Investigation of plasmon resonance in a silver nanoparticles
Open Research DataSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
Chemical investigation of the Al2O3 ultra-thin films
Open Research DataUltra-thin layers of oluminum oxide (Al2O3) were deposited by ALD method. Atomic layer deposition provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. Samples with a thickness of 2 and 8 nm of alumina...
-
Formation of gold anostructures detected by SEM microscope
Open Research DataGold nanostructures were prepared on silicon - Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air...
-
Simulation of perovskite-based CuI/CH3NH3PbI3/TiO2 solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/TiO2 model structure (Model 1) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/SnO2 solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/SnO2 model structure (Model 2) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/ZnO solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/ZnO model structure (Model 3) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Hemocompatibility of nanocrystalline diamond layers
Open Research DataThe biocompatibility of the diamond films were investigated with whole human blood samples. Blood used in this study was drawn from 10 healthy human patients of different age, sex, and blood group. A 2 ml samples were collected into standard tubes with EDTA anticoagulation agent. Blood was used within 6 hours from the collection time. A reference blood...
-
Anomalous anisotropy of deuterium-grown boron-doped diamond and the role of boron-tetramers in the Mott-Insulator transition
Open Research DataWe show anisotropy in the superconductivity for boron-doped diamond thin films prepared with Microwave Plasma Assisted Chemical Vapor Deposition using deuterium-rich plasma. This anomalous phase transition is linked with the emergence of boson quantum entanglement states behaving as a bosonic insulating state. Here, we show that the superconducting...
-
Chemical analysis of the Au-Ag nanoaloys
Open Research DataThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Substrate characterization in a electrochemically derived Manganium-Cobaltium thin films
Open Research DataManganium-Cobaltium thin films were electrochemically deposited on a Ni foams subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
Ferromagnetic nanoparticles imaging by means of Magnetic Force Microscopy
Open Research DataFerromagnetic nanoparticles can be used as building blocks for advanced thin film magnets, and can also be used in data storage and biomedical technologies. Nano-crystalline ferrites with the chemical formula NixZn (1 - x) Fe2O4, where x = 0, 0.2, 0.4, 0.6, 0.8, 1.0 show anti-corrosion properties and suppress electromagnetic interference, in the case...
-
The electrochemical studies of thin boron-doped diamond films deposited at conductive poly(lactic acid) 3D prints
Open Research DataThe dataset contains the electrochemical characteristics of the electrodes composed of thin boron-doped diamond films coated on commercially available graphene-doped polylactide acid. The boron doping level expressed as the [B]/[C] ratio in the gas phase for these studies was 500 and 10,000 ppm.
-
Data obtained by computation for X-ray imaging of grating without magnification using oriented Gaussian beams
Open Research DataThe propagation of X-ray waves through an optical system consisting of grating and X-ray refractive lenses is considered. In this approach, the propagating wave is represented as a superposition of the oriented Gaussian beams. The direction of wave propagation in each Gaussian beam is consistent with the local propagation direction of the X-ray wavefront.
-
Data obtained by computation for X-ray imaging of grating with magnification factor equal 2 using oriented Gaussian beams
Open Research DataThe propagation of X-ray waves through an optical system consisting of grating and X-ray refractive lenses is considered. In this approach, the propagating wave is represented as a superposition of the oriented Gaussian beams. The direction of wave propagation in each Gaussian beam is consistent with the local propagation direction of the X-ray wavefront.
-
Data obtained by computation for X-ray imaging of grating with magnification factor equal 4 using oriented Gaussian beams
Open Research DataThe propagation of X-ray waves through an optical system consisting of grating and X-ray refractive lenses is considered. In this approach, the propagating wave is represented as a superposition of the oriented Gaussian beams. The direction of wave propagation in each Gaussian beam is consistent with the local propagation direction of the X-ray wavefront.
-
Data obtained by computation for X-ray imaging of grating with magnification factor equal 8 using oriented Gaussian beams
Open Research DataThe propagation of X-ray waves through an optical system consisting of grating and X-ray refractive lenses is considered. In this approach, the propagating wave is represented as a superposition of the oriented Gaussian beams. The direction of wave propagation in each Gaussian beam is consistent with the local propagation direction of the X-ray wavefront.
-
Mn-Co nanofilms on nickel foam measured by XPS mehod
Open Research DataManganium-Cobaltium based thin films were electrochemically deposited on a Ni based subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
Investigation of the C-1311 glucuronidation: an electrochemical approach
Open Research DataThis study was undertaken to investigate the glucuronidation of the compound C-1311 (5-diethylaminoethylamino-8-hydroxyimidazoacridinone – the model anticancer acridine derivative) using electrochemistry/mass spectrometry (EC/MS) as a complementary technique to in vitro (liver microsomes) and in silico approaches.
-
Sounding rocket temperature and heat transfer data
Open Research DataThis dataset contains temperature and heat transfer data measured during REXUS 25 sounding rocket HEDGEHOG Experiment launched from Esrange Space Centre, Kiruna, Sweden. For experiment details, please see: