Microstructural and electrical properties of Y0.07Sr0.93-xTiO3-δ perovskite ceramics
PublicationIn order to find a relationship between electrical and microstructural properties, yttrium-doped strontiumtitanate (7 mol%) with various values of strontium nonstoichiometry was investigated and shown in this work.It has been observed that yttrium doping can affect the electrical properties of SrTiO3 to a great extent.Moreover, the microstructural and electrical properties can be influenced by strontium nonstoichiometry.The defect...
-
La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ oxygen electrodes for solid oxide cells prepared by polymer precursor and nitrates solution infiltration into gadolinium doped ceria backbone
PublicationInfiltration is a method, which can be applied for the electrode preparation. In this paper oxygen electrode is prepared solely by the infiltration of La0.6Sr0.4Co0.2Fe0.8O3‐δ (LSCF) into Ce0.8Gd0.2O2-δ (CGO) backbone. The use a polymer precursor as an infiltrating medium, instead of an aqueous nitrate salts solution is presented. It is shown that the polymer forms the single-phase perovskite at 600 °C, contrary to the nitrates...
-
Electrical conductivity relaxation measurements - oxidation and reduction of BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Open Research DataThe dataset consists of 2 main catalogs: measurements performed for oxidation/reduction in dry conditions and in humid conditions. For Electrical Conductivity Relaxation (ECR) measurements, platinum reversible electrodes were applied in a four-probe arrangement and the sample was measured in the ProboStat™ measurement system. The ECR measurements were...
-
Characterization of novel GdBa0.5Sr0.5Co2−xFexO5+δ perovskites for application in IT-SOFC cells
Publication -
Evaluation of BaY1−Pr Mn2O5+δ oxides for oxygen storage technology
Publication -
Investigation of In-doped BaFeO3−δ perovskite-type oxygen permeable membranes
Publication -
Electrical properties of Y0.08Sr0.92Ti0.92Nb0.08O3-δ after reduction in different reducing conditions
PublicationElectrical properties of perovskite Y0.08Sr0.92Ti0.92Nb0.08O3−ı after reduction in different conditions were studied. Relatively high electrical conductivity in samples reduced in ammonia was observed. The conductivity of Y0.08Sr0.92Ti0.92Nb0.08O3−ı reduced in ammonia at 1500 ◦C was of about 600 S/cm at 200 ◦C. Conductivity after reduction in ammonia at 1500 ◦C was stable both in hydrogen and oxygen atmosphere up to 600 ◦C. Reduction...
-
A note on polynomial algorithm for cost coloring of bipartite graphs with Δ ≤ 4
PublicationIn the note we consider vertex coloring of a graph in which each color has an associated cost which is incurred each time the color is assigned to a vertex. The cost of coloring is the sum of costs incurred at each vertex. We show that the minimum cost coloring problem for n-vertex bipartite graph of degree ∆≤4 can be solved in O(n^2) time. This extends Jansen’s result [K.Jansen,The optimum cost chromatic partition problem, in:...
-
Structure and electric transport properties of Ca-doped bulk PrBa2Cu3O7−δ
PublicationThe crystal structure and electric transport properties of Pr1-xCaxBa2Cu3O7- delta (x= 0.0, 0.1, 0.2, 0.5) bulk ceramic samples, prepared by the standard solid-state reaction in air, were examined by X-ray power diffraction, resistivity measurements and room temperature thermoelectric power determination. Ca atoms introduce additional holes to the system as well as structural defects. The orthorhombic-to-tetragonal structural...
-
Effect of sintering temperature on electrochemical performance of porous SrTi1-xFexO3-δ (x = 0.35, 0.5, 0.7) oxygen electrodes for solid oxide cells
PublicationThis work evaluates the effects of the sintering temperature (800 °C, 900 °C, 1000 °C) of SrTi1-xFexO3-δ (x = 0.35, 0.5, 0.7) porous electrodes on their electrochemical performance as potential oxygen electrode materials of solid oxide cells. The materials were prepared by a solid-state reaction method and revealed the expected cubic perovskite structure. After milling, the powders were characterised by a sub-micrometre particle...
-
Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ on structural, electrical, and electrochemical properties for potential oxygen electrode of intermediate temperature solid oxide cells
PublicationThis work presents the results of a comprehensive study on the impact of the A-site non-stoichiometry of SrxTi0.3Fe0.7O3-δ (x = 0.90, 0.95, 1.00, 1.05) ceramics on their physicochemical properties. The materials were fabricated by the conventional solid-state reaction method and their structure was determined by X-ray diffractometry, X-ray photoelectron spectroscopy and electron microscopy. Their sintering and thermal expansion...
-
Enhanced Mechanical and Electromechanical Properties of Compositionally Complex Zirconia Zr1–x(Gd1/5Pr1/5Nd1/5Sm1/5Y1/5)xO2−δ Ceramics
PublicationCompositionally complex oxides (CCOs) or high-entropy oxides (HEOs) are new multi-element oxides with unexplored physical and functional properties. In this work, we report fluorite structure derived compositionally complex zirconia with composition Zr1- x(Gd1/5Pr1/5Nd1/5Sm1/5Y1/5)xO2-δ (x = 0.1 and 0.2) synthesized in solid-state reaction route and sintered via hot pressing at 1350 °C. We explore the evolution of these oxides'...
-
Novel cobalt-free BaFe1−xGdxO3−δ perovskite membranes for oxygen separation
Publication -
Superconductivity in PrBa2Cu3O7−δ single crystals after high-temperature thermal treatment
Publication -
Electrochemical impedance spectroscopy measurements - conductivity vs. temperature and conductivity vs. oxygen partial pressure - BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Open Research DataThe dataset consists of two main catalogs consisting of measurement data: of the electrical conductivity of the BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) sample as a function of temperature and of the electrical conductivity as a function of oxygen partial pressure (pO2). Measurements as a function of temperature were carried out in dry and wet air (pH2O ~...
-
Selection of material for infiltration of non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ
Open Research DataThe porous electrodes used for the infiltration were prepared from A-site non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ synthesized by the conventional solid state reaction method. Screen printed electrodes (0.5 cm2) on CGO-20 substrate, were fired at 800 °C for 2 hours in an air atmosphere. Infiltration of the scaffolds was performed by a water-based precursor...
-
The effect of Fe on chemical stability and oxygen evolution performance of high surface area SrTix-1FexO3-δ mixed ionic-electronic conductors in alkaline media
PublicationDevelopment of environmentally friendly, high performing oxygen evolution reaction (OER) catalysts is an important research challenge. In this work, iron doped strontium titanates with a general formula SrTi1-xFexO3-δ (x = 0.35, 0.50, 0.70, 0.90, and 1.00) denoted as STFx, were synthesized via a solid state reaction technique and characterized in terms of oxygen evolution reaction electrocatalysis in an alkaline electrolyte (0.1...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Open Research DataThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed in order to force the exsolution process of metallic nanoparticles.
-
Correlation between crystal and transport properties in LnBa0.5Sr0.5Co1.5Fe0.5O5+δ (Ln - selected lanthanides, Y)
Publication -
The Influence of Iron Doping on Performance of SrTi1-XFexO3-δ Perovskite Oxygen Electrode for SOFC
PublicationSolid Oxide Fuel Cells (SOFC) are based on electrolytes and mixed ionic and electronic conductivity (MIEC) materials. The need to reduce costs causes an increase in interest of new compounds suitable for operating temperatures between 600 °C and 800 °C. The SrTi1-xFexO3 (STF) perovskite material is a perspective material that could be used for the oxygen electrodes. In this work STF materials with different content of iron (x =...
-
Synthesis of Polycyclic δ-Lactams with Bridged Benzomorphan Skeleton: Selectivity and Diversity Driven by Substituents
Publication -
Structural and electrical properties of Sr(Ti,Fe)O3-δ materials for SOFC cathodes
PublicationW niniejszym artykule, dwa związki SrTiO3 domieszkowanego Fe przebadano pod względem przydatności na katody w tlenkowych ogniwach paliwowych. SrTi0.65Fe0.35O3 i SrTi0.5Fe0.5O3 zostały przebadane pod względem reaktywności chemicznej z elektrolitem YSZ. Stwierdzono, że przewodnictwo elektryczne tych związków jest stosunkowo niskie: 0,4 S/cm i 2 S/cm odpowiednio dla STF35 i STF50.
-
Microstructure and electrical properties of SrTi0.98Nb0.02O3-δ-based composites applied as porous layers for SOFCs
PublicationPrzebadano właściwości elektryczne oraz strukturalne kompozytów Sr(Ti,Nb)O3-YSZ i Sr(Ti,Nb)O3-CeO2 naniesionych w postaci warstw porowatych na podłoża YSZ
-
SEM images of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials after reduction at 900 deg.C in hydrogen
Open Research DataThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) powder materials synthesized via the Pechini method after reduction in hydrogen at 900C for 10h.
-
The influence of synthesis method on the microstructure and catalytic performance of Y 0.07 Sr 0.93 Ti 0.8 Fe 0.2 O 3-δ in synthetic biogas operated solid oxide fuel cells
PublicationThe Y0.07Sr0.93Ti0.8Fe0.2O3-δ (YSTF) material was fabricated using three different synthesis methods: modified polymer precursor method (MPP), Pechini method and a solid state reaction method. It was applied as an anode catalytic material for biogas reforming in solid oxide fuel cells. Clear differences in the microstructure of fabricated catalytic layers were found, mainly with respect to a grain size and distribution of grains....
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials
Open Research DataThe ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Open Research DataThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed to force the exsolution process of bimetallic nanoparticles.
-
Effects of Ni-NCAL and Ni–Ag electrodes on the cell performances of low-temperature solid oxide fuel cells with Sm0.2Ce0·8O2-δ electrolyte at various temperatures
PublicationThree low-temperature solid oxide fuel cells are built using Sm0.2Ce0·8O2-δ (SDC) as the electrolyte. Cell A is symmetrical and features Ni–LiNi0.8Co0·15Al0·05O2 (Ni–NCAL) electrodes, Cell B comprises a Ni–NCAL anode and a Ni–Ag cathode, and Cell C is fabricated using a Ni–NCAL cathode and a Ni–Ag anode. The ohmic resistance and polarization resistance (Rp) of Cells B and C are significantly higher than those of Cell A. The reduction...
-
Unveiling the Electrocatalytic Activity of the GdBa0.5Sr0.5Co2–xCuxO5+δ (x ≥ 1) Oxygen Electrodes for Solid Oxide Cells
Publication -
Tailoring the Stability of Ti-Doped Sr2Fe1.4TixMo0.6−xO6−δ Electrode Materials for Solid Oxide Fuel Cells
Publication -
Water uptake kinetics and electrical transport in BaCe0.6Zr0.2Y0.1M0.1O3−δ (M = Tb, Pr, Fe) protonic conductors
PublicationBaCe0.6Zr0.2Y0.1M0.1O3−d (M = Fe, Pr, Tb) is a mixed conducting oxide in which three mobile charge carriers – oxygen ion, electron/hole, and protonic defects – are present. These types of materials have gained much interest as electrode materials for protonic ceramic fuel cells (PCFCs) and protonic ceramic electrolysis cells (PCECs). In this study, the water uptake and oxygen transport properties of different BaCe0.6Zr0.2Y0.1M0.1O3−d...
-
Badanie przewodnictwa jonowego materiału katodowego do ogniw SOFC na bazie La1-xSrxMnO3-δ
PublicationMieszane przewodniki jonowo-elektronowe na bazie domieszkowanego manganianu lantanu znajdują powszechne zastosowanie m.in. jako elektrody w ogniwach paliwowych, czujnikach gazów lub jako warystory. Jednak wciąż niepoznane do końca mechanizmy występowania zjawiska mieszanego przewodnictwa sprawiają, że prace nad tymi materiałami wciąż trwają. Określenie składowej jonowej tego typu materiałów perowskitowych wymaga zastosowania...
-
Evaluation of La 2 Ni 0.5 Cu 0.5 O 4+δ and Pr 2 Ni 0.5 Cu 0.5 O 4+δ Ruddlesden-Popper-type layered oxides as cathode materials for solid oxide fuel cells
Publication -
The XRD diffraction patterns of as-preapred (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co)
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co) were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrodes sintered at 1050 °C before and after test
Open Research DataThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrode sintered at 1050 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using...
-
Co-free triple perovskite La1.5Ba1.5Cu3O7±δ as a promising air electrode material for solid oxide fuel cells
Publication -
Cu-Content La1−XSrxNi1−YCuyO3−Δ Perovskites As Cobalt-Free Cathode Materials for High-Performance It-SOFCs
Publication -
Enhanced oxygen mobility by doping Yb in BaGd1-xYbxMn2O5+δ double perovskite-structured oxygen storage materials
Publication -
Crystal structure and proton conductivity in highly oxygen-deficient Ba1−xLax(In,Zr,Sn)O3−δ perovskites
Publication -
Single-Step Symmetrical Double Alkylation of β,γ-Unsaturated δ-Lactams via Magnesium ‘Ate’ Complexes
Publication -
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 900 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1000 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1100 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials synthesized via the solid state reaction method
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
Ti-doped Sr2Fe1.4-xTixMo0.6O6-δ double perovskites with improved stability as anode materials for Solid Oxide Fuel Cells
Publication -
High Cu content LaNi1-xCuxO3-δ perovskites as candidate air electrode materials for Reversible Solid Oxide Cells
Publication -
Ruddlesden-Popper-type Nd2-xNi1-yCuyO4±δ layered oxides as candidate materials for MIEC-type ceramic membranes
Publication -
Processing of Ce0.8Gd0.2O2-δ barrier layers for solid oxide cells: The effect of preparation method and thickness on the interdiffusion and electrochemical performance
PublicationCe0.8Gd0.2O1.9 (CGO) barrier layers are required to mitigate the chemical reactions between Sr-containing oxygen electrode materials and Zr-based oxygen ion conductors in high-temperature solid oxide cells. Barrier layers produced by different methods were studied in this work. As a reference, a cell with no barrier layer was measured. The application of the powder-processed barrier layers, considerably increases the performance....