIRX beamline in SOLARIS National Synchrotron Radiation Centre. Measurements were perfomed under ultra high vacuum in total electron yield (TEY) mode.
-
SEM images of symmetrical cell interface with SrTi0.30Fe0.70O3-d electrode and CGO-20 substrate in function of sintering temperature
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with SrTi0.30Fe0.70O3-d electrode and CGO-20 substrate in function of sintering temperature (800 °C, 900°C and 1000 °C) . Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage...
-
SEM images of symmetrical cell interface with SrTi0.65Fe0.35O3-d electrode and CGO-20 substrate in function of sintering temperature
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with SrTi0.65Fe0.35O3-d electrode and CGO-20 substrate in function of sintering temperature (800 °C, 900°C and 1000 °C) . Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage...
-
SEM images of symmetrical cell interface with SrTi1-xFexO3-d electrodes and CGO-20 substrate sintered at 800 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with SrTi1-xFexO3-d (x=0.35; 0.50; 0..70) electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum...
-
SEM images of symmetrical cell interface with SrTi0.50Fe0.50O3-d electrode and CGO-20 substrate in function of sintering temperature
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with SrTi0.50Fe0.50O3-d electrode and CGO-20 substrate in function of sintering temperature (800 °C, 900°C and 1000 °C) . Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 4-8h.
Open Research DataWear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer.Running time: 4-8h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21, #22-#23, #24-#25, #26-#27,...
-
Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 0-4h.
Open Research DataWear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer.Running time: 0 - 4h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21, #22-#23, #24-#25, #26-#27,...
-
SEM images of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...