X-ray diffraction spectra of modification of TiO2 nanotubes by graphene - strontium and cobalt molybdate perovskite
Open Research DataData show XRD results for strontium and cobalt molybdate-modified nanotubes that were also decorated with graphene oxide. The crystalline phases were characterized by X-ray diffractometer (Philips X”Pert with detector X’Celerator Scientific).
-
XPS measurements of the Fe-Bi based glass
Open Research DataFe-Si-O and Fe-Si-Pb-O glass was measured by XPS method. The influence of Pb dopand on the glass structure, including the valence of iron, was investigated. The influence of the annealing temperature on the behavior of iron in glass was also investigated. Studies have confirmed the mixed valence of iron in glasses and a high proportion of metallic Fe.
-
Spectroscopic studies of Nb-doped tricalcium phosphate glass-ceramics prepared by sol-gel method
PublicationCalcium-phosphate based glasses and glass-ceramics play a crucial role in the tissue engineering development. Apart from their high biocompatibility and excellent ability to undergo varying degrees of resorbability1, they exhibit relatively high bioactivity and due to that they are commonly used as bone and dental implants. A substantial research effort is devoted to improve calcium-phosphate materials physico-chemical properties...
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Magnetic properties of the garnet and glass forms ofMn3Al2Si3O12
Publication -
Superconducting properties of BiPbSrCaCuO and BiSrCaCuO glass-ceramics
PublicationW pracy zbadano główne różnice pomiędzy właściwościami nadprzewodzącymi krystalizowanych szkieł BiPbSrCaCuO i BiSrCaCuO. Obie grupy materiałów wytwarzano w takich samych warunkach i zawierały one podobne ilości fazy nadprzewodzącej 2212. Mimo to, właściwości elektryczne w stanie normalnym oraz właściwości nadprzewodzące znacznie się różnią. Głównym źródłem różnic są różnice mikrostruktury obu grup materiałów.
-
Magnetic properties of the garnet and glass forms of Mn3Al2Si3O12
PublicationPrezentujemy wyniki pomiarow podatności magnetycznej i ciepła właściwego dla Mn3Al2Si3O12 w formie krystalicznej i amorficznej. W ten sposób przeprowadzamy porównania stopnia magnetycznej frustracji dla obu form tego samego związku chemicznego.
-
Photocatalytic activity of TiO2 immobilized on glass beads
PublicationAktywność fotokatalityczną czystego TiO2 oraz TiO2 modyfikowanego borem zbadano w reakcji degradacji wodnego roztworu fenolu. TiO2 osadzono na szklanych kulkach i umieszczono w reaktorze wyposażonym w szklaną, kwarcową rurę, którą naświetlano promieniowaniem z zakresu UV-Vus
-
The new steel-glass architecture of buildings in Japan
Publication.
-
Determination of pyridine and adenine nucleotide metabolites in Bacillus subtilis cell extract by sweeping borate complexation capillary electrophoresis
Publication -
Water absorption and blistering of glass fibre-reinforced polymer marine laminates with nanoparticle-modified coatings
PublicationMacro and microstructural damage was studied in typical glass fibre-reinforced polymer laminates with two types of coating systems – (a) isophtalic gel coat: pure or mixed with SiO2 nanoparticles 5 wt% (5%N) or 10 wt% (10%N) and (b) a two-layer coating system: urethane-modified vinyl ester-based gel coat and additional polyester barrier coat layer. Accelerated tests were performed at 50C for 50 days for specimens with nanoparticle-modified...
-
Impact Behaviour of Glass Fribre /Epoxy Composites with Nano-Enhanced Resin after Water Exposure
PublicationImpact behaviour of glass fibre /epoxy composites with nano- SiO2 modified resin was studied in terms of low velocity impact after water exposure. Nanocomposites with 1%, 2%, 3% 5% 7% nano-SiO2 (Nanopox- Evonic) were investigated. Peak impact load and impact damage area as a function of nanoparticle contents were compared for dry specimens and for samples exposed to water (0.7 %wt. 1.7% water absorbed) at 1J, 2J 3J impact energies....
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
Synthesis, structure and physical properties of new intermetallic spin glass-like compounds RE2PdGe3 (RE = Tb and Dy)
PublicationNew intermetallic compounds Tb2Pd1.25Ge2.75 and Dy2Pd1.25Ge2.75 have been synthesized using the arc-melting method. The crystallographic structure and magnetic, electronic transport, and thermal properties are reported. The crystal structure obtained from powder x-ray diffraction analysis suggests that these compounds crystallize in the AlB2-type structure (space group P6/mmm, no. 191) with lattice parameters a = 4.228 53(5)/4.230 54...
-
Linear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Conductivity and superconductivity of (Bi,Pb)4Sr3Ca3Cu4Ox glass-ceramics
PublicationAmorficzny materiał (Bi,Pb)4Sr3Ca3Cu4Ox w zależności od warunków wygrzewania może być albo granulastym materiałem albo silnie nieuporządkowanym metalem. W pracy przedstawiony jest wpływ mikrostruktury na właściwości elektryczne w stanie normalnym oraz przejście do stanu nadprzewodzącego.
-
Conductivity and superconductivity of (Bi,Pb)4Sr3Ca3Cu4Ox glass-ceramics.
PublicationW układzie(Bi,Pb)-Sr-Ca-Cu-O poprzez krystalizację w fazie stałej można wytworzyć materiały o bardzo różnych właściwościach elektrycznych i nadprzewodzących. W zależności od warunków krystalizacji, można wytworzyć nadprzewodnik o temperaturze krytycznej między 8 a 105 st.K lub materiał nie przechodzący do stanu nadprzewodzącego. W pracy pokazano i przedyskutowano wpływ składu fazowego, struktury i mikrostruktury na przewodnictwo...
-
<title>Glass-ceramic fiber optic sensors</title>
Publication -
Properties of glass-ceramic for solid oxide fuel cells
PublicationW pracy przedstawiono właściwości krystalicznych pyro- i orto- krzemowych szkieł przygotowanych dla tlenkowych ogniw paliwowych. Zbadano rozszerzalnoność, ubytek masy, zmiany widm rentgenograficznych oraz widm impedancyjnych dla szkieł narażonych przez 60 dni na atmosfere ulteniajacą i redukująca w temperaturze 800C.
-
Tellurite based glass doped by Eu3+ ions - XPS measurements
Open Research DataEu3+ doped tellurite glass ceramics containing SrF2 nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF2 nanocrystals in glass matrices after...
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 annealed glass was measured by impedance spectroscopy method.
-
Analysis of the chemical composition of MnO-B2O3 glass
Open Research DataStructural and thermal properties of xMnO−(100−x)B2O3 (where x = 40, 50 and 60 mol%) glass samples have been investigated with the employment of various techniques. Fourier transform infrared spectroscopy results revealed the influence of MnO on glass matrix. Decrease of B–O bond-related band intensities has been observed. MnO addition was found to...
-
Linear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Effect of slag coal ash and foamed glass on the mechanical properties of two-stage concrete
PublicationTwo-stage concrete (TSC) is known by various names such as colcrete, Polcrete, preplaced aggregate concrete and prepacked concrete. It is different from traditional concrete in two fundamental ways, namely method of construction and mix proportion. Two-stage concrete (TSC) is defined as firstly, coarse aggregates are placed into the formwork and grout is applied to fill in the between coarse aggregate particles voids. Secondly,...
-
Transmembrane Transport and Anticancer Activity of Strontium Ranelate Delivered with Nanosecond Pulsed Electric Fields (nsPEFs) into Human Cells in Vitro
Publication -
Nonlinear impedance as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Influence of synthesis conditions on glass formation, structure and thermal properties in the Na 2 O-CaO-P 2 O 5 system doped with Si 3 N 4 and Mg
PublicationOxynitride phosphate glasses and glass-ceramics were prepared using new synthesis routes for phosphate glasses. Materials were melted from pre-prepared glass samples in the system Na-Ca-P-O with addition of Mg and/or Si3N4 powders under different preparation conditions. The melting process was conducted at 1000–1500 °C either under air or nitrogen atmosphere to obtain materials with different nitrogen content. Their topography...
-
Structural and luminescent study of TeO2-BaO-Bi2O3-Ag glass system doped with Eu3+ and Dy3+ for possible color-tunable phosphor application
PublicationTellurite glass systems of 73TeO2-4BaO-3Bi2O3-1Ag:xEu2O3-(2-x)Dy2O3 (where x = 0.5, 1, 1.5, 2 in molar ratio) composition have been successfully synthesized. In order to acquire Ag nanoparticles, materials have been heat treated at 350 °C in the air atmosphere. Structural properties of obtained samples were evaluated with various techniques. X-Ray Diffraction (XRD) measurements indicated that obtained materials are amorphous in...
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 fully crystallized glass at 813 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 partially crystallized glass at 613 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 partially crystallized glass was measured by impedance spectroscopy method.
-
Predicting Performance of Lightweight Concrete with Granulated Expanded Glass and Ash Aggregate by Means of Using Artificial Neural Networks
PublicationLightweight concrete (LWC) is a group of cement composites of the defined physical, mechanical, and chemical performance. The methods of designing the composition of LWC with the assumed density and compressive strength are used most commonly. The purpose of using LWC is the reduction of the structure’s weight, as well as the reduction of thermal conductivity index. The highest possible strength, durability and low thermal conductivity...
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
The (Bi,Pb)4Sr3Ca3Cu4Ox glass-ceramics: disordered metal and superconductor
PublicationAmorficzny materiał (Bi,Pb)4Sr3Ca3Cu4Ox wygrzewany w odpowiednich warunkach staje się granulastym metalem i nadprzewodnikiem. Może być uważany za silnie nieuporządkowany metal. Ma duży opór i zazwyczaj ujemny współczynnik temperaturowej zależności oporu. Nieuporządkowanie i granulasty charakter materiału ujawnia się również w jego właściwościach nadprzewodzących.
-
The structure of rarefied and densified PbSiO3 glass: a molecular dynamics study.
PublicationArtykuł przedstawia wyniki symulacji dynamiczno-molekularnychstruktury rozrzedzonego i zagęszczonego szkła PbSiO3 (w zakresie gęstości od 3000 kg/m3 do 8000 kg/m3). Otrzymane wyniki dokładnie przedyskutowano pod kątem blisko- i średnio-zasięgowego uporządkowania atomów i porównano ze strukturą szkła PbSiO3 o normalnej gęstości (5970kg/m3) oraz ze strukturą rozrzedzonych i zagęszczonych szkieł PbGeO3.
-
<title>Technology of soft-glass optical fiber capillaries</title>
Publication -
Cluster-glass behavior of a highly oxygen deficient perovskite, BaBi0.28Co0.72O2.2
PublicationZostała przeprowadzona synteza zwiąku typu perowskitowego BaBi0.28Co0.72O2.2. Stuktura krystalograficzna została określona poprzez dyfrakcję neutronową i promieniowania rentgenowskiego. Pomiary podatności magnetycznej AC i DC wskazują na zachowanie typu szkła klastrowego, które wynika z oddziaływań klastrów ferromagnetycznych.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 473 K for 3h and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-